6010 ROOT TIPS & TRICKS | VERY DETAILED, HIGHLY REQUESTED PIPE WELDING
Вставка
- Опубліковано 16 лип 2024
- In this video I'll be stick welding pipe, showing you how to do a 6010 root in 2g 5g and 6g position. ill be very detailed (step by step) explaining how I do a root and the settings I used when I'm welding in different positions.
CHECK OUT MY WEBSITE!👇🏼
www.theweldlab.com/
Best Affordable Welding Lens on the Market!
amzn.to/37KYNqW - Навчання та стиль
i've a welding teacher that insisted our keyhole be big enough to practically stick the rod through. no pressure on the plate at all... super hard to do, and then youtube showed me the right way to do it! always glad to see comprehensive 6010 open root videos.
Same!
for tests most places want an uphill root, welds ran uphill are structurally stronger, when you’re in the field after the test it’s different, downhill root is faster
I've welded 25 years as a pipefitter and on the weld tests we take we have to run the root the hot pass and cap all uphill. I'm guessing this guy is a pipeliner because he's running downhill. He explained this video very well. Looks like a pretty decent welder.
What I love about welding is you’re always learning something. I learned something from this.
Right on im still learning till this day
Ok I got confused from this..
The pipeliner I bought my SA200 from been in the business 35 years. Said he has never had to weld higher than 2nd gear. I welded pipe coupons in his shop and he instructed me to always keep the rod at 90 degrees.
What gives ?
Less amps = less chance of too big a keyhole?
I'm just an amateur, not my day job.
I like the way you make arc welding seem like a breeze. Good stuff
Thanks !
I'm a welder myself. And I have to say your videos are very informative and precise. Keep up the good work!
I've watched you for awhile, now like your detail structure in direction! as I always say keep'em guessin!!
Wow! That is root pass. All I know using 6010/6011 for root pass is to travel through whip and pause to fill up the key hall but you did it very easy to look at but I pretty sure it needs mastery to perfect it. Thank yoi so much! From Philippines
Great video. Confirmed some of what I was doing, but also brought to my attention some things I wasn't cognizant of. Cheers!
You got great explanation skills! Masta Masta your videos have helped me prepare for my test exponentially
good job Rigo, there's a bright future ahead of you doing what you're doing. stay safe y hechale pa adelante
Easy simple and hit all the details right on the money thanks man awesome video
U did a great job on this video like seeing fellow welders help others in the craft 😀
Idol very well said. More power to all welder around the globe. Am Filipino welder
Great, great video! Getting an education from every one of your videos!
Thanks so much 🙏. You have help me step up my game!!
Excellent advice for novices! Bless you! Great instructions. Most welders online hide their amps, travel speed, etc. Btw, most welding instructors teach welders to keep the rod "at 90° to the center!"
Thanks for the feedback 🙏🏼
Gr8 tutorial man. I was surprised to see no whip and pause. Only when you needed to fill an occasional keyhole. Thanks for the lesson bud
im glad you enjoyed it ill have more tutorials on the way with way better quality and audio
If you have a good gap you can just drag make sure you're breaking down both walls. Only need to step if you keyhole
I love this video so much. You did it very well
Thank you for sharing your knowledge.
Nice to know how to do it right! Thanks!
Your video was so helpful thank you so much 🙏🏾👍
Already!!!! Back it it again!!!!
Saludos des de Houston, Texas
#Covid_Season_2021
Thanks bro! Very informative.
Best video on 6010 pipe
Great video! Thanks for the info.
Excellent tutorial buddy
Very detailed video 👍🏽
Outstanding job sir.
As a welder i enjoyed your video a alott
Thanks for the video man 😎
Great video and information
Glad it was helpful!
Thank you!
Good information. Cheers.
Thanks for the advise very helpful
appreciate the support!
Man luv that sizzle 6010 makes when u getting it.
Bro. Thank you! I will bring this to TWS
Glad I can help brother !
Spider pipe clamps would help your fit-up better and faster with various sizes for pipe, best investment, time saver as well!
I'm a painter but good shit. I like your videos!
Nice video!
God bless my brother
Thx for the video.
Sehr gut.Sehr gut.
Good video
On your last weld the 2g pipe. What do you do to have the weld come out all the way across? Thanks for the tips man and awesome videos.
Excellent videothank you .
🙏🏼 thanks
good
video
Awesome weld
Like the video
Well Done!!!!
Im in school for welding rn in Houston, i was having issues with my key hole i kept wondering why it was just getting big?! Didn't realize i didnt have it an angle
Good stuff
Nice explanation
thanks man!
Good job,hop it is useful
Nice job..
Thanks!
Good info
thannks
Which welder machine you recommend to weld 6010 ??
push= hotter Drag=cooler 90degrees or straight will give you the most penetration and consistency if you can handle it...fit up plays a big role in which angle to use
I have an sa 200 red face but mine doesn’t have a remote what settings should I run bro
Thanks. You make it look easy.
Your Almost at 1M views 💯💯👊🏼👊🏼
Yeah man that’s crazy! Did not expect that at all
Nice work man . Hate those coatings for fumes
Awesome job explaining. Im on open v groove in school and they teach us the “step” method where you burn forward and step back into the puddle. Why don’t you have to do this on pipe?
When doing downhill pipe you’ve got a very tight gap with ussually little to no land. So if the bevel can hold the puddle with out keyholing very big you don’t have to wip in the root. On 6010 uphill roots if you get your heat and landing on your bevel perfect you can drag the rod uphill and get the same results. If you’ve got a bigger root opening or small amount of land on a fit up you can turn your amps down and wip and pause your root to get the same result. Its all puddle malipulation/ control. Watch the puddle and keyhole and you’ll get it!
Do you put any land on the bevel ? If so how much ?
i’m starting welding in highschool and my teacher has told me to whip n pause but i’ve seen multiple online videos of welders dragging. does anyone know some pros and cons to either side
which grade will be better for SS pipe?
Can you please do down hand capping. Thank you .🙏
When you mean having it straight you mean like… 90 degrees? Like if ur on top dont have it straight up, if ur on the left dont have it straight left and etc, thats correct?
Mantap
Nice support this channel
Great work guy good welding I can see u pay attention to what the weld is doing u take pride in the work u you u put your heart n soul on it .what part of Texas u r located
H-town!!
@@TheWeldLab thats good Im glad I will subscribe to your Chanel I will message you later on I have a welding company will be needing good welders like you .great work again .
Cool hit me up!
My instructor forces me to use whip and pause motion when doing the root pass. I’m I wrong for just moving forward consistently like shown in this video
Can you do an up hill one please
สุดยอดครับ
ขอบคุณ
Can you show the inside of the pipe after you run your root ?
I’m a bit confused are you moving it or it’s moving itself
Bro do you have a video on how to make a 1beed cap
I have a 6010/7018 5g on here
always been told to see a key hole to know that both joints have fusied?
Why are my downhill roots flat?
Интересная конструкция держака
💯💯💯
Can you make a 7018 1/8 vertical up. I’m trynna learn and it’s tricky. I do better on the 3/32 . But everyone else is using the 1/8
A little advice from a seasoned welder of 25 years . Big rod big mess small rod small mess when you're a beginner .
Excelente video solo falta la opción de subtítulos!
ya esta las voy a empezar a poner
Con la imagen lo entiendo
The thing with me is I’ll run it good dig it in but then it gets stuck and I try to strike again it’s a pain and when I’m going down to 6 o’clock it’s a pain
arc welding i like bro thanks for sharing nice❤
how about a uphill video also?
Never seen no one run 6010 down hill on pipe!
@@leeebtire5107 you haven't ever pipeline welded then
@@drewjackson1127 your right I stick to 30/100
What’s the pros/cons of running a stringer vs a whip with the 6010? Is it just personal preference?
If your running beads drag it unless the key hole opens up then you wanna step in when you downhill . Only time I really whip the bead in is if my doing uphill
No gloves at 4:23 gangster af
👍👍
Also grind your pipe inside and outside about one inch
👍
Lloyds inspector hear in uk would march us off site if we welded like that in the uk
like the video tho
I was always taught to whip 6010 didnt know you could drag it they always say that 6010 has alot of burn through so whip it, does the drag for 6010 also work for plate etc
yes but you need to have the rite gap and landing
@@TheWeldLab cool thank you, I will try it out nice vids just subscribed the other day keep it up
Thanks man
If you have a remote dragging the rod is easier and faster. Most of the time you don’t, so you learn how to weld with one heat all the way out. Even with 6010bead and Lohi out I’ll keep the same amperage. Uphill you’ll want to whip that bead in to help avoid trapped slag or internal undercut on the root. Also depends on weld procedure your working under. Api1104 will let all kinds of trash welds where b31 will not. All depends on the job. I personally prefer to whip 5p in on the root to insure a good reinforcement on the inside with no undercut.
How can I contact you?
👌👌👌👌👌👌👌
30 - 40 amps right
Bro I need some help with my root, my instructor tells me to penetrate the keyhole but everytime I do that and drag start dragging it.. my rod gets stuck
Run a nickel land and a dime gap. Run your rod 90deg. To pipe . Run a 5/32. 5p pluss rod. Run enought heat to move forward at a ready pace, yes you will have a key hole just keep going if the key hole is not filling in turn down in incriminates of 5 on the box. I learned this a long time ago . I will tell you that for a reference two welders on a 30 inch pipeline tie in crew can put a bead in the pipe in 20 min. Or less. So keep practicing. Good luck.
332 gap 1/8 rod , strike it like you would a match on heat effected zone . If you get stuck pull the stinger off the rod and grab another cause you probably knocked off the flux on the end of the rod and that's why you keep sticking .
Do you actually rest the rod on the bevel? I try that with my miller and it sticks
Yes I do and a lil pressure with the heat it will keyhole...are you using the correct rods ?
@@TheWeldLab yep 5p+ but I was always told that Lincoln u can apply alot of pressure but miller u cannot. I haven't welded pipe in 8 years and its giving me alot more hell to relearn downhill than I thought it would
Not sure which Miller u r using but I have used both on the Miller PipePro make sure ur heat is up like a Lincoln but also turn ur dig/arc force up more n it will help penatrate breaking walls u should see ur small key hole, hope that helps
@@1pipepro actually im using a hobart champion 225 basically a miller but no arc force or anything fancy. It welds just like a miller. Tomorrow ill just get real aggressive with it and run my root around 85 to 90 amps and really push on the rod. I bought the machine because it was cheap and same thing as my buddys trailblazer. Not looking to pipeline but chase rigs like he does so maybe I can relearn pipe again. Its been 8 years so its startin all over for me
Keep a clean lens also to see what you're doing❗️❗️❗️
Where your welding gloves at
what is 6010?
I also don't wear gloves welding with P-5. ore sleeves 4:08