I love welding Titanium, almost becomes magnetized. Love when it pulls the filler rod into the puddle. I cant wait to start another Titanium project! Love the channel!
Couple things that will help.....don't handle filler rod with bare hands, don't remove filler from Argon envelope while it's hot. You can brush oxides off tubing before continuing bead.
Hay man..dat waz 'tooo-easy'..asme 9 boilie/welder me-self n wouldn't mind having a go at titanium welding..done carbon n stainless steel.. good tutorial lessons n skill..well done.. awesome vid 👍
Could this be done lengthwise on a smaller diameter, irregularly shapped tube? Wondering if I could weld some cracks in an old titanium lacrosse shaft. Thanks!
Great job and very informative, i do mostly SS and just got a quotation in for some Ti welding. Do you mind posting the spec of your cup and Ti filler rods you are using.
Can you guys show us how to prep a bevel to practice , i normally use a torch with butane as acetylene is way too expensive here in Mx , and i always have a hard time on preparing the plates , hope 2 hear from u guys soon
Is it a fact today that the weakest part of a titanium frame, or the most likely failure point, the welds? True of bicycle frames and non bicycle frames or anything built with Ti?
I think your wire sticks because it's a small diameter wire and the shake of the wire itself it makes to sticks.. its happens with an others tipe of wires
Thanks for your encouragements and the advises. Your ZTA is too large. It's 10mm max. The pin holes are there for a few reasons I saw. You're going too slow, your arc is too long at the same place at the end, your tungsten tip is maybe not the right shape including the top shape. I polish my tungsten tips and it makes all the difference. And at the end, instead of staying at the same place to make a hole, I do a spirale while getting away slowly from the too close distance to help stop the arc faster than my foot on the pedal. Excuse my English, it's not my first language. Cheers 😉
Why are you not wearing a cotton glove on your feed hand?! You discuss using acetone and not touching the tube after you clean it to prevent transferring oils, but you are putting your oils all over your filler. I weld titanium most days and you are spot on with the straw color and cleanliness otherwise. We, in aviation, have very strict tolerances and you discuss your shop in the video. I get the impression you try to go above and beyond which is great but this is a very simple step, SAFETY WISE TOO, to just toss out. The weldment looked great and I'm not trying to bust balls but I couldn't watch and not mention this. Thanks for the video!!!
You only need a 10 second post flow if you have a trailer running behind for the gas coverage.... you also only need to bump up the Argon. to the same gas flow as the torch. Your torch is working way too hard.....! gas flow should not be that high, and neither should amperage....
Bunch of misinformation in the first few minutes of this video.First off you don’t run 1/2 your cup diameter you can run the full diameter of your cup and second you don’t need to hold you post flow over a tack for 15 seconds, once the red glow is gone plus a few more seconds to cool off and you can move on without getting color. running 1/2 inch at a time is ridiculous, I use a #16 cup (1”) and run 1” beads with no discoloration, if you know how to balance amps/travel speed to get the right heat input you won’t get colors and sitting over a tack for 15 seconds is a complete waste of argon. Should you wait for 15 seconds of post flow after a full bead? Absolutely you should but that 1” bead needs A LOT more time to cool than a single tack. Thought this channel would have better info. I’m disappointed
👇WeldTube Store👇
www.weldlife.com
Just caught this video,
Any possibility you have fabricated a exhaust for a motorcycle?
I love welding Titanium, almost becomes magnetized. Love when it pulls the filler rod into the puddle. I cant wait to start another Titanium project! Love the channel!
Discount code warriorweldingtx for 10% off
www.weldlife.com
Weldtube Online Store
Hello guys 🙌 i have so many videos about JAPAN STRUCTURAL WELDING WORKS,PROUD WELDER HERE
I love love love Ticon Industries. They really help me get started in Titanium welding.
Couple things that will help.....don't handle filler rod with bare hands, don't remove filler from Argon envelope while it's hot. You can brush oxides off tubing before continuing bead.
That first tack weld doesn't look silver, it looks like a diamond lol.
mind you dont get a chug nut stuck up your nose 😄
Bonus tips: Be careful to not blow your gas by flipping your hood and keep the end of the wire under the gas
Yup, I was running a 2 second pre flow to eliminate any issues there, good lookin out!
@@Warriorweldingtx id also wear silicon glove or something similar on the feeding hand. The oil on your skin can and will contaminate the wire.
@@Thorn19774 I knew someone would call me out on that lol
@@Warriorweldingtx lol im guilty of it too sometimes youre in a rush and if it aint goin to x ray ¯\_(ツ)_/¯ its a good habit to keep for sure though.
My dream as a new welder is to build a titanium bicycle. Great video, thank Matt.
If you like titanium welding have a look on my channel 😁
Titanium? Dayum
11:17 hahahaha! Thanks for this video, Matt's stuff is always very helpful and entertaining.
Thank you for watching! 🙏🏻
Good video. Can’t beat a good titanium exhaust system 😉
Hello guys 🙌 i have so many videos about JAPAN STRUCTURAL WELDING WORKS,PROUD WELDER HERE
That’s where a high frequency rig comes in!
I really love your job guys. Your knowledge inspire me. Thanks for all.
What size of cup should be used to do tube to tubesheet joint of titanium gr.2. size of tube is 32mm & 1mm thick.
I really dig how you can "backfire" like those exotic cars! Bappa Bap Bap
Nice demo, bro. Do you have a purge cabinet for big headers and odd shapes?
I run 3 second post flow on my tacks and get silver tacks every time. quick burst on tacks. need perfect fitment tho or you're in trouble
Hay man..dat waz 'tooo-easy'..asme 9 boilie/welder me-self n wouldn't mind having a go at titanium welding..done carbon n stainless steel.. good tutorial lessons n skill..well done.. awesome vid 👍
What name brand is that long sleeve black welder shirt ? I like it
Just a wrangler black pearl snap 👌🏻
Could this be done lengthwise on a smaller diameter, irregularly shapped tube? Wondering if I could weld some cracks in an old titanium lacrosse shaft.
Thanks!
What are the most commonly used thicknesses in titanium pipes?
Really appreciate your knowledge.........thank you kindly
Nice video. Very informative stuff. We don't work with much titanium in the pipe fitting industry an I was curious how to weld it.
If you like titanium exhaust have a look in my channel 😁
Great job and very informative, i do mostly SS and just got a quotation in for some Ti welding. Do you mind posting the spec of your cup and Ti filler rods you are using.
You need to pull from end to end the tension out of that welding trailing shield curtain to get rid of the puckers/waves in it.
Can you guys show us how to prep a bevel to practice , i normally use a torch with butane as acetylene is way too expensive here in Mx , and i always have a hard time on preparing the plates , hope 2 hear from u guys soon
What current did you use?
Completely unrelated, but which wrangler button up is that? We don't have any where in canada that stocks the good stuff so I need to order online!!
Good videos tutorial brother
Sweet demo, quick as quick can B
Hey! What was its amper?
Is it a fact today that the weakest part of a titanium frame, or the most likely failure point, the welds? True of bicycle frames and non bicycle frames or anything built with Ti?
Very good video pro
What size rod use ? 1/16 or 3/32 🤔?
Cool tehnology.
Can you make a video of titanium tig welding in spanish Please??🥺
I think your wire sticks because it's a small diameter wire and the shake of the wire itself it makes to sticks.. its happens with an others tipe of wires
Thanks for your encouragements and the advises.
Your ZTA is too large. It's 10mm max.
The pin holes are there for a few reasons I saw. You're going too slow, your arc is too long at the same place at the end, your tungsten tip is maybe not the right shape including the top shape. I polish my tungsten tips and it makes all the difference. And at the end, instead of staying at the same place to make a hole, I do a spirale while getting away slowly from the too close distance to help stop the arc faster than my foot on the pedal.
Excuse my English, it's not my first language.
Cheers 😉
Stainless RMD!
#weldlife🔥🤜🏽🤛🏽
💯 🦅
I want to buy welding machine with torch... I live in Hanoi city
Indonesia Malaysia like to me welder asiaa.. 👍👍👍👍👍🙏🙏🙏🙏
Bro i am welder..form Qatar..Ac.mig.tig.
Where are you from..
Bad ass!
They never show stainless stick cap on pipe in 6g position
Anyone else here that wanted to see the inside of the tubing? Haha
👍👍👍👍👍👍👍👍👍👍👍👍👍👍👍👍👍👍👍👍👍
Why are you not wearing a cotton glove on your feed hand?! You discuss using acetone and not touching the tube after you clean it to prevent transferring oils, but you are putting your oils all over your filler. I weld titanium most days and you are spot on with the straw color and cleanliness otherwise. We, in aviation, have very strict tolerances and you discuss your shop in the video. I get the impression you try to go above and beyond which is great but this is a very simple step, SAFETY WISE TOO, to just toss out. The weldment looked great and I'm not trying to bust balls but I couldn't watch and not mention this. Thanks for the video!!!
How can I get into aviation welding @brandon McElroy
How can I contact with you
I know all about that sticky puddle
Muito bom 👍
Why do you use a standard helmet and not an auto darkening helmet
It is an auto
Wont get as clear a view through any auto than you will through a passive lense anyways. Especially a gold coated lense👍
@@kf8575 the weldbeast lenses are actually clearer than any passive lens I’ve ever used
@@Warriorweldingtx
did you add the flipping lens yourself onto the Helmet ?
or are they available readily in this style ?
thx in advance !
Love me them fupas 😏
You only need a 10 second post flow if you have a trailer running behind for the gas coverage.... you also only need to bump up the Argon. to the same gas flow as the torch. Your torch is working way too hard.....! gas flow should not be that high, and neither should amperage....
that trailing cup was to large and bro put on a glove so you don't end up with cancer
That is a 6G process
6G is a position, not a process
8 minutes per weld...... just wire brush it or passivate after welding
Bunch of misinformation in the first few minutes of this video.First off you don’t run 1/2 your cup diameter you can run the full diameter of your cup and second you don’t need to hold you post flow over a tack for 15 seconds, once the red glow is gone plus a few more seconds to cool off and you can move on without getting color. running 1/2 inch at a time is ridiculous, I use a #16 cup (1”) and run 1” beads with no discoloration, if you know how to balance amps/travel speed to get the right heat input you won’t get colors and sitting over a tack for 15 seconds is a complete waste of argon. Should you wait for 15 seconds of post flow after a full bead? Absolutely you should but that 1” bead needs A LOT more time to cool than a single tack. Thought this channel would have better info. I’m disappointed
Mit.drehtisch ist einfach........mal nicht drehen und von unten nach oben schweißen!!!!
SUB ESPAÑOL O DISLIKE
Stainless RMD!
Coming soon👍