Platinum Palladium and silver extraction from Rock | Ore processing for precious metals
Вставка
- Опубліковано 30 кві 2024
- Demonstrate the processing Rocks for precious metals.
Determine Platinum palladium and silver content of ore.
Please subscribe to my UA-cam channel by ➰clicking on Link below 👇
❌ Your support will aid me in creating higher-quality videos:❌
👇
ua-cam.com/users/PickyPlans?su...
Contact me on :
Instagram : / pickyplans
Facebook: / picky.plans
telegram: t.me/pickyplans
#smelting
#silver
#palladium
#platinum
#smelting
#cupellation
#goldore
#silverore
#palladiumore - Розваги
Ore precious metals concentration was 7.2 ppm
Silver 3.6 ppm
Palladium 2.1 ppm
Platinum 1.2 ppm
Muy bien.
Здравствуйте, серебро, ПД и платина по ходу 😊
عالی بود
Good job bro 👍🔥🔥🔥🔥🔥🔥🌹
Thanks bunches, bro 🙏🌹
💪💪💪👍👍👍
Nice video, keep going bro
Thank you so much bro!
Our chemist is a pro 😁😁😉
Thanks Hosam, you helping a lot🌹
Excelente vídeo!
Apreciaria muito se puder responder umas questões.
Como você obteve as quantidades do Paládio e da Platina?
Conseguiu determinar se o resíduo insolúvel na digestão ácida era o Ródio?
Você tem algum vídeo sobre a metalurgia do Ródio?
Obrigado!
gracias mi amigo. el paladio se precipitó usando zinc y se cupeló por separado. Hice lo mismo con el polvo restante en el ácido nítrico y luego lo pesé con una báscula sensible. Alao, puedes hacer la prueba con una pistola XRF antes de tratar con ácido nítrico. Sí, el residuo negro podría probarse hirviéndolo en un poco de agua regia. Si se disuelve, es platino y, si no, lo más probable es que sea rodio. Desafortunadamente, todavía no tengo ningún vídeo sobre el refinado de rodio, pero estoy considerando hacer algunos...
Thanks man. Please clarify one more doubt for me. Wouldn't Platinum have dissolved in nitric acid along with Silver and Palladium?
No problem.
No it would be released as black powder while dissolution of alloy. This happens to gold and rhodium but gold and platinum could be dissolved in hot aqua regia.
Thank you my friend.🙏⚗
the concentration method you used could be used for other dense minerals right? such as lead or tungsten bearing minerals?
Yes as you mentioned it could be used for other dense materials.
Usually denser than 5 g/cm3 could be concentrated this way.
@@PickyPlans thanks for the verification, also wondering if you could make a video focusing on this concentration process on its own? im looking to build a larger setup and some pointers would be greatly appreciated.
@adelinyoungmark1929 I do need a large setup too but still not sure about building a shaker table or just larger blue bowl.... In any case I'll make a video on that
Hi, can you do smelting in a cast iron crucible?
Yes, it could be done, but the temperature should not exceed 1000°C.
It depends on your flux system
Assalamualaikum, i want ask you a question. I have 250gram of mix IC, flat pack, transistor and 56 gram of chips, bassed in your experient how much gold that could i get. Thank you.
Depending on your material types you would get 0.3-0.5 grams of gold.
@@PickyPlans Well that's enough Alhamdullilah i still got revenue from refining that material Insyaallah.
Dear sir white powder is falling down in Aqua Regia what is it i don't understand
It's silver chloride forming by addition of silver nitrate solution to HCl solution.
❤😂
Мне кажется что с магнитным шлихом (магнетитом) могло уйти небольшое количество драгоценных металлов.
Я не уверен в этом... такое может случиться... но однажды опытный парень сказал мне, что если не соскребать дно кастрюли, двигая магнит, то вы не потеряете при этом ни одного драгоценного металла. с магнитами.
I’m sure the electricity used to grind the rocks was more than the results
Metal recovered through fire assay analysis doesn't necessarily cover analysis expenses.
درود
دوست عزیز
شما ابتدا تشویه را انجام بدهید به روش احیا بصورت سه مرحله ای
در نظر داشته باشید اکسید الومنیوم موجود در خاک یکی از عوامل مزاحم است که بسیار مشکل زا هست. و کمتر کسی به آن توجه میکند.
شبیه به فلز روی ، فلزات گرانبها را به سرباره منتقل میکند.
ممنون از توجه شما
به دلیل کم بودن حجم نمونه فرایند رو خیلی پیچیده نکردم و سعی شد که سولفید با لیتارژ یا آبه سربی اکسید بشه .
اکسید آلومینیوم تا حجم های مشخصی در وجود بوراکس و آبه سرب به سرباره روان تبدیل میشه ، حتی توی کاتالیست خودرو هم با این فرمول مشکلی ایجاد نمیکنه
A waste of time