I am new to resin casting and I couldn't find anything in the way of instructional videos as to the process of making blanks with the perfect swirls in them...until I stumbled across your channel. You cover everything there is to know on casting. I'm pretty sure your the only one who goes into depth on how to cast. This is perfect! Thank you so much for your videos. Instant sub and will now go on a Casey Martin binge watch. Thanks again and can't wait to see more vids.
Excellent video.....I've purchased a few of your blanks over the last couple months and they turn great and make stellar pens. Thanks for the video and I just made my first resin purchase using your discount code.....I hope it helps pay the bills.
Hi Casey, Glad college is going well. I've been waiting for this video as I've always ended up without distinct separation. Thanks for sharing. Cheers, Huw
Hey Casey if you are ever interested in buying whole large ( 500 to 200 Lb) birch burls, come to Quesnel ( just south of Price George) and check out the many burls I harvest.
Can you make a video about the orientation of the wood in the mold for hybrid blanks? It seems like Mine just look plain or not that interesting cause of the way im placing them in the mold
Casey, Since you haven't posted in a while I imagine school is keeping you busy. Hope all is well. Good information in this video. I've tried this but probably didn't wait long enought to mis. Got some nice purple blanks!
I’ve been quite busy with it Tom. The free time I’ve had has been in the shop but making a UA-cam video and social media was put on hold for awhile. But school has been going well. It’s just much more demanding in this program because a 3.0 GPA is the minimum to graduate. But I’ll still make time for videos now that I’ve settled into it more!
good to see you on the tube again, Casey. I have done that but found one has to be real careful for 3" pours. My mill are 3x3x11 1/2 with one side being wood but full depth one the other. Two times I found I waited too long and had very tiny bubbles throughout. They look like tiny specks when your turning. It took a while too figure out why and then I recalled I waited for color separation on those mills. Cheers, Lee
I have not but I’ve seen it done many times and know the process of it, which I believe will unnecessarily mix the resins more than necessary. It can look cool but to me it usually looks like a blob of colors rather than swirls
Hello, Just watched your pressure pot video (comments turned off on that so couldn't ask a question there).......do you leave your pressure pot attached to a compressor whilst the resin is curing?.....I wanted to leave mine over night ( new to this) but am unsure if I should leave a pot connected due to leakage..................
Hey Daisie, thanks for alerting me about the comments. I guess UA-cam turned them off because the video isn’t “suitable for kids” which is lame. Will try to fix that. I don’t personally leave it attached because I don’t have any major leaks in mine that would cause it to drop more than a few degrees in 3-4 hours, which is the max I would ever leave my resin in. That’s because alumilite cures so fast. For epoxy that may take 24 hours or so to cure, you definitely should keep it connected if you have a leak that’ll make it drop over a long period of time like that.
I have not yet but I would imagine you would have to wait until it starts to get hot and to a jelly consistency. The problem with that is then you could incorporate air bubbles and you don’t have pressure to get them back out
Casey just what I have been looking for. Using alumilite slow and pushing out my time. I will try using a temp gun. Quick question why did you add white to your resin with the colors other than black?
Amazing job, I found your channel today and I’m watching all your videos. Just a question, which type of colours are you using? Are alcool base or another type?
Thanks Casey. Does this mean we can disregard the “12 minute working time” from Alumilite to get these temps higher or do I just need to use greater volume? After 12 minutes I’m only at like 90. Thanks!
I’m using alumilite clear normal set. So it normally has a 7 min working time. But yes depending on your ambient temperature where you’re casting it may be longer
Would you be interested in making some 2in by 2in blocks that I could purchase and mill down to make some handles for my welding rig hopefully I can get my name out and start a small business
Why are you stirring so fast? Everyone says the faster you go the more bubbles you get. Yes you can do heat to make the bubbles come to the top, but the less bubbles you have the easier it is to work with...
I use pressure, amount of bubbles doesn’t matter because they go away when I put the resin in the pressure pot. Pressure is required for alumilite clear
Thank you, very instructive! Next time clean your table before making your video. You can’t appreciate the steps. Constructive criticism 👍 Love the video and learned a lot .❤️👍
I appreciate the criticism but I make hundreds of blanks a week and thousands a month, not worth cleaning the table for a video, as it only gets just as messy right after. I’m moving my shop in a month and am going to transition to a silicone mat for that and that’ll be easier to clean than the HDPE.
There are no bubbles in the blanks, and I didn’t apply a finish. I sprayed the blanks to get them “wet” for the video and photos, but that’s it. These aren’t finished products. These are pieces of material that get turned on a lathe into finished products like pens, handles, etc.
I am new to resin casting and I couldn't find anything in the way of instructional videos as to the process of making blanks with the perfect swirls in them...until I stumbled across your channel. You cover everything there is to know on casting. I'm pretty sure your the only one who goes into depth on how to cast. This is perfect! Thank you so much for your videos. Instant sub and will now go on a Casey Martin binge watch. Thanks again and can't wait to see more vids.
Very clear and concise instructions.
Glad it was helpful!
Excellent video.....I've purchased a few of your blanks over the last couple months and they turn great and make stellar pens. Thanks for the video and I just made my first resin purchase using your discount code.....I hope it helps pay the bills.
Awesome Michael thanks so much buddy!!
Those purple orange and green are amazing! How did you get those colors?
Great video. Very helpful info.
Hi Casey, Glad college is going well. I've been waiting for this video as I've always ended up without distinct separation. Thanks for sharing. Cheers, Huw
Thanks Casey,I'll defiantly be trying this method next time I cast
Great video. I learned I didn't hold off mixing long enough. Ordered a temp gun and looking forward to trying it. Thanks for the lesson
When using alumilite what would be the average cure time before turning a blank?
Loved the video! Thanks for taking the time to film and edit while grad school is so heavy! :)
I enjoy your videos very much. Thanks for sharing this with us
Great job. They look great!
Hey Casey if you are ever interested in buying whole large ( 500 to 200 Lb) birch burls, come to Quesnel ( just south of Price George) and check out the many burls I harvest.
Hi, Jerry. How can I get a hold of you. Would like to check out your burls.
Wow, this video is something I needed for a long time and I am happy you made one. I really enjoy your videos. Thanks👊👌
Love the tips
Can you make a video about the orientation of the wood in the mold for hybrid blanks? It seems like Mine just look plain or not that interesting cause of the way im placing them in the mold
Your blanks are incredible
Casey, Since you haven't posted in a while I imagine school is keeping you busy. Hope all is well. Good information in this video. I've tried this but probably didn't wait long enought to mis. Got some nice purple blanks!
I’ve been quite busy with it Tom. The free time I’ve had has been in the shop but making a UA-cam video and social media was put on hold for awhile. But school has been going well. It’s just much more demanding in this program because a 3.0 GPA is the minimum to graduate. But I’ll still make time for videos now that I’ve settled into it more!
Go Mustangs study hard but I do like your videos esp since I am a Cal Poly alum as well.
Nádherná práce 👍🏻👍🏻👍🏻
Great looking pen blanks
Make more of those purple green and orange for Etsy man those are amazing
this is so gorgeous but im wondering those pieces are for what ??
good to see you on the tube again, Casey. I have done that but found one has to be real careful for 3" pours. My mill are 3x3x11 1/2 with one side being wood but full depth one the other. Two times I found I waited too long and had very tiny bubbles throughout. They look like tiny specks when your turning. It took a while too figure out why and then I recalled I waited for color separation on those mills.
Cheers, Lee
Great work! Is it possible with slow cure resins? 24 hour. Alumilite is not available where I live ..
Great info. Many thanks for sharing.
Can this method be used for deep pours like table or bowls?
Yes but the timing is a lot different and the temperatures may be slightly different but yes you definitely can
Very cool!
How would you achieve swirls in a two piece or even a one piece cut mold when you only have a single pour sprue?
what do you use to cut your resin?
Casey, 2 questions. What do you for white to mix into your pour? I forget the second one.
Alumilite white dye!
Maybe a idea for your shop rond ring blanks
Have you ever tried the flip cup method? wondering on the pros and cons of it.
I have not but I’ve seen it done many times and know the process of it, which I believe will unnecessarily mix the resins more than necessary. It can look cool but to me it usually looks like a blob of colors rather than swirls
If you go beyond recommended time to get up to heat will you end up with bubbles? I use Alumilite slow mix. Thanks.
Yes you will
Hello, Just watched your pressure pot video (comments turned off on that so couldn't ask a question there).......do you leave your pressure pot attached to a compressor whilst the resin is curing?.....I wanted to leave mine over night ( new to this) but am unsure if I should leave a pot connected due to leakage..................
Hey Daisie, thanks for alerting me about the comments. I guess UA-cam turned them off because the video isn’t “suitable for kids” which is lame. Will try to fix that.
I don’t personally leave it attached because I don’t have any major leaks in mine that would cause it to drop more than a few degrees in 3-4 hours, which is the max I would ever leave my resin in. That’s because alumilite cures so fast. For epoxy that may take 24 hours or so to cure, you definitely should keep it connected if you have a leak that’ll make it drop over a long period of time like that.
Casey, have you tried using Alumilite Deep Pour and achieving good swirls. At what temp/time is the best time to swirl?
I have not yet but I would imagine you would have to wait until it starts to get hot and to a jelly consistency. The problem with that is then you could incorporate air bubbles and you don’t have pressure to get them back out
Great video - thanks
Casey just what I have been looking for. Using alumilite slow and pushing out my time. I will try using a temp gun. Quick question why did you add white to your resin with the colors other than black?
To make them opaque
Amazing job, I found your channel today and I’m watching all your videos. Just a question, which type of colours are you using? Are alcool base or another type?
I use Alumilite dyes
Thanks Casey. Does this mean we can disregard the “12 minute working time” from Alumilite to get these temps higher or do I just need to use greater volume? After 12 minutes I’m only at like 90. Thanks!
And THANK YOU for all of your time and commitment to these videos...it’s truly amazing!
I’m using alumilite clear normal set. So it normally has a 7 min working time. But yes depending on your ambient temperature where you’re casting it may be longer
Thanks for sharing, I need find where to get resin in the UK. 🇬🇧
Reach out to Nick Zammeti. He's in the UK though I dont know where.
Amazon
No thermometer in your "Tools"?
Does anyone know if these can be heated and bent to keep a shape? Thank you
Yes they probably could to an extent but it’d be much better to just use a mold and cast them that shape from the beginning
Will this technique work without a pressure pot?
Yes it should but if you’re using epoxy or something without a pressure pot needed it will take a lot longer for the resin to get hot
What's an average cure time before turning a blank if using alumilite clear?
🔥🔥🔥
Donde se compran los MOLDES de silicona?
Ptownsubbie.com
@@CaseyMartin707 gracias
7:49 there is a blank right in the middle that looks like the left side of someone’s face really cool.
awesome thank you
Would you be interested in making some 2in by 2in blocks that I could purchase and mill down to make some handles for my welding rig hopefully I can get my name out and start a small business
what is you don't have a pressure pot
I actually have 8 of them
@@CaseyMartin707 Can you recommend me a 2.5 gallon pot?
Just saw this video.... am I the only one who sees faces on those pieces??
Why are you stirring so fast? Everyone says the faster you go the more bubbles you get. Yes you can do heat to make the bubbles come to the top, but the less bubbles you have the easier it is to work with...
I use pressure, amount of bubbles doesn’t matter because they go away when I put the resin in the pressure pot. Pressure is required for alumilite clear
Thank you, very instructive! Next time clean your table before making your video. You can’t appreciate the steps. Constructive criticism 👍 Love the video and learned a lot .❤️👍
I appreciate the criticism but I make hundreds of blanks a week and thousands a month, not worth cleaning the table for a video, as it only gets just as messy right after.
I’m moving my shop in a month and am going to transition to a silicone mat for that and that’ll be easier to clean than the HDPE.
7 minutes working time? I thought it was good for 25 minutes.
This is Alumilite clear regular. It’s a polyurethane. You may be looking at an epoxy version they have
You have a big problem with your finish, like a lot of bubbles and you should polish your piece as well
There are no bubbles in the blanks, and I didn’t apply a finish. I sprayed the blanks to get them “wet” for the video and photos, but that’s it. These aren’t finished products. These are pieces of material that get turned on a lathe into finished products like pens, handles, etc.
Any way good job , hope you continue to inspire us 😍