MIG Welding 3g Vertical Open Root Plate Test
Вставка
- Опубліковано 29 вер 2024
- for a detailed article on this topic go to goo.gl/abO4Pi
visit the store here weldmongerstore...
this Mig welding test is used mostly as a preparation for pipe welding. The settings that you get dialed in for plate will also translate just fine over to pipe welding. Downhill root and uphill fill and cap is pretty common for pipe shops.
That looked awesome. Your definitely an inspiration to us younger generation welder. Every video you post has helped me in my welding career. I am working for Huntington Ingalls shipyard and everyday I try my best to become better and a Master of my craft. I just want to thank you on behalf of all the younger welders that have been truly inspired by your work and techniques. Thank you!
Jose Rodriguez:
Can you help me to get a job in your company
@@Thahir. sorry I no longer work there
@@joserodriguez2255 why’d you leave? that shipyard is a stone throw away from me
@@matarnold1371 contractors make more money
You have the best welding videos online. Cheers
R4-DRZ yea
R4-DRZ click on to big Ron at Motherwell Bridge 🌉 he is the best welder in the world, big Ron's the name welding is the game
Nice
That's cool.
Should do a stringer plate test. And why does no body do any dual shield videos in my 17 year career I've ran 1000's of miles of that stuff maybe its a PNW thing ??
Hi Jody; Going back to your Stick Welding Tips Vertical 7018, you said some testers were not allowing weaving because of too much heat input causing grain growth failure, how does it or will it apply to the weave when doing a mig vert. up, like in this video. It seems to have similar heat input to the work and if it causes a problem with stick welding, why wouldn't it cause a problem in mig welding also?Thanks again for your videos, your channel is great.
Hey Jody at 5:20 there's a whisker on the very bottom. Just curious to know if your plate would bust for that? Beautiful welds kick ass videos you are tha shit dude
Could you tell me you machine settings on the vertice uphill vgroove? I'm having issues with dialing in on this position. Thank you! I love watching your videos!
Suas aulas são muito top. Aprendo muito assitindo
Why don't you use a slight drag angle on your uphill passes? It should carry a hotter puddle and increase penetration.
great video
nice weld man
Mantap....the best
Very nice
where i work i got told that we should never weld downhill. I weld the rootpass on 6g and 3g uphill. is that wrong?
Not at all. A lot depends on the thickness of material, process, gas mix (if applicable), and ultimately, what does the WPS say. Up hill is a structural weld. Manufacturing uses a lot of down hand, some kind of wire feed process; usually with a spray transfer which allows the welder to use higher voltage and wire speed. Learn both, but if you have the uphill in control, the down hand should come to you without too much effort. But put some practice in on down hand, in case you run across a WPS that calls for it.
is this even possible ?!!! I was searching for videos doing uphill mig on rootpass but it's sooooo rare ! why is that ?? I heard that downhill is avoided because the lack of fusion and inproper penetration, but since it's an OPEN root I can't see why ??, without mentioning that you increase the risk of shooting the wire through and thus you loose the arc, I think it's more difficult.
Pickle sickle
In my apprenticeship program we was told the same thing, Not to run any pass downhill.
using LN -25 I passed 3G using a downhill root method. later learned how to uphill root was a bit more challenging for me.
Pickle sickle 8
no
Nice video
How much amp is 200 ipm?
only 19 Volt's ? 24> 25 Volt's at 400 to 450 ipm wire speed is what I am welding at !! it's really hot but you get some really good weld's
it's spay mode isn't ??
Thanks
God bless you all. It would be great to accept Jesus now. He died and rose so that we may live. Time is coming. He loves us. Why not live for Him?
🙏🏽
AMEN and GOD BLESS YOU TOO
We are here to weld. If i wanted to hear a sermon id go to church.
Yes he create him self, and he puts him self in the belly of mary, nice teory
Nice weld.I wish you would have cut it and shown us the penetration.(looked good)
I have had three or four welding classes and never learned as much as when watching you. thank you for you patience and excellent descriptions of what you are doing.
Please sir welding job in dubai
an alternative to a root with more penetration using a tighter gap like that would be to crank the voltage up to 18-19 volts & turn down your wire speed! like 18.5/180-190. was tricky learning that the longer i can keep the puddle molten, the more wire i can feed into it before it sets. when i started i just tried to turn it down & throw as much wire in there as i could do long as the machine ran well & what you start to realize is the roots sets faster the colder you go & the increased wire speed only fills the gap faster so it doesn’t necessarily give you time to break down the walls & let the puddle soak up any wire.
Going through welding school now and really struggling on uphill MIG, you've helped be out alot buddy, next week got the uphill certificate test coming and with your help I might even make it! Thanks.
lmao !!!! Jody you're the best! I love watching and learning from your show.
here in japan that first pass is done by putting or used a back chip ceramics for welding..we dont do downhill welding position..here in shipyard
I like this works so murch make proud of me I go every where in wold
In my school we are certifying with 4x7x3/8 plate in the horizontal position with a bevel (one flat, one prepared) with a 33 degree angle can you possibly make a video for that it'll be very helpful
I’ve watched this vid countless times and my root is flawless, hot pass looks pretty darn good but my cap tends to crowns and build up. Videos are so much help btw.
Your videos are so informative and precise. Currently in my final phase of welding school and we are doing bend tests. I needed this! Thank you!
You made it look simple. This gives me great confidence. Thank you.
Keep it Clean, filling, clean again ppl. UK is screaming out for Welder's. Good money too, i just got my Coded papers 👨🏻🏭
WWJD= what would jody do? This is a good statement to live by.
Hey Jodi I like all your vids very helpful, I have an issue with a machine I bought about two weeks ago it's a miller trailblazer 302, the problem I'm having is I'll set the machine to let's just say 120 amps and when I strike the arc and run a bead it reads at maybe 89 or 90 amps. Idk how to figure out this problem hope it's not a bad machine can anyone help thanks.
Kỹ năng thật giỏi “ mình là người việt nam, mình cũng đang học Hàn C02 , nhìn bạn Hàn đẹp quá
I was taught to always go uphill , i did my exam always going uphill, why did you go downhill during penetration? I passed my exam but can i got downhill on the first pass when i have another exam? Is it against the rules of the exam?
Thanks for the video. My welding instructor isn't worth a damn. I just got my 2g cert yesterday. Going for my 3g tomorrow. This video helped a lot. Thanks again
Jade Tighe if you don’t mind me asking , what school or Academy are you attending?
I have practice my down hill for 3g at NAIT, your demostracion it is perfect!!!
una pregunta amigo, que es mejor hilo tubular 1,2 mm o hilo tubular 1,6 mm en vertical. gracias.
I have a lincoln 350mp for more than 7 years and to date I have not been able to find someone to help me set the correct parameters to weld aluminum. It is for me the worst investment I have ever made in my life. I would be very grateful if you could help me make the adjustments. to the machine to see if I can finally use it I bought it for fun no one puts a video where I really explain how to adjust it in detail I would appreciate any help
I wished I saw this Video before I took my mig test. Great job btw!! Really helpful
An old timer taught me to butt weld with a bit of a lower wire speed than u normally would use and still keep the volts the same. This will result in a nice flat run
I also noticed at the very top of the plate that it gets almost too hot and the puddle recedes and draws the plate metal creating a divit per se at the very top. This is a problem I've had welding plate GMAW or smaw in the past. how can you prevent this while having well enough amperage to get good penetration but without causing that? Maybe sacrifice a solid bead for a tie in mid section hit it colder on the final segment? What do you say?
Whats a good voltage n wire speed to do this on 1/4 inch carb steel?
Thanks a lot ... I needed this one! I'm getting ready to weld up sum gates for my landscape trailer so I'm compiling my practice list for my horrible pre-weld day practice tries... LOL!
how many amps is he using?
can you make a video of a 3g mig welding test and all passes are traveling down hill. l need to pass a welding test and this is their requirements. it would be a great help thanks.
Excelente tutorial, muchas gracias por su aporte siempre muy importante para nosotros los soldadores
I need to practice my vertical up.. I tried it yesterday at work and it was freaking horrible smh
Practicing 3G downhill open root right now, except the teacher wants a 1/8 in. gap with 1/16 in. lands. I figured a bit of oscillating was necessary, but I guess not as long as you stay on the weld puddle.
Anyone have a recommended gas flow rate?
When the camera zooms in on the second pass it looks like you're angled up slightly am I correct on that?
On my test they made me go uphill on all 3 runs including root and the minimum voltage was 23 how in the hell do you pass that?
pra um profissional esse teste tá bosta.
esse trançadao é reprovado pela qualificadora.
Hey Jody. I appreciate your videos! They help a lot! I hear that you live in georgia. Heard that from my welding instructor at Georgia trade school. Would you be interested in helping out a new welder? Training wise. I can help you out with anything you might need. Work etc. Thanks again for the video posts!
Why do you need training if you were at this trade school? Did it suck and they didn't teach you much? The one I went to sucked ass like pretty much all trade schools. All they want is your 10-20,000.
Looks great have a question I have to do vertical on 3/16 plate form my job cant get my weld to look good its not the best looking ones haven't had them break on me but can you do a video on thinned plats than you
Jodii is a weldingg god wanna learn to weld combination in all positions watch jodiii took my welding to awhole nother level.
You ever going to show some videos using .045 wire? As in our shop we never use wire smaller then that.
Sir MIG welding starting se pura process revision karwaiye
At my tech school we do a end of course weld test for Seniors after our 2 year program. This year we did 3G mig. Everyone passed in my class. It was a x-ray test! Thanks Jody for helping me pass the test!
Were good your welding 👌
You should do videos on thinner gauge material like 1-2 mm. I'm trying to take a welding test and need to have some kind of reference.
I’m trying to learn vertical MiG but to pass the test where I work it has to be bottom to top
Sir I maintain the root gap 2mm but the material not come on bottoms of plate what is the reason. Means not penetrating
So easy to run a root pass with such a small gap but it's completely different whenever you run into something like a 1/4 inch between 2 beveled plates.
You are really an example of my dear friend. I wish you all the best
Tutorial 2 layer welding 3g this plat 1.2 mm tanks
Its illegal for us to weld down hill at huntington ingalls, the root and all goes up hill on the vertical test
If someone makes something look easy,it normally means there pretty damn good
I know that welding vertical up is not the only way to do it, but why did you chose to do it down? What is the difference between up and down? Does up have more penetration? I am on a welding school and about to certify and need to know as much as I can! I enjoy all your vids thanks !!!!!
Alguien que me explique en español la raíz la iso en descendente??
try a down hand root on a full pen inspected weld in california and youll be shown the door if you ovwerheat any part of the material "heat effected zone"youll fail the piece will failand if any of those passes are wider than 3/8 youll fail and who uses hard wire on a weld test 71m 71t dual shield with straight co2 is all you need which produces a slag but there is no easier wire than dual shield 0.52/.0.64,even after you get your certs in our shop you will take another when you apply and if you run a cover pass as wide as that youll not make it in Cali 3/8 is as wide as they let you go ive welded 1"plate tro w36x120 with a full pen with open root 1/8 and a single 30 deg bevel with and without ceramic backing bars,they can eliminate the need to carbon arc the backside and your talkingf a 1"weld and that was at least 15 passes
where is your academy? please
Man. Could you do a 3G FCAW with 100% CO2 tips video?
My jaw dropped when I saw that bead in the beginning of the video
Parabéns. Professor. Seus. Vídeo. É. Muito. Bom. Gosto. Muito. De. Trabalhar. Com. Solda. E. Quero. Ser. Um. Promocional. Igual. Al. Senhor. Vol. Fazer. Uma. Cursos. Para. Ser. Um. Bom. Profissional. Igual. A. Você. Obrigado. Professor.
Lot of sunk in spots with no build up support. It'll rust in a year
thank you so much..your this video is helping me alot...
i cant find a school to improve my welding skill but your this video is helpinh a lot.
My instructor wont let us do downhill on this. Also from my experience,3/32 gap is too large. I have a problem with whiskers on the backside for sure though. I hope i can pass it today!!!
Welds look good. Some diffrences in what you are showing and what I was taught in the boilermakers apprenticeship no down hill all verts and that also includes root pass. Most of the time we are allowed a backing plate but sometimes they want it to be an open joint. Caps are done in 3 passes. One in the center and then one on each side.
That's owesome iam also a welder ,bt your technique is high appreciated, i also need more and more techniques from you
it would be great to see a vertical up open root that's how you are tested in Ireland
isn't too difficult with a MIG gun ??
thats the only way to run mig up hill
It's not too difficult. My mig welding test I had to do a verticle uphill to get my cert
Great video, Speaking of crud building up on the mig nozzle, why don't do a quick tip video showing how you clean it. I clean mine and then wipe a thin film of anti spatter on the outside and inside on the nozzle and also on the contact tip.
I think its way better if u do the root uphill. Not only u can control much better the puddle and the wire at the tip of it, but u get a waaaay better penetration behind. Just my way to do it. And if possible, ill use solid wire for the penetration and flux for the filling! Nice welds!!
why you need to go uphill and get penetration since it's an OPEN root ?? isn't more difficult to do so ?? may be uphill just for fill & cap ?
@@senuolicak7097 in uk we never go down hill it’s called stoving weak as piss
Dayum that looks beautiful... Our school old machine setting can't make those wave unless it flat surface or just downhill mig welding
can this be done with 0.45 wire? i know im late.
CAN. You make one on a 1inch carbon plate in 4g
great video Jody. I do have 3 questions for you tho.
on a plate test like that, is going down-hill acceptable only in open root? in school they only allowed us to go uphill on the 3G plate test, but that's with a backing plate, not open root. can up-hill be done 3G open root?
and grinding... when you want to grind a weld for aesthetics or looks what's the rule or proper way of doing that? I have ground down some welds for looks before, but only ended up weakening the weld and having it break loose or fail.
thanks in advance
Am I on Pornhub? Never seen such weld porn!!
I know the mig welding but now i m job less i did 2 years migwelding in a company now i need a job anyone could help..?
It more or less depends on where you live. If you are near Elkhart Indiana, there are lots of jobs for a MIG welder
Jody... I think i remember in school i was taught the root pass was vertical up and we used a backer plate?? Does AWS spec that for the test?
making the root downhill is not correct. and root pass second pass uphill. lol. you get one pass for the root and it has to be uphill. 😂
Uphill works too but it really Depends on the procedure. There are definitely qualified procedures for downhill roots using mig. I took a downhill mig root pipe test years ago at a nuclear facility.
Stoved get sacked most places weldinf like that
how come you dont go side to side downhill but you do uphill?
That's looks so nice and clean! I'm practicing this now at work. Thanks for the video and tips.
Definitely not the proper way to do root pass! Thats Falsh! All Countries in Europe!
thanks for your lessons, they help to master the profession of welder
Fez solda descendo ja matou a solda😂😂😂😂😂😂
Hi teacher can show me ........v ........A thank you teacher
are you just using 75/25?
Hola profe estoy soldado tuberia de 48" a 40 grados de inclinacion con fluxcore pero se me prese ta porocidad a las 6 no encuentro la falla me puedes ayudar? Gracias
hello friend your explanatory videos are great while I would like to prepare more study on the types of welding soon subire one of my videos you know where I can prepare more in welding I have little experience and want to learn I like welding thanks greetings
Gostei muito da sua soldagem professor e parabéns 👏👏👍
Jody, I'm getting ready to weld up side strips that go around the perimeter of a table top. It's aluminum, and I'm not sure how to approach this thing in terms of avoiding distortion. I want the table to be flat when I'm done, but will be welding this strip all the way around the perimeter. It may not be a problem, but it sounds like a recipe for distortion. I've got ideas as to how to keep distortion down, but I'm curious if you have any general ideas on how to approach this thing. I watched your video on distortion, but don't know how that would apply to what I'm doing.
After all of these years I have to thank you for the zillions of excellent videos you've made.
Could you give me some tips on 3G uphill with a 1/8 inch gap and 1/8 inch landing, setting on machine ? Flux after root, ( root hard wire)
I’m about to take a Canadian weld test that has a stop and start mid plate. I have to do flat, horizontal, vertical and overhead. Do you have any tips? I’ve never had to take a test like this before.