Today's Triple-T (tools, tips and talk) #106, we continue our Damascus patterns series and we'll look at feather damascus in this episode. I'll also review a new tig welder from Vevor.
TIG Welder Link: bit.ly/3felj1A
All Welders: bit.ly/3CbNuXm
US Store Homepage Link: bit.ly/3QPhQUG
Coupon Code: VVG5%OFF(5% OFF for all the products in VEVOR)
Maritime Knife Supply: maritimeknifes...
My Website: www.tyrellknife...
My Instagram: / tyrellknifeworks
My Patreon: / tyrellknifeworks
Abrasives by Brodbeck Ironworks: brodbeckironwo...
Full List of Product Links:
General Tools
Wen Horizontal Bandsaw - amzn.to/3nS7Vzi
Horizontal Bandsaw blade: amzn.to/2VctTTZ
Wen Drill Press: amzn.to/2YkqfG1
Wen Portable Bandsaw: amzn.to/3aKJvDX
Titanium 200 Welder: amzn.to/3jkqNoQ
Bosch 4.5" Angle Grinder: amzn.to/36I2tbA
5" Vice: amzn.to/34PvAsF
Kant Twist 2" Clamp: amzn.to/3wp1hoB
Vice for quench plates: amzn.to/3hlZd9M
Checkering/Jimping File: amzn.to/34L2SJa
Magnetic Plastic Vise Jaws: amzn.to/3aLL4lh
Metal Ruler pack: amzn.to/2WOkHmr
Equal Distance Tool - amzn.to/2JoMUgD
Epoxy Color Powder pack: amzn.to/3nXgtoC
Edge/Center finder: amzn.to/38E3vFJ
Magnetic Angle Meter: amzn.to/3aKLBUo
123 Blocks: amzn.to/3hyhFwl
Height Gauge: amzn.to/3hnqF7a
Surface Plate (6" x 18"): amzn.to/2MdzEfR
Blue Dykem: amzn.to/2WQ4k8Q
Center Drills: amzn.to/3mTn3ev
Cle-Line Drill bits: amzn.to/3mMpTSo
Countersink Drill bits: amzn.to/38DoecD
Digital Calipers: amzn.to/3MzGmaH
Photography Light Box: amzn.to/3sFvOgh
Gas shock (10", 35lbs): amzn.to/3qM81JH
Nicholson Files: amzn.to/3dFLDyv
Nicholson 6" Files: amzn.to/3bnMJ0f
Nicholson Needle Files: amzn.to/3dGJS3Z
Carbide Burrs: amzn.to/2O2qjc8
Forging
Copper Roll (6"x120"x0.020"): amzn.to/3eTermn
Propane Torch: amzn.to/3kOxHoW
Bolt Jaw + Wolfjaw Tong set: amzn.to/2XZEIKs
Offset Knife Tongs: amzn.to/3ATXGks
Forge Scale Brush: amzn.to/3nWWgyY
Parks 50: amzn.to/3mV4eYd
Hardness Files: amzn.to/2L3O41C
Ferric Chloride: amzn.to/2TNZSt7
100 lbs propane tank: amzn.to/3hnqhFK
Propane adapter: amzn.to/34OM6Jf
Pyrometer Gun (-2700deg): amzn.to/38HVgIy
Rigidizer: amzn.to/2M6otoZ
Kaowool 24x24x2: amzn.to/3ht50KT
Stainless Steel double forge burners: amzn.to/37RFFqG
2" Gate Valve: hamzn.to/3NcdS5R
1/4" Solenoid: amzn.to/3zX1SlS
1/4" Ball Valve: amzn.to/2M89evP
1/4" Needle Valve: amzn.to/3hne18d
Pulley Block: amzn.to/3rHkn7k
6" Inline 440 CFM Blower: amzn.to/3OdkJgx
6" to 3" Fan Reducer: amzn.to/39IOYNw
Grinding / Sanding / Finishing
1500 Grit Hamon polish: amzn.to/3lekHrW
Belt Cleaning Stick: amzn.to/3hoyzwY
Dust Collection System: amzn.to/34QqsVc
Loc-Line Dust Collection Tubing - amzn.to/3hlri17
Mother's Wax: amzn.to/2WQILF6
2x72 Leather Belt: amzn.to/3hqtdRZ
Sanding Drum Set: amzn.to/34MSlgB
Sanding Drum Sleeves: amzn.to/3rA6nMn
Grinding Wheel (variable speed grinder): amzn.to/3ppMSV2
DuraGold 220 grit Roll: amzn.to/3aK9TxI
Brownell Oxpho Cold Blue: amzn.to/3aTzcgO
Leatherworking
Thread spacing tool: amzn.to/3psKcpw
Springfield Leather 13ft Double Shoulder: amzn.to/3psoNgl
Dragon Scale Stamp: amzn.to/3prNidr
Basket Weave stamp: amzn.to/34NO0dd
Stone stamps (combo pack): amzn.to/3rysUJp
Dye - Dark Brown: - amzn.to/34QpbgS
Dye - Burgundy: amzn.to/37S1yGH
Dye - Light Brown: amzn.to/37RHx2Q
Dye - Tan: amzn.to/2KHR4kj
Dye - Blue: amzn.to/34Mbpfd
Snaps: amzn.to/2WPj1Jy
Daubers: amzn.to/3ugJIWJ
Hydraulic Press
13 gpm Pump: amzn.to/3yZPhfm
Switch: amzn.to/3pyqrx7
Valve: amzn.to/2KId7am
Oil Filter: amzn.to/37SJDzG
Motor: amzn.to/38KohDQ
Reservoir: amzn.to/37To4Pj
Coupler: amzn.to/34MR7Sx
Surface Grinder
Slide table: amzn.to/3sFvKwM
Magnets: amzn.to/3sCMCV7
Linear Guide rail: amzn.to/3thKGBE
(These are Amazon Affiliate Links and this channel gets a commission with no cost to you)
Any questions about the feather pattern that I didn't cover?
when you started the layers of steel were like a sandwich then you crush corners
then draw it out do you draw it out with the layers running up and down vertically before restack.
@@robertpiano9991 You want the crushed W's running vertically in the billet. Meaning as you press the bar, your W's are being compressed. The other way would flatten them, if that makes sense. The graphics represent the orientation of the bar.
what would happen if after the cutting, you did a twist on each half in opposite directions, squared up, and reforged? :o
@@jeffclarke1694 Oh IDK but that sounds kinda cool. Maybe it would delaminate????
@@jeffclarke1694 Once you twist something, you really lose most of the pattern. I've found that after twisting most patterns, it just looks like a twist. Plus this would have a VERY high chance of shearing apart.
Adding the graphics is a nice touch to show how the damascus develop
I'm happy the graphics help. Thanks for watching!
25:20 When you were pressing it and the feather was being imprinted on the scale! It looked awesome.
The scale coming off the billet can look so cool at times. I need to up my game on the video production and do some slow-mo shots of that. Thanks for watching, Jamie!
@@TyrellKnifeworks Don't up it too much, I love the authenticity of your videos. Some channels have their cameras on tracked dollys and the video is more about the production of the video and not the work. 👍👍🎦🎦🎥🎥
"Oh! Hey Everyone! I'm Dennis Tyrell. Let me take two EXTREMELY complicated ideas -- ring-of-fire damascus, and TIG welding, and make EVERYONE feel like they can do those things with my calm, concise, simple and easy to understand explanations." **ten homes immediately blow up as people think they're expert TIG welders** (including mine). Seriously -- I LOVE this channel. I learn so much, EVERY SINGLE TIME I watch a Tyrell Knifeworks video. They're the best!
Haha, thanks for following the channel! Sorry about your house blowing up. 😜
You're seriously like... the Mr. Rogers of knife making. Here we are as parents trying to explain to our kids the big feeling of jealousy, and we can't figure out how to tell our 4 yo that it's ok to be jealous of their new baby sibling, and along comes Mr. Rogers with the perfect explanation. And here YOU are, giving perfect explanations for all us new knifemakers. I really do appreciate your channel. It makes me excited to keep going and keep learning.
@@hunt_trap_fish I don’t know about Mr Rogers… maybe Bob Ross. 🤣. Listen to the podcast, I’m not quite as wholesome as Mr Rogers. 😜
@@TyrellKnifeworks well… Mr Rogers for adults then 🤣🤣🤷🏻♂️
Man I don't even know how to express how I feel about your videos. Your damascus billets are always amazing. What I'm so floored about is how freely you give the processes to us. I can imagine filming and editing gobble up a ton of time. Thank you, I am a huge fan Dennis.
Thanks so much for watching, I appreciate it. 👍
It doesn't matter if you know the exact details, every person, every hand, is giving a different outcome, the experience, the style, the perception, makes the difference.
Great job brother! And yes indeed, Tig is the only way to go with damascus in my opinion.
Loving this series on patterns it’s saving me tons of money on steel. Less mistakes! Thanks for the video bud, great work!!
I’m thrilled you guys are getting something out of it. Next week should definitely be something new for most!
Very nice explaining in the beginning. I bet it is so so much work to do this feather damascus. Keep up the great work ❤
It can certainly be a challenging pattern, but on of my favorites. Thanks for watching.
What a cool pattern! Never seen "river of fire" before.
I really like this pattern. I'm looking forward to cutting in the bevels and seeing what it looks like. Thanks for watching.
I enjoyed the explanation about welding equipment 👍
I'm glad that was helpful, Alex! Not everyone understands the different welding techniques so I thought this would be a good thing to go over. Thanks for watching.
These videos couldn’t have come in a better timing for me lol. Love seeing these I’ve learned so much!
I'm happy they are timely for you! Thanks for watching, Armen!
@@TyrellKnifeworks look at the comment below yours lol
Hi 👋 there Tyrell this is my first time commenting on video 📹 and I really have to say that's an amazing knife 🔪 pattern beautiful
You'll definitely want to checkout the full build video on this one coming soon! I'm excited about this one, having never done a spear before. Thanks for watching, Guillermo.
Glad to hear yet another good review of the Vevor welder. I've seen quite a few now and I think I've decided to purchase the MP welder that they sell; it's like $300 I think and so still a pretty good deal for what it is. Just need to run a sub panel out to my shed and I'll be good to go. Then I can finally build a press and try out some of these patterns.
If their multi-process welder has the HF start, it’s an amazing deal. My HF welder is almost 3x that price!
Great video. The nice thing about tig welding is you can make your own filler rod. You can make the filler rod out of the same material as the billet.
Yes, you could indeed. Thanks for watching, Jeff!
Wow mate that's beautiful. Love the graphics... Your videos are really getting better.
I’m glad the graphics help! Thanks for watching.
Thank you for sharing useful knowledge about Damascus Patterns. Hope you make more useful things!
Stay tuned, the patterns are just starting to get interesting! 😉
One of the most useful tips to date,adding side bars to the stack before you split it
Good job
Not before you split it, but before you reforge the splits back together. This was a huge improvement on the feather process. I've always had a love/hate relationship with feather because it always tries to split as you draw it out, this totally addresses that. 👍🏻. Thanks for watching, James.
@@TyrellKnifeworks we’ll say both then ,yes and that’s also my hate for it
The splitting and the forging
@@jamesball7322 It's just that if you forge weld on the side plates before the split, its an extra forge session, as opposed to doing it while you forge the splits together. Either way though, it's a huge improvement.
@@TyrellKnifeworks I’ve seen a lot of wasted time on patterns that didn’t have the pop so I’m not to worried about an extra step
Thank You!!! Great presentation! Fantastic series - learning a bunch! Gonna give it a try when I get my press going!!
Definitely one of my favorite patterns, this one. Give it a try, David! 👍
awesome video denis learned alot appreciate it and wow im buying 1 of those tig units it will be perfect for just damascus i really want to do feather but my buddy who welded my press together didnt leave a big enough opening for my dies he made the opening the same as the travel on my ram 8 inch so now i need to figure things out there probly gonna have to torch out the welds and re do it thanks again Mark😃👍👍
Email me a few pics of your press, I might be able to help. Thanks for watching, Mark
Really bloody awesome. Fantastic work!
Thank you! Cheers!
More great info! Thanks for sharing more of your knowledge with us! Can't wait the see the rest of the project!
You'll have to wait on the completion of this one. It'll be up in a few weeks I hope. Thanks for watching, Stephen!
Can't wait to see the next part and the final build!💪⚒️
You're going to have to wait for the full build video on this one. We're on to another cool damascus project in next week's Triple-T! Thanks for watching, Dan!
Also when you are using a scratch arc tig, to prevent pinholes, you have to roll the tungsten off, don’t lift it. We welded pipe for MANY years, and still do, before they came out with pedal start. They are nice rigs though. I need one! 😁😂
When you say "roll the tungsten off", what exactly do you mean? (I'm certainly no expert at tig, as you can tell). Thanks for watching, Tony!
Coming along nice. Can’t wait to see the spear build. That split was stressful to watch! 😬😬Lol. Oh, the little diagrams out add are really helpful to see what’s going as you progress.
Thanks, buddy! I’m looking forward to putting together your mosaic and showing that off! 👍
Question: How much of the metal do you lose to the scale falling off when you press it? Is it enough to notice or insignificant?
Usually you lose one percent of metal when you heat it up. You can see piles of scale around the power hammer or anvil. But the amount of steel you use decreases as you forge and heat as the billet as the billet gets smaller as you keep heating and forge . I think a math size could come up with a formula for the amount of loss over time. A long answer for a simple problem.
Math wiz instead of math size. I dislike auto correct …..
It depends on how often you have to heat it and the ratio between surface area and volume of your billet. From start to finish of making a more complicated pattern I’ve heard people losing as high as 3/4 of the material but that also depends on how much grinding you do. But I would say it is always enough to notice
What Robert and Simon have said is spot on. This is why I say some patterns aren't realistic to do by hand because you'd need to start with so much steel because you'd have to do so many heats that you'd lose most of it to scale. This is one of those patterns. Thanks for watching.
@@copper7309 I feel the autocorrect pain. It kicks my ass too.
Speak of the devil. I typed "the pain of autocorrect" not "the autocorrect pain."
You’re amazing I really appreciate it how fascinated Louise playing through everything is pretty cool how many do that so appreciate it and like the show the lights up to continue on with them I’ll keep watching
Thanks for watching!
That's cool, glad u did the wavy patterning in the video
Thanks for checking it out, William!
@@TyrellKnifeworks would you consider doing the other way of that wavy patterning (forge then grind) technique.
@@williammorrin7933 What exactly do you mean?
@@TyrellKnifeworks you forge your billet into a wave then grind the sides down to make it straight again
@@williammorrin7933 I wouldn't try to forge curves into the feather, its very prone to splitting and you would be putting a ton of stress on the exactly where the splits occur. You'd be better off adding the steel to the outside, putting in the scallops and then grinding all the steel away if you wanted just the feather (with no other steel on the sides).
Great one Denis!
Thanks, Brigham! I appreciate you watching.
I got two Lincoln migs and a Lincoln 600-lb gas stick welder and a plasma cutter but really need that TIG thanks for the info! 👍
For $195, you can't beat it! Thanks for watching, Michael!
That's gonna be one fancy spear! Thanks for the tutorial.
Yeah I hope it turns out as nice as I hope! Thanks for watching, Bryson!
Nice idea on the edges of the feather with the extra steel
This was really a great discovery. I'll be doing feather more often now given this new process I think. Thanks for watching, Terry
Awesome video. How long have you been making damascus? Does it take half a life time to learn? I am due to retire in the next couple of years and love this combination of art and metalworking. You really are one of the best I've seen. Cannot wait to see the finished spear.
I've been bladesmithing just under 5 years. It doesn't take long to learn. Watch my Beginner Series playlist, that will help you get started at bladesmithing! 👍🏻. Thanks for watching.
Like always...BEAUTIFUL😊
Thanks for watching, Akshay!
Awesome review on the welder! I've been looking for a decent TIG that wasn't in the thousands range. Just bought one now
They also have a multi-process welder with these same tig features plus mig for $520. So that's a good deal too. 👍🏻
@@TyrellKnifeworks yeah I got what you got. But apparently it came down in price a little bit. I got it for 180
For the scallops removal, would it be possible to use a bandsaw, and use the steel for something else? Like bottle openers?
I doubt it. Plus that amounts to maybe $10 in steel... not worth the effort in my opinion. Thanks for watching, Diego.
when you stack your steel on top of each other you draw it out then you crush corners for your C then do you flip the billet on its side so the layers are different than when you started. i hope i explaind it as best as i can
When you stack your steel, you keep it in that orientation to crush the corners. Then you turn it 90 degrees so the layers are running up and down and press the bar flat. Make sense?
I have what is probably a silly question but what would happen if you did a bar of twist pattern and stacked it like you would for a feather? Then split it just like you would a feather. I’m sure it’s probably been done but I’m wondering what the pattern would look like.
You'd get some weird twist that wouldn't really be that recognizable. Plus to get a twist that thick it would have to be a twisted bar stacked on itself. I'm not sure what it would look like but probably something akin to a crushed W feather. Thanks for watching, Bill.
Second! 2 is a bigger number so I totally win ;)
haha! Thanks for following along!
Cool build.
Thanks for watching, Chris
Great video, should be in schools
Thanks so much, Josh! I appreciate you watching.
Hey Denis,
Another great video! Now I'm going for the Tig welder and will have to get an Argon cylinder. What size do you use, and what regulator? Thanks again for all that you do. Please continue the great work!
I just have a 60cf tank and a basic reg off of Amazon. Thanks for watching!
you make it look so simple
Ha, well I’ve made all the mistakes already in previous builds. 😜. Thanks for watching
Nicely done
Thanks for taking a look!
As a non knife maker I understood the first uses of Damascus was for increased blade strength. Do all these modern variations also add strength?
But you need to consider the steel from that period was terrible by today's standards. They first took bloom steel created in a furnace and then combined different steels in a crucible and melted them together to form traditional damascus or what we call "wootz" steel. This was stronger because it removed more impurities that plagued steel of that period. Today's modern steel is very pure and MUCH stronger so modern damascus is done by layering different kinds of steels to produce a pattern. In itself, it is not stronger but actually can be weaker than the original steel if not done correctly. You are forge welding those steels together and if any weld isn't done right, it introduces a point of failure. I hope this helps. Thanks for watching.
Just an interesting fact, fusing / welding without filler material is called autogeneous welding and in my experience is mostly used with plasma welding
Thanks for taking a look!
Super awesome
Thanks for watching!
Awesome video Denis (as usual). An idea for the river of fire. I am curious what it would look like if you layered in a little 15N20 with the 1084 on the edges or even get a little crazy and substitute the 1084 for some cu mai.
Sure, you could even do Damascus edge bars, though you’ll grind a fair amount away. For this spear build I want the “shore” to be black. 😉. Thanks for watching.
You can buy wire for AR 500 that's a lot harder than typical ER70 wire for mild steel? I'm not a blacksmith but been a welder for 40 yrs, don't know if that helped or not?
That wire would still not be the hardened steel that matches the steel in the work you're doing. It would show up differently when etched and look like a blotch. You don't want to introduce any different steel into the work piece and I very much doubt you'd find exactly the same steel in a wire for a mig. Thanks for watching.
Feather is my favorite .I don,t have a press. Could I do a simple by hand?
As it is a variation of hot cut, it should be doable by hand, depending on the size of the piece would probably require a few reheats
I disagree a bit, I don't think feather is a pattern you can realistically do by hand. The problem is the number of layers, the crushed W's and the forge weld of the tall stack are incredibly challenging to do without a press. Could you do it with enough time and effort, sure. You're probably going to need 3x the amount of steel though because you're going to lose so much steel to scale.
@@TyrellKnifeworks Thank you sir
Did the blade deflect during the cutting of the billet?
Yes, the wedge actually deflected. I had to hammer it straight after that. It’s 1/4” thick! Thanks for watching, Dan
Your videos are so informative I just subscribed. I have a 20 ton press and it seems to work hard doing this. How big of a press would you recommend? Thankyou Sir.
20 tons should be plenty to split a feather. Just do it slowly and make sure the billet is very hot. My press is only 28 tons, so not much more than yours. thanks for watching, Joe.
@@TyrellKnifeworks Thankyou Sir. I'm looking forward to learning more from your videos.
Really cool
Thanks for taking a look, Daniel!
@@TyrellKnifeworks thank you I'm learning a great deal from your work 👍
Perfeito ! Obrigado.
Obrigado por assistir!
Hey Denis, would this Vevor tig torch work well for making oxygen free billets? If so, how do you like it still? The link is now expired as well. I think I found the same one on their page, but it looks a bit different now. Thank you
That’s exactly what I use it for… fusing Damascus without adding filler rod. I really like it. It has a HF trigger start, not lift-TIG like the Titanium. The price is great on these as well. (Note, you’ll need a 100% argon bottle).
it is posible to combine like fether damascus and turkish twist?
I always consider a twist on its own. Once you twist something, it really muddies the pattern and you lose any other pattern you did unless the twist is very loose. Generally its better to treat these on their own. Thanks for watching.
Could this be combined with the raindrop pattern to add eyes to the feather, like a peacock?
You won’t actually see rings though when you do the holes. The feather pattern goes the other way through the billet. You’d get something but it wouldn’t look that circular and not like eyes. Thanks for watching.
😮 sooo cool
Thanks for watching, Marty! 😉
I really enjoy watching your videos. Very impressive and informative. Have you watched any videos from Manuel Quiroga? He has only a few out on youtube but does some fantastic work. If you haven't seen any-check him out. Not sure if this is listed under the full name or not Manuel Quiroga Güiraldes.
I’ll have to check him out. Thanks for watching, Jonathan.
Best 3 pairs of tongs for the newbie knifemaker?
#1 Bolt jaw tongs, #2 Z Offset tongs, #3 Wolf jaw tongs. Some people like box-jaw tongs but you need a bunch of sizes. I hope that helps.
@@TyrellKnifeworks thanks again!
I broke down and bought a higher end yes welder tig/stick.
For the amount of welding I do, I can’t justify an expensive welder. I’m sure you must do a fair amount at work?
@@TyrellKnifeworks agreed! The yes welder I bought was 450 they have a lower end model that’s about 279. People seem to like them and they have pretty good reviews. No way I’m spending the money for a miller to fuse billets!
@@HeavyForge The vevor multi-process with a foot pedal for tig is only $520 so that's a great deal. I wish I got that one instead. 🤣
hey Tyrell Cj here from grayson Ga qt can you tig weld without the gas
No, you can’t tig weld without shielding gas. You need the 100% argon or what you’re welding just oxides. Thanks for watching.
@@TyrellKnifeworks and thank you for the responce and happy new year to you and your family
Excelente..
Obrigado por dar uma olhada.
Wait, what?! 200 bucks for a TIG machine? Might have to grab one 🤔
Remember though you need an argon bottle and reg, so that's another $200. Still, $200 bucks for a welder is a crazy good price! Thanks for watching.
Idk why but I somehow always expect you to say "Tools, tips and tacos"
Hmm.. I love tacos! Maybe I'll add that in the future. 🤣. Thanks for watching.
@@TyrellKnifeworks Hehe :) Thanks for an awesome video, as usual. I respect your knowledge.
I’m unable to pull up your website
I just tried and it’s working fine. Http://www.tyrellknifeworks.com
@@TyrellKnifeworks it’s working now, if only to make me look dumb 😁
@@BulykrynVancho No worries, thanks for letting me know.
@@TyrellKnifeworks side note: would love to see this pattern on a butterfly knife
That tungsten was sticking WAY TOO FAR outside the ceramic cup on your Tig torch. Also on the Tig welding, you don’t need to only use the mild steel Tig rod like ER70S or simply fusing the steel, you can actually get high carbon steel wire like 1080 wire from McMaster-Carr on a roll in various diameters so you are welding with steel that can be incorporated into the Damascus without needing to be completely ground out
As you can tell, I’m no expert welder. Thanks for the tips and thanks for watching.
@@TyrellKnifeworks you should really try using a foot pedal if your new welder will accommodate one, either a foot pedal or a thumb wheel on the torch as they both function the same just one uses your foot to turn on and turn up the juice and the other has a thumbwheel that rotates to do the same thing
@@peltiereric6497 It doesn't support a foot pedal. It just has the button for gas/HF on/off.
First!
You guys are funny! Thanks for watching!
What ever that cutting wedge was made of you injected that in your blade
No, it just melted back. There's no mild steel in the billet, you'd see it in the etch if there was. This wasn't my first time using this wedge. Thanks for watching.
As i recall when i first learned how to use a TIG machine was rule number 1: Don't touch the electrode to the work piece because it causes contamination of the weld. So im wondering what the maker of your first machine was thinking...
Love the series btw :)
It's very common to have a lift-tig start on the lower end machines. When they mean that rule, it was after the arc is started. Thanks for watching.
so it's like a feather/serpent pattern
Yeah, I guess you could call it that. Thanks for checking it out.
218th😎😂
🤣🤣 Thanks for checking it out!