These are nice as cut then throw in the roller to make round. I make them small and want to do color star to crackle. I'm planning and 8 inch ball shell with red to green to crackle center mabey glitter to crackle havnt decided but thanks for sharing
Greeting Sir, Hope you are fine, I have made my magnalium powder 50mg and 50 alluminium with red lead and bismuth subcabonate with lequier but nothing explode or cracking like you kindly guide me what problem in my formula thanks
Good day to you friend. I am not sure about your problem. I am not familiar with your formula. It looks like to me the problem lies in the bismuth subcabonate with lequier. I Do not know about this. I am only experienced with my formula. Yours doesn’t look the same. There are too many differences. I don’t use red lead. My magnalium is commercially made that I purchase ( to insure quality) and I use bismuth trioxide not bismuth subcabonate. I am not a professional. Just a hobbyist having some fun and learning along the way. Good luck to you. There are many resources on the internet.
@@micropyro7470 Is the high copper low bismuth mix louder than other way around ? Btw: use 5% dextrin works better and is still not too much. If you go higher say 10% noise goes down a lot. I can only speak for 65% CuO and 30% MgAl 5% Dextrin If you want to test it also works well !
These are nice as cut then throw in the roller to make round. I make them small and want to do color star to crackle. I'm planning and 8 inch ball shell with red to green to crackle center mabey glitter to crackle havnt decided but thanks for sharing
Nice
Thank you so much sir
Use bright Al powder 5% of weight,Nitrocellulose lacquer (10%) for binding..Gives more sound...
Thanks. All I have is german dark right now. Maybe I try with that.
You need to cover the stars with black powder its make a little delay and its make its better
What is the coating formula you use for crackling star ?
Regular BP
Use a glas ball to mix them well😊
U should use 80-100 mesh mgal, it gives a louder bang, then can coated with titanium smolder composition
Bạn làm ơn cho mình xin thành phần phủ Titan được không bạn
@@hientruc5788 35kno3/15c/6s/6sb2s3/20 phenolic resin/25titanium/5dextrin
صديقي
ماهي المواد
وكم قياساتها
Greeting Sir, Hope you are fine, I have made my magnalium powder 50mg and 50 alluminium with red lead and bismuth subcabonate with lequier but nothing explode or cracking like you kindly guide me what problem in my formula thanks
Good day to you friend. I am not sure about your problem. I am not familiar with your formula. It looks like to me the problem lies in the bismuth subcabonate with lequier. I Do not know about this. I am only experienced with my formula. Yours doesn’t look the same. There are too many differences. I don’t use red lead. My magnalium is commercially made that I purchase ( to insure quality) and I use bismuth trioxide not bismuth subcabonate. I am not a professional. Just a hobbyist having some fun and learning along the way. Good luck to you. There are many resources on the internet.
Nc lacquer
I wouldn't use that stick in the mix. crackle mix is very static sensitive!!!!!!! BOOM!!!!!!!!!
Thats very little, you need a lot more for a yonshakudama😅
What is that machine u used to ball up the powder called??
Just a old drill motor from a battery powered one. Then I hook up a variable dc power supply to control speed. Leave the gearing and chuck on too.
Wish you would have filmed it.
Was thinking the same thing like nice we seen nothing of this. 😂
Use bismut and nitro way lauder....
Composition sir
Pb2o3 +MgAl +Cuo chemical composition
Used bismuth trioxide instead, lot less toxic.
@@micropyro7470 Is the high copper low bismuth mix louder than other way around ? Btw: use 5% dextrin works better and is still not too much. If you go higher say 10% noise goes down a lot. I can only speak for 65% CuO and 30% MgAl 5% Dextrin If you want to test it also works well !
i'm from Vietnam, can you give me a fireworks recipe?
Deveria ter peneirado.
You have a very very small concept of safety.
That should have been mixed by diaper method.
Don’t blow yourself up.
Glad I wasn’t the only one thinking this….
It's not that sensitive. Of course feel free to diaper anything you like if you're that skeeered.