BGA Bottom Parts Gold And Silver Recovery | Recover Gold And Silver From BGA Chips
Вставка
- Опубліковано 1 чер 2022
- Hello Viewers,
In this video, we are showing you how to recover gold and silver from BGA Bottom Parts.
We already have shown you how to recover gold from BGA IC Chips And BGA top parts.
Here's a separate video for the BGA bottom parts
#ewaste #ewasterecycling #goldrecovery #silverrecovery #goldmelting - Наука та технологія
I'm impressed. Not too many people would do this, meaning do gold recovery video of BGA bottoms. Most people say that they're worthless.
✌️✌️
Dear Shane, Your presence makes me happy and enjoyable. Thank you very much.
I checked your website and got very useful information. I wonder if you leave a link to buy the tools you use on your site.
Hey guys I've watched several of the videos more than several what question is how do you make your compels or your melting dishes what do you use thank you. 🤔👍😎
I noticed you often dissolve gold in unheated aqua regia, looks like it's hot outside 😉 My gold plating does not dissolve without heating. Good video 👍
The sulphuric acid does the heating
@@TrinityGoldRecovery 100%. I just didn't notice that you added sulfuric acid😉
Very good 👍🏾
Where do you get your filter fabric and the little clay bowls? In the removing green solder masks video I noticed you had several pieces with the little black blob on them. If you use heat and a scraper those will come right off. There are gold wires beneath them. I enjoy your videos. Where do you live?
Good video sir👍
With lots of love💞
Beautiful video! Thanks! 🌟 👍
✌️✌️
What did you mean by saying "Beautiful video!" 😁
What was beautiful in the video, their hands or the reaction of nitric acid? 😅
@@akgoldbear7669 I like the way they present the processes.
Beautiful!
✌️✌️
Thank you, Mr. Thomas Anderson
Nice video sir
Mantap 👍
May I ask how long does it take to complete a fabric and cotton filters ? Especially the silver solution will starts dropping slowly due to the presence of thick sludge until its completely stopped passing through . I will use a vacuum pump.
Hmm depends on what the sludge is
Try to decant solution before or into filter. Keep most of the said sludge, in beaker and dilute with water a few times and decant. The more that ends up in the filter early, the slower the flow.
Another tip. Don't wet filter paper before adding a non-diluted solution. The filtering will be faster, if the solution is the first thing in.
Show, mande sempre vidíos abraço.
Excellent program i like your videos
✌️✌️
I have a question-when you put some acid or aqua regia in the plastic bucket why doesn't it gets corrode or why doesn't it melt??
Are there any gold bonding wires inside the bottom?
Wondering if it's worth further processing if there are any bonding wires inside them.
I saw Idelelectrotech burn the fiber boards on flip chips to release gold plated circuit trace.
Yes you can see by pausing video there is gold wire left inside, this isn't the perfect way to recover, it should have to be treated with sulphuric acid first 🤦
Ok mantab👍👍
Big question herw what percent of each chemicals are u using .my hydrochloric acid is 31.0 percent cant remember what my nitric acid is.what are you using
Thank you sar love you Pakistan
✌️✌️
One time I had exactly the same kind silver chloride solution, its not Settle, also passes from smallest filter, after 1 days only small thin layer form’s at the bottom of water ..
.. make me tired and finally I poured it out.. i think its about 6-8g silver.. now I thinking i did so stupid things because there is a way for recovering them..
That was amazing! Im saving mine up! I have close to what you had in the video. All the gold I got from the tops I evaporated trying to refine it. Ughh.😔
Nice work!
No cuadra la cantidad de gramos de oro???
Doesn't it take the outer coating in the nitric acid process because there is very little output this time?
The amount of gold from their material is normal. I would be surprised (in a bad way) if they got more.
I have another question, why they use so many acids? 🤔
@@akgoldbear7669 I think it's better this way because neither too much nor too little material is eye-catching.
wonderful
✌️✌️✌️
Qual é o pH para baixar o ouro
It didn’t work out very well because theres copper chloride and tin mixes in with the silver.
What is the solution?
Pour 0,5litre H2s04 firt stir it well and filtering using fabric the lead will perticipate. Then use nacl to perticipate the silver
The balls are not completely silver. Tin and silver and great work as always. Hope you're doing well
Yes✌️
I find if theres another base metal i wasn't expecting and i messed up; Just add more water and acid until i get back to where i should be.
Then use lesson for next time haha.
Those damn tin balls got my solution so hot so fast, that i had my first boil over, (into my pyrex rescue cassorole dish) when i first tried some bga bottoms.
I put the silver/tin solution into my low grade pins waste bucket, as dilution and adding acid over and over basically is the point in there. 😉
Very nice video.👍🏻
Nice new crocks to😁
✌️✌️
@@TrinityGoldRecovery I watch all your videos keep up the good work take care.
👍
반갑습니다 😁
To begin with, what is the equation of nitric with water?
Did you put 1 nitric and then 3 . water?
After that, I used Captique
1: 2 HNO3: H2O, you can follow the same ratio 1: 3 HNO3: H2O, but I was wrong that it should have been dipped in hcl for 24 hours to dissolve lead and tin.
👍👍
What kind of nitric acid is used to gold recovery and silver recovery
Commercial
а что это за расствор такой соляная+ серная + азотная кислота ? ( 9.30-9.50 ) что то новенькое в расстворении золота
The hydrocloric and nitric acid eats the gold and the sulfric acid will get rid of any left over metals. Hope this helps
can i use filter paper in every progress instead of cotton ?
yes you can!
very good work.. some of gold under green..
Is it? you serious ?
@@TrinityGoldRecovery yes my friend.
@@TrinityGoldRecovery burn it
I'll ,thanks dear friend...
@@TrinityGoldRecovery welcome
Hi so how did you sort out the silver?
You only showed half of processing and how was the silver solution extracted.
Lost me.i see green liquid then shown silver.how did you get it
Столько гемора с етимы отходамы!))) Лучшие отложить на тяжолые времена!) Лайк вам ✌️🤗
Слабо что то вышло... С 1600грамм, даже 0.1% не вышло! Не верю
@@Gold-fever 🤔🥴😏
How much HNO3 and H2O at the first stage of separating silver and gold from the BGA?
Can you tell sir please 🙏
Kapan ya bisa membuat emas
My dear sir the HCL you use looks like yellow but I bought HCL 32% industrial grease from the shopkeeper it looks like white but it works. I want to know what is the difference with the HCL you use please my dear sir
HCL can gradually change color and acquire a light yellowish color after exposure to air.
@@TrinityGoldRecovery thank you sir 👑
Nice shoes. 👍. You didn't show how you got the silver from the blue solution.?
I believe the tin in the balls led to the white powder or metastannic acid (H2SnO3) that formed before the first filtering. My assumtion is silver is in either in the metastannic acid in the first filter, (where the silver dropped out of solution overnight.) Or it is in the left over solution.... but i find it harder to make sense for it to be there. Unless something is keeping it more stable then the AgCl. But if it's silver nitrate (AgNO³) and chlorine is available it should convert. My last thought would be, if it is there, add heat perhaps to convert.
I laughed at the perhaps risky shoes originally. Then somehow i ended up in almost the same pair on hot days. Easy to rinse quick 😉
@@colonialcharlie8702 You should of seen his old shoes Lol. One way to get around the metastannic acid acid is to use boiling sulfuric acid instead of nitric acid.
@@toomuchdebt5669 oh wow went back and noticed the nice new ones. (Still looks like crocs) Yea mine are like the old ones bahaha
Hi, my silver solution is just like yours. It doesn't percipitate. How did you solve this problem?
I sifted the whole silver chloride on the filter paper and washed its acidic properties with clean water. Then I left silver chloride overnight with HCL. HCL dissolves all tin metals and other base metals except silver.
@@TrinityGoldRecovery Yes. The metastannic acid can cause all sorts of problems.
Hey guys how much is a 1 kilogram of old cpu worth?
Why are you dont use hydrazine hydrade?
May not be easily available in his location. I see people from turkey use it to drop gold.
Everyone uses what they like best. I used hydrazine hydrate but now I using only iron sulfate which I make myself. Only myself 😉
Gold check ing chemical details
What about the silver? How did you recovered it?
Cpu 작업이네요
무슨 말을 하려던 겁니까 ... 작업이네요 😀
+196 👍👌🎓
팔라듐 추출 영상 한번 올려줄수 있어
No discussion about the cost of various acids, chemicals, if you have to buy all these it makes all process poitless.
I think , it's a little Palladium in this balls ..
From these chips you can get copper, brass, silver, gold and tin🙂 Sometimes bad manufacturers add lead 😥 There no any palladium😉
@@akgoldbear7669 ok
Ha ha ha!!!
Time west
Did silver not work out bc mistake or bc the balls are really tin?