Drawing Forming Limit Diagram (FLD) curve in ABAQUS (S-rail forming)

Using ABAQUS, Forming Limit Diagram (FLD) curve was drawn.
Data were adopted from PE - Max. In plane strain (Major strain) and PE Min in plane strain (Minor strain)
Report - Field output - PE (In plane strain)
- SPOS (Top location)

[@ganeshkumarv1409]

Can you tell Where did you get those values(Red colour line - FLD curve values) in notepad which u copy-pasted as X2 and Y2?

[@AmaltheDarkman]

can you please upload fld with hemispherical punch

[@supernova9721]

I want to get a forming limit diagram using nakazima test for an aluminium alloy. Can it be done on ABAQUS?

[@wonjanglee]

Simulation can be done through ABAQUS. Distribution of major strains and minor strains can be drawn. However, forming limit curve is not obtainable. It can be done only with experiments.

[@supernova9721]

Need the Major strain vs minor strain with failure points. Is that possible?

[@kt-um5vh]

major strain의 음수값을 무시하는 이유가 있나요?

[@wonjanglee]

보통 판재 성형에서 압축 응력이 발생하여 재료가 압축이 되는 경우 wrinkle 가능성이 증가합니다. 그래서 보통 음수값은 잘 보지 않는 경우가 많습니다.

[@kt-um5vh]

​@@wonjanglee 답글 감사합니다. 저가 알기로는 fld상에 주름이 나타날 가능성이 있는 부분은
minor strain/major strain < -0.5 이며 비율이 작은 값을 가질수록 주름경향이 크다고 알고있습니다. 주름은 성형공정에서 방지해야 할 주요 결함으로 인위적으로 무시하면 안될 것 같아서요.

[@wonjanglee]

@@kt-um5vh 잘 알고계시네요!
사실 메이저 스트레인 0이하그리면 그래프가 안예뻐져서요ㅎ
그리고형상마다 다른데 해석에어는 실제 발생하지 않는 압축변형도 발생하는걸로나와서요(두께증가) 보통 이부분은 주름예측하는 다른 방법이 필요합니다.

[@kt-um5vh]

@@wonjanglee 메쉬를 작게하니깐 압축변형값이 감소하네여 ㅋㅋ 굿