Vertical Root Pass. Advantages and disadvantages of high and low current. Tig Welding 3G Butt Joint
![weld [HAGOJIBI]](http://yt3.ggpht.com/ytc/AIdro_lButtTy6bwshHHOdUuuc7ktsddm0YgRj2FhqoPUm3aQA=s48-c-k-c0x00ffffff-no-rj)
Вставка
- Опубліковано 29 кві 2020
- Subscribe
/ weldhagojibi
-
Instagram (-) .-
/ weldhagojibi
-
Hello everyone.
Today, the carbon steel sheet was welded butt to the vertical position.
This is a video about the ROOT PASS during the welding process.
Advantages and disadvantages when welding with low current.
And the video shows the advantages and disadvantages of welding with high current.
Please share your opinions and know-how in the comments window.
I think your writing will be very helpful for many colleagues.
Thanks for watching.
Please take good care of your health.
#Back
#bead
#weld
#procedure
#specification
Please write your know-how or opinion.
Your writing will be of great help to many colleagues.
Thanks for watching. Have a nice day.
여러분의 노하우 또는 의견을 적어주세요.
여러분의 글은 많은 동료들에게 큰 도움이 될것입니다.
시청해주셔서 감사합니다. 즐거운 하루 보내세요.
I myself find it hard to get proper penetration on tig root passes and I believe its my filler wire technique. I need more practice on how to hold the filler wire as well as feeding the wire. Lack of penetration has caused alot of problems during the bend testing process. I think all of your videos have helped and practice is definitely key to better welds. Thank you for showing other techniques to make better root passes.
Even when the alcohol isn't broken,your still a fantastic welder and I appreciate your willingness to teach.
As an American craftsman, welder and machinist I am always pleased to see expert skill, then ad the patience to share.
Many thanks!
You are the best tig welder I've ever seen
Thanks a lot for sharing your knowledge
우와...영상들 다시 보고있는데, 실력나아진후(연습많이 해본후) 영상을 다시보니 영상을 한번봤을때 안보이던것, 안들리던게 들리네요!!
진짜 , 1~2개월후다시보면 예전엔 '음, 당연한거지' 했던게 다르게 보이네요
용접만큼이나 설명도 잘하시네요!!
I normally keep my torch angle steep and filler rod angle shallow. I really need to practice your methods.
I always learn from your videos. Thank you.
Great work as always. I would only be allowed to Mig something mild steel, that big. I would also love to learn how to "Walk the Cup" and do as neat work as you do.
A GOOD SHOW TO WATCH ON THE COMPUTER,:WELDING TIPS AND TRICKS,THE GUYS NAME IS"JODY",IT'S HIS OWN SHOW,DOES ALOT OF TIG,SOME MIG,STICK UPHILL ON PIPE,DOWNHILL ON PIPE,SALES LOTS OF VIDEOS,HAS WHAT YOU CALL A "TIG FINGERS"SO YOU DON'T BURN YOUR FINGERS WHEN TIG WELDING BUT HE MOSTLY TIG WELDS AND VERY GOOD AT IT!HE'LL SHOW YOU ON YOU-TUBE ALSO HOW TO "WALK THE CUP"WHEN WELDING PIPE AS WELL AS"FREE HAND".YOU CAN ALSO WALK THE CUP ON FLAT MATERIAL(1G)SINGLE BEVEL GROVE,OPEN ROOT(NO BACK-UP BAR).HE ALSO SALES PRODUCTS AT:THE WELDMONGER STORE.COM. BUT THERE SOME INFORMATION TO GET YOU STARTED,GOOD LUCK,STAY HEALTHY-CRAIG
역시 대 선배님 이십니다 저는 수직이 특히나 아렵더라구요
Sim mestre essa soldagem em chaparia retas é fundamental trabalhar com tungstênio mais longo eu tenho minha opinião e um bocal menor dessa forma com amperagem mais alta e mais rápido controlando o material de adição fica uma raiz mais perfeita e a produção é bem melhor obrigado pela orientação por essa maravilhosa aula 🇧🇷🙏
덕분에 많은 배움과 도움이 됩니다.
대단하십니다
잘보고 갑니다.~
설명이 넘 좋아요 최고에요★★★★★
Muchas gracias
Felicitaciones excelentes clases .
Хороший учитель, молодец
Always great videos .
감사합니다. 도움이 정말 많이되었습니다. 구독하고 갑니다^^
유용한 영상 항상 감사드립니다.
Всегда рад новому видео, всегда познавательно. Спасибо.
감사합니다
최고입니다
잘 봣습니다 선배님. 파이프 백 낼때도 버티컬할때가 좀 긴장되는데 저도 종종 전류가 높아서 그런지 용융풀에서 와이어가 분리가 돼요. 다음에 시간되시면 넓은갭을 백내는 방법을 알려주실수 있나요? 파이프를 배블링를 하다 보면 칼개선쪽에 평평하게 나오지 않을때가 많아요. 그래서 갭이 좁앗다 넓어졋다 하는데 그때마다 넓은갭에서 골치아프더라구요.
Nice
진짜 용접 예술이네요 39 이제 용접을 시작 했는데요 기회만 된다면 선배님 밑에서 기초부터 제대로 배우고 싶네요^^
공감합니다 저는 용접 3-4년 했는데 시작을 아주 이상한 야매 용접으로 시작해서 기본기도 없고 막용접이 몸에 뱃네요 ㅠ
@@user-qx8tl3bv1y 가르쳐주는사람을 잘 만나야 용접을 다재다능으로 할 수 있죠 오로지 기능사 기사 합격을 위주로 야매 방식을 가르치는 선생님 밑에서 배우면 자세히 못 배울 수 밖에 없죠
배우고 싶습니다
Thank you for given knowledge...
Beatiful, como siempre un 10 XD, saludos desde Chile ✌️
Very good! The high amperage is my way.
Thanks you for video very good
hola buenas noches tengo una pregunta que gas usas cuando soldar con tig acero al carbón saludos gracias
감사합니다
Nice video.
Very well explained and shown.
The one with the wedge so that the gap doesn't contract, I didn't know that.
I think welding with low current is quite good for beginners.
And the better you can weld, the faster you automatically become.
The one with the lower and higher current is a nice welding exercise.
Nice rest week desired.
He can weld the weld at 80-95 amps, increase the teavel speed, and voltage And not need the wedge.. just need to tack it together.. this will also increase the penetration on the back..
용접고수셔서 멀하든 잘하시네요 부럽네요
Gooddd
장단점 잘 보았습니다👍🏻👍🏻
Buen vídeo amigo
도움에 늘 감사히 보고 있습니다 저는 용접이 신기에서 집에서 연습을 하는데 생각처럼 전혀 진행이 안되네요 근데 텅스텐봉이 님은 끝만 붉게 되는데 저는 텅스텐이 길게 붉어 지면서 검게 되는데 원인이 무엇인지요~
저도 그게 궁금했었는데 후기가스 주는 시간을 조금 주면 나아지더라구요.
Parabéns use este talento . Deus deu para supli sua necessidade . Para abençoa o próximo Jesus ama voce
좋아요
good study video
Здравствуй как звать то тебя меня Владимир некоторые моменты я у тебя перенял спосибо тебе но меня интересует вертикальный стык трубы как у тебя получается облицовка
Good
영상 잘 보고있습니다~
혹시 알루미늄용접 영상도 올려주실 수 있나요?
6G 연습하고 있어요
버티컬에서 자꾸 터지면서
백이 두껍게 쌓이네요
이 부분이 해결이 안되는데 조언 부탁드려도 될까요?
버티컬에서 넓게할까 생각중이에요
10호만 사용해서
건너면서 진행하고 있습니다
봉을 짧게도 잡아보고 전기도 70~90 사용하는데 안되네요
용접을 배우고 싶어요
기회가 되시면 한수 가르쳐 주세요
쌤 혹시 각 포지션마다 위병. 모션 있는 영상은 없을까요??
안녕하세요 선생님 서스 가스지그만들어 보려하는데 제대로된 사진 좀 볼수잇는곳 없을까용
Good!
Super👍
항상 잘 보고있습니다! 파이프 연강 용접을 100A로 용접하는데 비드 색이 탁하게 나와서요 ㅜ 저렇게 광택있게 나오는 비결이 무엇일까요?
the Best
아싸 좋아요 1등!!
Hocam yürütmeyi yapamıyorum fincanı yürütürken torcu bastırıyormusunuz
Cool
배관 백비드 연습중인 왕초보입니다 . 아시다 싶이 용접봉 공급이 많이 미숙합니다. 용접봉을 기존에는 많이 눞혀서 공급하고 잇는데 잘 안되고 잇습니다 . 영상에서 보니깐 용접봉 거이 세우다 싶이 보이는데， 세워서 공급하신거 맞나요 ? 맞으시면 루트면 백비드용접할때 용접봉 눞여서 공급할때와 세워서 공급할때 장단점에 대해 알고 싶습니다 ...부탁드리겟습니다
Nasıl yapabilirim kaynağın üstünden bir daha nasıl geçerim
Is the edge of the v shape sharp or with a little flat stand? About 1 mm.
Gtaw is a dcen process with very little penetration... if you use a chamfered edge or landing.. you will need more heat to penetrate.. but more heat means less wire / travel speed, you will end up starving the puddle for metal, and it will take the metal from the base material, and concave the root (cause suckback) you will get more penetration with a wider gap @ lower amps then you will with a tight gap and high amps.. per travel speed..
Always use a clean knife edge..
Whats the rod angle?
👍👍👍👍👍
Weld turned out nice and even, it would be even better if you steadied your hand with one more glass of alcohol. hehe
안녕하세요 동영상 늘 잘 보고있습니다.
혹시 탱크 용접 눕혀놓은 자세로 하는거나 파이프 5G돌릴때의 느낌이나 같은가요? 파이프는 돌릴 자신감은 있는데 큰 탱크 같은거 돌릴수 잇는가고 물어볼때 자신감이 떨어지네요.탱크를 때본적 없어서 할수 있다고 할라니 참 애매합디다.5g 자세 파이프 돌릴수 있으면 압력탱크도 가능할까요답변주시면 감사하겠습니다.
입문자 입니다. 실례를 무릎스고 이렇게 글을 올리게 됬습니다.
혼자 사무실에서 독학으로 진행할려다보니 아는것도 없고 인터넷은 광고 글뿐이고 주변에 용접하시는 분이 없어 이렇게 글을 올림니다.
알곤용접기를 어느정도로 선택해서 구매해야할지 고민이 많이 됩니다. 용도는 다용도로 사용할예정입니다.
너무 범위가 크죠... 초보자라 잘몰라서 그런것이므로 양해를 부탁드리겠습니다. 욕심인지는 몰르겠으나 SUS박판과 알루미늄용접을 하고싶습니다.
어느정도 용량을 구매해야할지.. 고민이 많이됩니다. 가격이 고가인지라 한번 선택이 엄청난 후회를 불러올거 같아 선뜻 구매하지 못하고 있는 상황입니다.
지나가던 용접사입니다.
STS(Sus) 박판과 알루미늄이라고 하셨는데요,
박판의 기준이 어느정도선인지, 용접량(시간)이 얼마나되는지 모르겠지만,
두께 6mm아래의 모재만 짧게 한두시간정도만 용접하려면 300A나 250A로도 괜찮구요
그 이상 두께도 써야되고 용접시간도 길면 350A가 마지노선이라고 생각합니다.(크기가 큰편이고 220v 지원안되는경우가 많다는 단점이있네요)
300A도 쓸순있지만 안정적이진않아요.
알루미늄을 원하시니 당연히 ac/dc겸용 용접기로 선택하셔야겠죠.
하루종일 용접해야되는게 아니고 또 220v도 사용하고싶으시면 300A
ac/dc겸용 용접기가 가장 범용성높은 선택인듯하고
휴대성,편리함,가격 vs 출력,용접시간
취향따라 위아랫급정도 쓰면될듯하네요.
🥂
💪💪💪💪💪💪
Ответ пиши на англискаком я смогу прочита
i could write a comment or give him some ideas but i will not.the U.S. has given away enough information to other countries(especially china)why should i give out any knowledge to another country so they can take away our jobs,figure it out yourself your so smart!
Hes not chinese and his country is allied with the US..
Nice