Hello Sebastiaan, and Thank You for this video! I do not speak Dutch, but was able to see the torch control and to understand the basic technique. There are few videos that show the detail as well as your video. I was almost ready to give up my attempts at torch-fired Plique-a-jour enameling, but now I am excited to try again . . . and again! Cheers from the USA!
Really nice to hear you like it and that I could be of any help. Please let me know how it works out for you. If you have any questions, please let me know. Succes!
Hello again with a question: The enamel grains appear to be held with a binder ? If so, what concentration works for you? Thanks, and Best Regards, James @@Streamcatcher
Hey Lana, I cut it by hand. Although casting would be my method next time. It is very labour intensive, specially because of the tiny holes. Are you planning to make something like this? 👍🏽
@@Streamcatcher yes! I am. I will make a bracelet, so it’s a bit tricky because of the shape as well. There’s no many videos about this, thank you for yours and for your kind answer!
Dankjewel voor de uitleg ! Ik wist niet dat je emaille kon trommelen. Kan je niet eventueel de blaadjes van draad vormen en solderen met extra hard dat zal toch veel sneller kunnen dan uitzagen? Ik vindt zagen erg leuk om te doen. Als je moeite hebt om kleine onderdelen vast te houden probeer dan eens thermo lock dat is bij meerdere toepassingen erg handig. Ik weet niet of je dat kent het zijn plastic staven die je in de magnetron of met heet water zacht en kneedbaar kan maken daar druk je dan aan een kant je werkstuk in en kan je het beter vasthouden. Wat voor sieraad heb je gemaakt van met die blaadjes aan het eind van de film? Heb je eens probeert om een heel fijn penseel te gebruiken ipv een soldeer pen om de emaille aan te brengen? Top sieraden hoor ik ga het binnenkort eens doen, ben benieuwd hoe het gaat, ik smelt alles denk ik 😅😂 ik krijg met mijn little torch geen klein vlammetje voor elkaar, gaat altijd uit hahah waarschijnlijk te veel druk.
Hoi Diana, graag gedaan! Zoals je zelf aangeeft, zulke kleine complexe vormen uit losse draadjes maken is hoogst waarschijnlijk niet makkelijker dan uitzagen. Het makkelijkst zou zijn: laser snijden of gieten vanuit een 3d print lost wax methode. Thermolock gebruiken wij ook, alleen zou het niet veel toevoegen in het geval van solderen, de thermolock zou heet worden en zacht/smelten/verbranden, afhankelijk van hoe dichtbij de soldeerbron de TL je onderdelen vast houdt. Thermolock wordt meestal gebruikt voor zet en graveerwerk. Ook is de vorm van losse draadjes niet de vorm die ik met uitzagen kon en wilde bereiken. Een kleine vlam kan zeker met de little torch, maar de druk en kop grootte moeten goedmatchen met elkaar. De kleinste soldeerkop heeft maar heel weinig druk nodig, iets wat je met een extra regelknop bij je gasfles zou kunnen afstellen. Een kwastje heb ik ook gebruikt, maar dat vond ik soms te swabberig, er zijn wel hele fijne kwastjes waarschijnlijk, maar een puntig staafje vond ik even goed werken. Op mijn site: www.sebastiaanstevens.nl kun je het eindresultaat zien van de oorbellen in deze video.
Heel erg leuk dat de techniek zo goed wordt uitgelegd. Bedankt
Hello Sebastiaan, and Thank You for this video! I do not speak Dutch, but was able to see the torch control and to understand the basic technique. There are few videos that show the detail as well as your video.
I was almost ready to give up my attempts at torch-fired Plique-a-jour enameling, but now I am excited to try again . . . and again! Cheers from the USA!
Really nice to hear you like it and that I could be of any help. Please let me know how it works out for you. If you have any questions, please let me know.
Succes!
Hello again with a question: The enamel grains appear to be held with a binder ? If so, what concentration works for you? Thanks, and Best Regards, James @@Streamcatcher
Hey Sebastian! Did you make this piece by cutting directly on the metal, or is it lost wax? I would love to know! Thank you!!!
Hey Lana, I cut it by hand. Although casting would be my method next time. It is very labour intensive, specially because of the tiny holes. Are you planning to make something like this? 👍🏽
@@Streamcatcher yes!
I am. I will make a bracelet, so it’s a bit tricky because of the shape as well. There’s no many videos about this, thank you for yours and for your kind answer!
@LanaLeon nice, good luck and please let me know if you have more questions
Dankjewel voor de uitleg ! Ik wist niet dat je emaille kon trommelen. Kan je niet eventueel de blaadjes van draad vormen en solderen met extra hard dat zal toch veel sneller kunnen dan uitzagen? Ik vindt zagen erg leuk om te doen. Als je moeite hebt om kleine onderdelen vast te houden probeer dan eens thermo lock dat is bij meerdere toepassingen erg handig. Ik weet niet of je dat kent het zijn plastic staven die je in de magnetron of met heet water zacht en kneedbaar kan maken daar druk je dan aan een kant je werkstuk in en kan je het beter vasthouden. Wat voor sieraad heb je gemaakt van met die blaadjes aan het eind van de film? Heb je eens probeert om een heel fijn penseel te gebruiken ipv een soldeer pen om de emaille aan te brengen? Top sieraden hoor ik ga het binnenkort eens doen, ben benieuwd hoe het gaat, ik smelt alles denk ik 😅😂 ik krijg met mijn little torch geen klein vlammetje voor elkaar, gaat altijd uit hahah waarschijnlijk te veel druk.
Hoi Diana, graag gedaan!
Zoals je zelf aangeeft, zulke kleine complexe vormen uit losse draadjes maken is hoogst waarschijnlijk niet makkelijker dan uitzagen. Het makkelijkst zou zijn: laser snijden of gieten vanuit een 3d print lost wax methode. Thermolock gebruiken wij ook, alleen zou het niet veel toevoegen in het geval van solderen, de thermolock zou heet worden en zacht/smelten/verbranden, afhankelijk van hoe dichtbij de soldeerbron de TL je onderdelen vast houdt.
Thermolock wordt meestal gebruikt voor zet en graveerwerk.
Ook is de vorm van losse draadjes niet de vorm die ik met uitzagen kon en wilde bereiken.
Een kleine vlam kan zeker met de little torch, maar de druk en kop grootte moeten goedmatchen met elkaar. De kleinste soldeerkop heeft maar heel weinig druk nodig, iets wat je met een extra regelknop bij je gasfles zou kunnen afstellen.
Een kwastje heb ik ook gebruikt, maar dat vond ik soms te swabberig, er zijn wel hele fijne kwastjes waarschijnlijk, maar een puntig staafje vond ik even goed werken.
Op mijn site: www.sebastiaanstevens.nl kun je het eindresultaat zien van de oorbellen in deze video.