If you want to lose all the gold you’ve been working so hard to collect, then by all means, keep using that beaker directly on your heating element. Get a corning-ware dish to heat your reaction vessels in and save your glass. If not, one of these days, your beaker full of aqua regia/chloroauric acid is going to break and you’re going to lose all of your gold. Be smart/work smart.
@Yodiyst The same happened to me but I collected all the dirt and papers I used to wiping the liquid from the ground and burned anything to ash After that I was able to recover the Gold in AR
@gyvren You are correct and sometimes it's only a boil over and a lot of your Gold has to be wiped of the whole area the AR splattered and flow around. If you have hours to invest it's not a to big problem, otherwise it's very recommended to do it like you wrote❣️
No electricty needed. The process of cementing out the gold will work with a nail or a srew dipped into solution alone. I would not use steel because then a lot of basemetals like copper will come down as well.
I would be careful using screws for anode/cathode. Because they might contain small amounts of chromium, you might inadvertently create hexavalent chromium, which is pretty nasty. So make sure you're using metals for your anode/cathode that don't contain chromium.
In the cathode there's no danger for the chromium to end in the solution, as it's catodically protected. The problem it's in the anode. You can use a tin can as anode for example as it's made of carbon steel
Thank you for the information you have provided. I would like to ask a question. How is the residue after the electrolysis process done according to the order of operation? So is it necessary to make king water again or just apply nitric acid?
Actually the cheapest way is to use scrap aluminum parts out of a computer. Small heat sinks are pure aluminum and will drop out the gold just like SMB.
Interesting! Did I miss the part where you denox the aqua regia with urea or is it not necessary if you precipitate with electricity? Thanks for sharing.
Trying to figure this out now but then remembered... If you neutralize the acid solution (aqua regia) the gold would come out of solution anyway from lack of acid.
Absolutely brilliant!!!!! SMB is expensive where I am from and also have to wait days for it to arrive. This method is by far the simplest and cost effective, can't wait to try it out. Would the nails leave iron trace elements with the powder
Hello sir, thanks for this wonderful video. I did the experiment, but a problem arose, which is the adhesion of gold to the iron electrodes. Is there any advice? Thank you
No way! It's impossible. Electrolysis does not dissolve gold but precipitates out of solution or separates gold from something. Only Aqua regia or chlorine gas can dissolve gold from the soil 🙂
This is not electrolysis !!!!!! I just putting iron to solution that way !!!!! Electrolysis don’t have nothing to do with my work !!!!!! It’s like putting iron sulfate in solution for that I using elektrisity
Hi great job but I have some questions: 1-your gold powder was so clean but we have all stuff metal( copper-gold-pt-pd-ni-...)in solution if we do this way all metals in solution precipitation? 2-we can use graphite or lead electrods or like you bolts which one best? 3-what was that granola(formula) you add your solution for dissolve your gold? Best regards 🙏
This way you can not get pure gold. If the anode and cathode are metallic, as in this video, and if the solution is dirty, then precipitation of metals such as palladium, gold, platinum, copper, silver, bismuth and mercury can occur. Of course if these metals are present in a dirty solution . Precipitation of which metals will be more depends on the concentration of hydrochloric or sulfuric acid in the dirty solution.🙂 Pure gold can only be obtained if the cathode from Titanium, and the anode is gold, any dirty gold but not lower than 10K. In this case, you will get 24K- 999.9 gold! 👌With this method, gold sticks very strongly to Titan, and the rest of the metals are sinks to the bottom 🙂
it precipitates faster than it dissolves. It's called chemical equalibrium reaction. As long as you seperate solution and solid fast enough after precipitation, you lose basically nothing.
I use 3 volts and abouth 5 ams but that doesn’t meter when you apply electricity to solution iron dissolves in solution and participating gold . That is easy way to get gold from solution.why I newer use it ?
thanks everything is in progress, my question now, The solution is boiling you see the gold been precitipate How long can i leave the solution, check now and then it keeps on boiling and precitipate?
ok thank you very much but this way isn't good for soil solutions because they have many metals inside copper will participate first then gold will ride copper
Hi sir, you mean electric battery charger is were you connect the nail positive and negative, is it what you mean. Or What type of electricity you mean Please am waiting for your reply and GOD bless you
My adventure has a DC power supply. A 12 volt battery charger can work but it might burn it out . If you hook the charger to the battery....Then you can run smaller wires from the battery to the pregnant gold solution. With the smaller wires coming from the battery, you can change the size of the wires and effect the amps coming through. I thought he said high amps. But he seems to run 5 to ten amps. The more amps the faster it happens. So don't go too long or you will pig out the solution with iron. I hope this helps. God Bless.
Yes cementing, but in nature no free iron.always in sulfides or oxides .the same with zinc ,tin ,copper .that why you founding gold with silver . But newer founding gold with oxides of another metals .i have absolutely different view of ewerithing what you see on UA-cam,mostly that is fake .
Black means iron is going into the solution. As iron goes into solution ,gold comes out It will get black because of the iron with gold or without any gold present. The stannous test shows the gold that is AVAILABLE in solution. I think you use HCL acid to remove the iron from your gold after the electrolysis
My question is even if there's base metals dropped out of solution, can another washing of metals with HCL and sodium nitrates clean your precipitates to a finer quality gold?
When you smelting that gold baise metals burns of .they having low melting temperatures and they just burns before your gold smelts . And you don’t have a lot thos metals so don’t worry to much. Anyway you need refine that gold then you and cleen it I newer have problems
t depends on the amps and the solution. Just stop it before it gets too dirty with iron. If it is not done, (still has gold in it), you can do it again to get the remaining gold.. when the iron goes into solution, the gold comes out of solution. As the iron goes into solution, it gets dark. You only need so much iron to get the job done. I hope this helps. You can test solution with Stannous Chloride before it gets too dark, to check for gold remaining in the solution.
It depends on the amps and the solution. Just stop it before it gets too dirty with iron. If it is not done, still has gold in it, you can do it again to get the remaining gold.. when the iron goes into solution, the gold comes out of solution. As the iron goes into solution, it gets dark. You only need so much iron to get the job done. I hope this helps. You can test solution with Stannous Chloride before it gets too dark, to check for gold remaining in the solution.
Very nice, at minute 3:04 you used a solution to detect gold in aqua regia. What is the name of this solution? Did you make it yourself or buy it from the market?
Dissolve solder (as lead free as possible but not critical except shelf life) in a small amount of HCL and you end up with Stannous chloride which is used to test for the presence of PM like gold silver and platinum.
DC Power Supply Variable, Adjustable Switching Regulated Power Supply (30 V 0-10A) with Encoder Coarse & Fine Adjustments Knob, Beach Power Supply with USB & Type-C Quick-Charge Interface
So, if you have old scrap computer parts, can you dissolve the AU from the parts with HCL and HNO3 to make Aqua Regia then add KHSO4 to get it to turn into dust?
Honestly, You are the smartest of all. Apart of that I wonder how electricity supposed to be cheap My Q is can i make electrolite cell by a 12v car battery as my power supply? Thabks alot
@@myadventure7069 I know it is abit strange but blieve me we go for a month or more to vast areas which is hundreds of kms away from civilization northern africa
I believe wee have those places too that way I making those tools . I don’t want bring rocks home too specially when you miles away from civilization . Africa is nice I always wanted to go visit that country
Go to walmart and buy tin sinkers in fishing supply. Then in dark brown glass put muriatic acid (hydrochloric acid) and sinkers at about 1 gram tin to 10ml acid in bottle. Do not stopper at first so be careful. When tin dissolved then stopper. Good for a couple months. Add a tin sinker then to renew solution or make new batch.
I would like to do the same cheapest way. But (1) is that liquid is Aqua Regia ? (2) katoda and anoda are stainless steel or what ?. Please sir... i need your answer as you give us cheapes way to process the gold
Don’t start till you lorn about making aqua regia .my way is the cheapest way. You can use nitric acide and smell toxic fumés or use my ways with no smell
اشتركت بقناتك واتبابعها انت رجل فعلا يريد الخير للجميع اشكرك جداI subscribe to your channel and follow it constantly. You are a man who really wants the best for everyone. Thank you very much
If you want to lose all the gold you’ve been working so hard to collect, then by all means, keep using that beaker directly on your heating element. Get a corning-ware dish to heat your reaction vessels in and save your glass. If not, one of these days, your beaker full of aqua regia/chloroauric acid is going to break and you’re going to lose all of your gold. Be smart/work smart.
Sometimes you gotta work with what you got man.
@@amashizainofr I lost like 5gs of gold in some dirt bc a drop of cold water on my beaker 😢
👌
@Yodiyst The same happened to me but I collected all the dirt and papers I used to wiping the liquid from the ground and burned anything to ash
After that I was able to recover the Gold in AR
@gyvren You are correct and sometimes it's only a boil over and a lot of your Gold has to be wiped of the whole area the AR splattered and flow around. If you have hours to invest it's not a to big problem, otherwise it's very recommended to do it like you wrote❣️
No electricty needed. The process of cementing out the gold will work with a nail or a srew dipped into solution alone. I would not use steel because then a lot of basemetals like copper will come down as well.
I would be careful using screws for anode/cathode. Because they might contain small amounts of chromium, you might inadvertently create hexavalent chromium, which is pretty nasty. So make sure you're using metals for your anode/cathode that don't contain chromium.
what type of bolts would you use?
@@meami5089use stainless steel that won't be attracted to a magnet.
@@joeyl.rowland4153 marine grade stainless steel contains 10% chromium. ???
Stainless steel has chromium
In the cathode there's no danger for the chromium to end in the solution, as it's catodically protected. The problem it's in the anode.
You can use a tin can as anode for example as it's made of carbon steel
I would love to see a stannous chloride test after the precipitation from the electrolysis. Great content and thank you 🙏
Yess I making new video and adding for you status test after electrolysis
How Volt and amp? Tanks so much master
اخي
ما هو الفولت المطلوب والامبير؟
هل يجب تخفيف المحلول؟
شكرا 🌹
Thank you for the information you have provided. I would like to ask a question. How is the residue after the electrolysis process done according to the order of operation? So is it necessary to make king water again or just apply nitric acid?
Just smelt it ,
Actually the cheapest way is to use scrap aluminum parts out of a computer. Small heat sinks are pure aluminum and will drop out the gold just like SMB.
Or…..How about VITAMIN C ? (Absorbic acid) tablets?
I am not chemist but I found cheapest way to recover that gold . Is cheap and safe.
What about zinc to drop gold
@@budzag it will work
Thank you Professor for sharing your knowledge👍 I'm doing an experiment on checking for Gold in my Black Sand. Cheers Kev
Nice work, I hope you can clarify the intensity of the electric current used, how many volts and how many amperes are used?
I have seen your all method but the best and easiest method is electric current with iron rods, excellent one
Interesting! Did I miss the part where you denox the aqua regia with urea or is it not necessary if you precipitate with electricity? Thanks for sharing.
Trying to figure this out now but then remembered... If you neutralize the acid solution
(aqua regia) the gold would come out of solution anyway from lack of acid.
Absolutely brilliant!!!!! SMB is expensive where I am from and also have to wait days for it to arrive. This method is by far the simplest and cost effective, can't wait to try it out. Would the nails leave iron trace elements with the powder
First you get the gold out of the rock then wee refine that gold. What country you are ?
@@myadventure7069 south africa
Did u tried it? And ur reault?
@@valourinternational734 yes I did thank you
Great job all around fam. Keep on having fun getting that au and living the dream. Gold Squad Out!!!
Thank you for the shortcut, you're wonderful.
Hi
5 amps to cathode & anode nail bolts . Very Impressed Thank you🌝
Is it ready to be molten in microwave ?
Hello sir, thanks for this wonderful video. I did the experiment, but a problem arose, which is the adhesion of gold to the iron electrodes. Is there any advice? Thank you
On electrodes is another metals more active metals .use nitric acide to dissolve all junk metals .dont use this method for electronic stuff
@@myadventure7069 ok, many thanks
from the phillipines!! great tutorial sir..someday i will do that..
Cuántos voltios usas para hacer la electrólisisHow many voltages do you use for electrolysis?
3 v
I love your heart feeling. God bless you🙏🙏🙏 bro
Hi many thanks from Mali. Does this work with cyanide pregnant solution ?
How can gold be dissolved from the soil by electrolysis with table salt without chemicals? Please give us an experiment. Thank you.
I told you I working on that be patient wait when I finish I make video
@@myadventure7069 Thank you very much. I wish you all the best, and more success .
No way! It's impossible. Electrolysis does not dissolve gold but precipitates out of solution or separates gold from something. Only Aqua regia or chlorine gas can dissolve gold from the soil 🙂
This is not electrolysis !!!!!! I just putting iron to solution that way !!!!! Electrolysis don’t have nothing to do with my work !!!!!! It’s like putting iron sulfate in solution for that I using elektrisity
@@myadventure7069 ..i'am agree
Please I want to know how pots for melting gold can be made and why they break
I buying them on eBay
Thanks for sharing knowledge. Where are you from?
Can you do this process on alkaline solutions with gold cyanide complex and what are the conditions
Hi great job but I have some questions:
1-your gold powder was so clean but we have all stuff metal( copper-gold-pt-pd-ni-...)in solution if we do this way all metals in solution precipitation?
2-we can use graphite or lead electrods or like you bolts which one best?
3-what was that granola(formula) you add your solution for dissolve your gold?
Best regards 🙏
This way you can not get pure gold. If the anode and cathode are metallic, as in this video, and if the solution is dirty, then precipitation of metals such as palladium, gold, platinum, copper, silver, bismuth and mercury can occur. Of course if these metals are present in a dirty solution . Precipitation of which metals will be more depends on the concentration of hydrochloric or sulfuric acid in the dirty solution.🙂 Pure gold can only be obtained if the cathode from Titanium, and the anode is gold, any dirty gold but not lower than 10K. In this case, you will get 24K- 999.9 gold! 👌With this method, gold sticks very strongly to Titan, and the rest of the metals are sinks to the bottom 🙂
@@akgoldbear7669 this guy does not what he is doing
Absolutely no chemistry back ground, so what to expect from a person trying to reinvent the wheel
Thank you very much for this information sir. big help!!
Thank you, very informative.
Do you need to neutralise the nitric acid before using the electrolis?
Yes
Question ,how much current 12 volt 24 volt DC ?
awesome tutorial.what the name of the electric machine sorry newbie here
Cathode /anode must be iron? Or can they be copper? Thanks Sir
Anode must be iron . Katode can be any metal
Question I have is what is stopping the gold from dissolving again in the aqua Regina
it precipitates faster than it dissolves. It's called chemical equalibrium reaction.
As long as you seperate solution and solid fast enough after precipitation, you lose basically nothing.
change the pH to like 5 first
استاد ببخشید اون منفی و مثبت کردی برق خانگی وصل کردی یا آمپر برقش فرق میکنه
جناب امید
نامفهوم کلمات را به ادونچر رساندی. این یک مبدل برق دی سی است. امپر هم ۵ و ولتاژ ۳ ولت
It's DC power.
Good video informative I learn something but where did you buy your 12 volt power supply thanks again
Amazone , or eBay . You can use any power supply or batery from the carr
@@myadventure7069 I thought you needed low amperage like 3 amps or five
I use 3 volts and abouth 5 ams but that doesn’t meter when you apply electricity to solution iron dissolves in solution and participating gold . That is easy way to get gold from solution.why I newer use it ?
سيدى الفاضل ماذا عن محايدة النتريك
thanks everything is in progress, my question now,
The solution is boiling you see the gold been precitipate
How long can i leave the solution, check now and then it keeps on boiling and precitipate?
Thank you. How can gold be dissolved from soil by electrolysis? Please, I hope you give us an experiment, God bless you.
I working on that but so far no results
adventure thank you
@@myadventure7069 Copper rods used in clay?
ok thank you very much
but this way isn't good for soil solutions because they have many metals inside
copper will participate first then gold will ride copper
Do you try copper ? I try ! Copper is a problem in solution and Wery slow
@@myadventure7069
yes I tried soil solutions
both poles were from stainless steel ,,, I saw that first participation for copper then gold on cathode
Hi sir, you mean electric battery charger is were you connect the nail positive and negative, is it what you mean.
Or
What type of electricity you mean
Please am waiting for your reply
and GOD bless you
My adventure has a DC power supply. A 12 volt battery charger can work but it might burn it out . If you hook the charger to the battery....Then you can run smaller wires from the battery to the pregnant gold solution.
With the smaller wires coming from the battery, you can change the size of the wires and effect the amps coming through. I thought he said high amps. But he seems to run 5 to ten amps.
The more amps the faster it happens. So don't go too long or you will pig out the solution with iron.
I hope this helps. God Bless.
Is the gold just cementing on the iron like silver cementing out on copper?
Yes cementing, but in nature no free iron.always in sulfides or oxides .the same with zinc ,tin ,copper .that why you founding gold with silver . But newer founding gold with oxides of another metals .i have absolutely different view of ewerithing what you see on UA-cam,mostly that is fake .
Does the color of the solution change to black, an indicator of the presence of gold in the solution?
Black means iron is going into the solution.
As iron goes into solution ,gold comes out
It will get black because of the iron with gold or without any gold present.
The stannous test shows the gold that is AVAILABLE in solution.
I think you use HCL acid to remove the iron from your gold after the electrolysis
Nice pure genius
Sir can we use mobile charger instead of battery for electro plating
For my two iron road work’s perfectly fine. ! And I don’t do electrolysis I keeping electrodes just 1 -3 minutes .
Bro can you show me the machine that you use ?
The name?
Mrque ?
Volatge?
And how to use
This method will not only percipitate gold but also some basemetals so I would’ve recommend using this method though
Hydrochloric acide dissolves all baise metals
My question is even if there's base metals dropped out of solution, can another washing of metals with HCL and sodium nitrates clean your precipitates to a finer quality gold?
When you smelting that gold baise metals burns of .they having low melting temperatures and they just burns before your gold smelts . And you don’t have a lot thos metals so don’t worry to much. Anyway you need refine that gold then you and cleen it I newer have problems
@brianburnssailorslife5383 yes but do you have hydrochloric acid inside solution no base metal be dropping out
Or must i leave it until it stops boiling or precitipate,
Sir please reply is very important
t depends on the amps and the solution. Just stop it before it gets too dirty with iron.
If it is not done, (still has gold in it), you can do it again to get the remaining gold..
when the iron goes into solution, the gold comes out of solution.
As the iron goes into solution, it gets dark. You only need so much iron to get the job done.
I hope this helps. You can test solution with Stannous Chloride before it gets too dark, to check for gold remaining in the solution.
Thanks for your knowledge shared us❤
Hi, please info me that both terminal atr the sam iron.? Thanks
Anode + must be iron . Katode - can be any metal
I use same metals iron . But katode can be any other metal
@@myadventure7069 thanks again for your information.
copper anode /cathode would be better.then wash with ammonia.
U mean one electrode is iron and other is copper?
@@valourinternational734 both copper and 1.5 volts.
Saludos desde Venezuela muy bueno ese modo puede decirme cuántos minutos se deja los clavos con la corriente aplicada gracias
It depends on the amps and the solution. Just stop it before it gets too dirty with iron.
If it is not done, still has gold in it, you can do it again to get the remaining gold..
when the iron goes into solution, the gold comes out of solution.
As the iron goes into solution, it gets dark. You only need so much iron to get the job done.
I hope this helps. You can test solution with Stannous Chloride before it gets too dark, to check for gold remaining in the solution.
Nice video
No killed nitric
Think
show me the equipment you using
How do I deal with the light precipitate that floats in the solution?
Found more gold and forget about that light gold . Use water to spry on that gold and gold go down
Why not just add some sodium metabisulfite?
Wonderful and simple..Sir, can you tell me what is the name of the power source that you are using because I will buy one like it
Probably the wall outlet
Hello, is it possible to dissolve gold in water like sugar or salt? I would like your help on this matter.
🤣😅🤣🥲🤣🥲you are joking ?
Very nice, at minute 3:04 you used a solution to detect gold in aqua regia. What is the name of this solution? Did you make it yourself or buy it from the market?
Dissolve tin metal in hidrochloric acide and you get stanous chloride. SNCL2
@@myadventure7069
Thank you
Dissolve solder (as lead free as possible but not critical except shelf life) in a small amount of HCL and you end up with Stannous chloride which is used to test for the presence of PM like gold silver and platinum.
What about copper present in solution.
No copper in my rocks
the machine were you clip the 2 nails is called what?
DC Power Supply Variable, Adjustable Switching Regulated Power Supply (30 V 0-10A) with Encoder Coarse & Fine Adjustments Knob, Beach Power Supply with USB & Type-C Quick-Charge Interface
So, if you have old scrap computer parts, can you dissolve the AU from the parts with HCL and HNO3 to make Aqua Regia then add KHSO4 to get it to turn into dust?
Why you don't do with vitamin c
Sir I've found a super Rich hard rock gold doing your way has worked need your help very rich gold in clay of Vein
What I can help you with
@@myadventure7069 super Rich Gold I will make a video of it ok? Watch it by tomorrow and get a hold of me so we can talk it over
@@myadventure7069 Made the video it will upload you will smile to see it?
What volte you use?
12 bots but you can use regular batery
@@myadventure7069 thank you for answering
I wish u visit sénégal
For gold and dimond prospecting
What is your way of doing Awua Regia?
Depends what you want to do. If doing refining I make full strain if I do recovery gold from the quartz I do week aquaregia.
The solution will dissolve the iron because it is not diluted with water, right?
No .
Won’t that drop all metals out of solution?
Love you bro so much. And God bless you🙏🙏🙏
very good. needs any ureia?
I have 5 pounds enuf for all my life
Thank you 😊
I've busted a 2 liter beaker setting on direct heat. I'll never do that again
Expensive mistakes 🤪. I don’t do that anymore . I try keep heat about 80 degrees, that more then enuf
Thank you bro!
I got 2 silver metal cathodes and what has been precipitating in the AR is a white sticky product. What is this?
Silver chloride
@larrycaso1126 So, I filter the silver chloride off, then what? Do it again? Should the gold then precipitate?
I making the video what’s be next
@larrycaso1126 Great!. More or less, when will it be ready? Today, tomorrow, one week or when?
Use copper its better then iron bolts
Thanks sir
Honestly, You are the smartest of all.
Apart of that I wonder how electricity supposed to be cheap
My Q is can i make electrolite cell by a 12v car battery as my power supply?
Thabks alot
Make your own
@@myadventure7069 will the car battery supply the cell cuz In the desert theres no electricity source
When you in the desert you don’t want cery heavy batery !
@@myadventure7069 I know it is abit strange but blieve me we go for a month or more to vast areas which is hundreds of kms away from civilization northern africa
I believe wee have those places too that way I making those tools . I don’t want bring rocks home too specially when you miles away from civilization . Africa is nice I always wanted to go visit that country
Excellent presentation. Thank you, Sir.
Good stuff.
Wow wow wow!
good evening one question how can i request it from the store these two decanters and what kind of metal are they thank you !!
Sir am still waiting for your reply from my question
Dus this work with platnum metals to
sir how can i make a stanous chloride?
Wach my last video
Go to walmart and buy tin sinkers in fishing supply. Then in dark brown glass put muriatic acid (hydrochloric acid) and sinkers at about 1 gram tin to 10ml acid in bottle. Do not stopper at first so be careful. When tin dissolved then stopper. Good for a couple months. Add a tin sinker then to renew solution or make new batch.
Problem ! in his country no walmart
💞💞💞💞💞💞💞💞💞👏👏👏👏👏👏💗💗👍👍💗💗
I would like to do the same cheapest way. But (1) is that liquid is Aqua Regia ?
(2) katoda and anoda are stainless steel or what ?. Please sir... i need your answer as you give us cheapes way to process the gold
Don’t start till you lorn about making aqua regia .my way is the cheapest way. You can use nitric acide and smell toxic fumés or use my ways with no smell
دوتا پیچ آهنی باشه فرق نمیکنه در آوردن رسوب طلا
Good job
I tried it and only iron from electrodes deposits😂
Yes
❤❤❤
Keren
Finally I've dun 30 of thys never got it right now I can take all of it an do this
Bravo bravo thanks thank you match
Dus this work with platnum metals to😊
No just with gold
Smokelees prossesing sir
Its iron on bottom
iron and gold......big difference.
If you don't have any gold, then it will be iron only
✌✌✌
سلام
Hi I try this why is not working?
That’s meens no gold in your solution ! Or to much nitric !
How to neutralise the nitric acid
What metals are the 2 wire nails please
Use urea . You aqua regia maybe is to strong deluge with water and you don’t have problems any more
Iron
Simple and cheap just like me 😁
اشتركت بقناتك واتبابعها انت رجل فعلا يريد الخير للجميع اشكرك جداI subscribe to your channel and follow it constantly. You are a man who really wants the best for everyone. Thank you very much