Buddy, if you don't understand it then just keep on moving, nothing for you here. You can always just go back and watch the "yoga butt" & "Big Booty Close Up" videos that I see you have favorited.
Most of my big chunks of lead came from a sailboat keel. If you haven't already seen it then check my video about how to find free and cheap lead. Thanks for watching!
Do you feel that this is a more accurate way of getting the BHN over the Lee tester. I just got my Lee in the mail today and it seems much easier to set up.....Now the dial indicator on yours seems much easier to read than through the microscope. Just wondering your thoughts?
There are two areas that need to be modified here, the point should not turn into the sample, this should remain pushed straight in by being free to rotate, an easy modification, and the end of the thrust plunger, that the dial indicator rests on should be dead flat, another easy modification, these two mods will make it a much better tool.
That was a long time ago. If memory serves the readings were repeatable once you learn how to operate the device in a consistent manner which includes proper placement of the material. I have not needed to use this tool lately but when you need it... priceless.
Buddy, if you don't understand it then just keep on moving, nothing for you here. You can always just go back and watch the "yoga butt" & "Big Booty Close Up" videos that I see you have favorited.
Most of my big chunks of lead came from a sailboat keel. If you haven't already seen it then check my video about how to find free and cheap lead. Thanks for watching!
The Ammo Channel
Thanks for the demo.
Do you feel that this is a more accurate way of getting the BHN over the Lee tester. I just got my Lee in the mail today and it seems much easier to set up.....Now the dial indicator on yours seems much easier to read than through the microscope. Just wondering your thoughts?
Did you say "ku-bine"? as in carbine? I though it read cabin as in tree cabine in the woods.
There are two areas that need to be modified here, the point should not turn into the sample, this should remain pushed straight in by being free to rotate, an easy modification, and the end of the thrust plunger, that the dial indicator rests on should be dead flat, another easy modification, these two mods will make it a much better tool.
how repeatable are the results. you took several from the same lead weight, how consistant were the readings
That was a long time ago. If memory serves the readings were repeatable once you learn how to operate the device in a consistent manner which includes proper placement of the material. I have not needed to use this tool lately but when you need it... priceless.