Clay powder changes depending on how it is applied to the cup. If you pour it over dry teacup clay, it will crack. If you put it on a soft cup of clay, it won't crack easily. The expression of slip changes depending on the state of the cup of clay.
Always learn a lot from your videos, thank you! If I don't use raw materials like kaolin or clay powder? Can I dry my commercial white clay, mix with water, to make a white slip? Thank you so much!
Thank you for your comment. Simply put, if you dissolve white clay in water, it becomes white slip. If you dissolve the brown soil in water, it becomes a brown slip. Kaolin and porcelain are often used instead of clay, but they have the same purpose.
Merci pour votre commentaire. Les sous-titres français sont difficiles. Veuillez essayer la traduction automatique. Je pense que vous pouvez le comprendre dans une certaine mesure en regardant la vidéo.
![[For beginners] This is my work mark! How to make a ceramic stamp.](http://i.ytimg.com/vi/YQiwNY3eLC8/mqdefault.jpg)
![[For beginners] This is my work mark! How to make a ceramic stamp.](/img/tr.png)
![[For beginners] It's not just glaze that makes it black! How to make black slip.](http://i.ytimg.com/vi/rxkPpoVQauk/mqdefault.jpg)
![[KOHIKI, a popular pottery technique] How to make good looking "KOHIKI pottery".](/img/n.gif)
説明分かり易く、素人が色々疑問に思っている事を的確に指摘してくれて、目からウロコ。早速試します。
コメントありがとうございます。
参考になれば幸いです。失敗もあると思いますが色々と試して見て下さい。
きらくさん観ると副交感神経優位になります。めちゃ落ち着くー
いつもコメントありがとうございます。
そう言って頂けると安心します。これからもよろしくですm(_ _)m
ありがとう！白化粧品は最高でーす！
そうですね！白化粧最高！
勉強になりました。ありがとうございます。
こちらこそ。いつもありがとうございます。
有益な動画をありがとうございます。私の理解では、焼成されたカオリンをボールクレイと一緒に使用したということでしょうか？カオリンの全ての部分が焼成されたのですか？
ボールクレイを選ぶ際、あなたが使っているものにアクセスできない場合、どのような特性をお勧めしますか？ ひび割れを追求しています
コメントありがとうございます。
私の使っている白化粧土は焼成していません。粉末乾燥白土を水で溶かしただけの状態です。
一般的に素焼きをした陶器に化粧土を施す場合は化粧土も素焼きをします。
私の場合は生（乾燥状態）の陶器に化粧土を施すので、化粧土も生です。
ひび割れデザインを求めるなら、陶器を乾燥した状態で白化粧土を厚めに掛ければ、ひび割れテクスチャーになりやすいです。
ただし、陶器が崩れたり化粧土が剥がれたりする失敗も多いです。
ひび割れの多い白土は「蛙目粘土（GAIROME CLAY)」で作ればひびが多く入ります。
色々とチャレンジしてみてください。
@@kiraku-pottery 返信ありがとうございます！焼成カオリンに触れられていたのですが、なぜ、そしていつ焼成カオリンからこのスリップを作るのかが気になりました。ニュージーランドのカオリンを使用して、あなたの比率に従って作ってみようと思います。
この最後の時に撃ち出すと、あなたの温度は何ですか？酸化でコーン6まで撃ち出すことはできますか？
返信ありがとうございます。
たぶん翻訳が上手くできてないと思います。
コーン6は何度を示していますか？
日本では1230℃前後で焼成する事が多いです。
@@kiraku-pottery はい、申し訳ありません。翻訳が完璧ではありませんでした。私たちにとってのコーン6は1222〜1240°Cです。
いつも配合されたのを使ってましたどんぶり鉢も使わないからなぁ😅でも参考に成りました有難うございます。
参考になって良かったです。
分かり易い説明で自作も出来そうですね。やはり緋色は他の材料を混ぜても酸化では無理でしょうかね。
コメントありがとうございます。
緋色は酸化では難しいと想像します。酸化焼成は窯変が少ないので優しい感じに仕上がります。
Thank you fo the informative video !
The white clay powder Is supposed to have same shrinkage rate to the clay body I am going to use ?
Thank you ! 😸
Clay powder changes depending on how it is applied to the cup.
If you pour it over dry teacup clay, it will crack. If you put it on a soft cup of clay, it won't crack easily.
The expression of slip changes depending on the state of the cup of clay.
kiraku WEB動画 陶芸教室 Thank you 😸
Always learn a lot from your videos, thank you!
If I don't use raw materials like kaolin or clay powder?
Can I dry my commercial white clay, mix with water, to make a white slip?
Thank you so much!
Thank you for your comment.
Simply put, if you dissolve white clay in water, it becomes white slip.
If you dissolve the brown soil in water, it becomes a brown slip.
Kaolin and porcelain are often used instead of clay, but they have the same purpose.
@@kiraku-pottery i see! Let me try soon, thank you so much!
こんにちは、質問させてください。白化粧で焼いた物を水に濡らすとピンホールや、口の辺りから染みるのですが、焼き方の問題ですか？本体は一般的な信楽の赤土です。
コメントありがとうございます。
白化粧した器は染み込みが見えやすいし、汚れが目立ちやすいです。
焼き方の問題ではなく、そういう性質があります。
気になる様であれば、焼成後に食器用の水漏れ防止材を施すと染み出しません。
私はフリップコートを使っています。気になった際は、検索してみてくださいませ〜
@@kiraku-pottery 早速の返信をありがとうございます！なるほど、そういう性質、、、！
焼成後食器用の撥水剤にしばらく漬けて、絞ったタオルで拭いて乾燥させてますが、それしても水で染みちゃうのです。フリップコート試してみます！
ご丁寧にありがとうございます。
黒化粧は粘土を溶かせばいいんですね！！
目の荒さを合わせないとダメだと聞いたんですが、合っていればどの粘土でも化粧土になりますか？
黒化粧はそれでも出来ます。もちろん他の作り方もありますが・・・。
目の粗さは合っていなくても大丈夫なモノもあります。あえて粗さを合せない方が面白くなる可能性も高いです。
Dommage qu on n’ai pas le choix des de potiers
sous titres en français comme dans les autres vidéos
Merci pour votre commentaire.
Les sous-titres français sont difficiles.
Veuillez essayer la traduction automatique. Je pense que vous pouvez le comprendre dans une certaine mesure en regardant la vidéo.
白化粧は白い粘土を水で溶いた物でもできますか? やってみたのですが、最初はいい感じに仕上がって、満足していたのですが、作品が乾ききってしまった後で白化粧の色が茶色っぽく変わってきてしまいました。なぜでしょう? 教えて頂けると有り難いです。
コメントありがとうございます。
どんな粘土を使っているのか分からないので具体的な説明ができませんが、粘土は「生」・「乾燥」・「焼成」の状態でそれぞれ色が違うと思います。
白い粘土で化粧土を作ったのであれば、焼き上げれば白くなると思います。
それでも白くならない場合は、白い粘土を変更するか、胎土（使っている作品の粘土）の鉄分が多く、化粧土に影響を及ぼしていると思われます。
色々と試して見てくださいね！応援しております。
@@kiraku-pottery 返信ありがとうございます。とりあえず、焼いてみます。動画のアップ毎回楽しみにしています。日本はコロナでまだまだ大変そうですが、頑張って下さい😊
先生、茶色っぽく変色してしまった白化粧、先生がおっしゃっていた様に一時焼成後、見事にきれいに白にかわりました😊 変わりそうにも無い色合いだったので、残念に思っていたのですが、嬉しかったです。アドバイスありがとうございました🙏
良かったですね！
何事も経験ですね～
what is wrong with may white slip?? it fall off..
Thank you for your comment.
White slip is good.