Your work is excellent bro, First time ever seen someone working in a professional way with a different recipe, easy simple with excellent results. You are winner bro. thank you for great share
Thanks for your video . Your videos teach me many things. You don’t hide anything , you show all true process and now i’m using your lead bath method. Thank you very much..
have never seen a refine done like that before! this video is very inspiring my friend,thank you so much for posting this! definately subbed and a huge like for your efforts✌
Exelent proces man, im glad you post it! Super result and purity, im recheve you pump yestrday, thanx for that gift brother, ceep going and dont care about bad coments on the groups, do it in you way! Once again, super video mate!
Heya ! Thanks for sharing your work ! Gold Mushrooms appears when job is done perfectly... ( Perfect denox with sulfamic, good pregnancy of the solution, an almost saturated SMB solution and... Heat ! ) You started apprentice and now you are a master... Working, working and working is the ultimate Secret of Achemist !!! ;) Have fun...
Smart guy, this is more like what i love to see, youre using 2 separate materials needed refining and combining, rather than 2 separate recovery processes.
You seem to be a master of the processes used to recover all types of metals in many different ways, I'm curious if you have ever retrieved the palladium and silver from surface mounted monolithic capacitors?
Hello, really great videos and from an experienced person. I really enjoy watching your videos. Can you tell me what is the chemical composition of sulfamic acid? Thank you very much
👍Интиресно замутил😀вот бы глянуть что в шлаке,на железе осталось.800 градусов маловато думаю,в тигле на горне это бы плавить,щолочи для флюса.Азотки много ушло наверно что бы растворить свинец😀да и всё в его солях потом было?Бывает с рудами полиметаллическими мутю,солей потом его при остывании кучи,очень ядовитая хрень.Интиресный метод,используется для бедной эликтроники,только там медь как купилирующий метал из самой эликтроники и эликтролизом разделяют медь с палладием в начале,что осталось на дне уже царём.Шикарный выход👍
Я не растворял свинца! Свинец после купелирование (на ролике не показано) превращается в PbO, оставляя только сплав AgAu, который обрабатывают азотной кислотой
your video is the most complete video in you tube for cpu gold recovering . i hope you explain the cupellation part in more detail. i have done this process just with litharge but i didn't get any conclusion,but when i add some lead it went OK. do you know why?
I tryed refining jewellry with aquaregia...but i dont get the aim of using cupellation...it's to extract the gold from ceramic? What about crushing all ceramic and add all to aquaregia?
@@OwlTech333 I dont remeber if it was your chanel video or from some one else...but he was ading HF, maybe to dissolve the glass inside the chips...what do you think about that?
Super'anlatimin ve durustce ugulaman 10 kilo işlemciden nekadar golt ve ne kadar sılver çıktığını biliçli bir sekilde labaratuvar kıvamında bilgiledirme övguye layik tır
@@OwlTech333 sorry me again, been doing some research I have read the alloy needs to be roughly 25% gold and 75% silver. With this in mind would 400 grams of silver be enough for the leaching process? Many thanks
How many degrees celcius should the temperature be for the molten lead bath? Thank you ..i think have problem my furnace’s heat because my stainless steel is pierced(it’a burned)
VERY Fascinating! I've been very interested in this new hobby. You know your stuff! I have dozens of old junk 486 computers and electronics. Is there a reliable resource to learn the basics, materials and tools needed, and techniques without the beginner fails? Thanks! SUPER COOL Video!
есть некоторое количество осадка платина палладий через алюминий из КМ , .....обязательно ли нужно серебро чтоб купелировать этот осадок ?? и зачем оно ??
Вообще то я знаю как их разделить , но вы когда то показывали купелирование конденсаторов с палладий платина плюс серебро под огнем лампы , и опыт меня заинтересовал .....вот думал повторить
Можно и без серебра, только оно тут присутствует как коллектор, хотя и свинец тоже коллектор, но тут разница температур в плавлении даёт преимущество в несколько раз. Можно использовать и цинк и олово, кто что , в данном случае серебро достаётся как бонус, не надо тратить кислоту для отдельной переработки. Почитай... chem21.info/info/1165402/
счет простой: на 1кг процессоров 1-1.5кг свинца и 0.1-0.15кг серебро.На магнитной основе процесс проходит на ура. Очень важно что там медь не была. Если она там присуствует надо добалят на 20 раза больше свинца чем меди.
Спасибо, очень занятно, надо попробовать. А сплавлять со свинцом или оксидом свинца? И для купелирования достаточно температуры пропан-бутановой горелки или надо автогеном?
The cupellation was done in the same stainless still pan from the video. Air was blown above the molten lead, forming solid litharge crust around the metal. The crust was periodically removed to allow further oxidation of the lead. After the "flash" the DORE was left to cool and was moved to a cement cupel to remove the last traces of lead. Finally the litharge from the cupelling was reduced back to lead by melting it with flour.
it can be done either way, without the big cupel you have to remove the litharge periodically, while with the big cupel it gets "sucked" in. For me its easier to recover the lead directly from the collected litharge than it is from the litharge cake (soaked cement)
Купелирование, так называется этот метод по русски. Kupelirovanie, this method is called in Russian. To attract subscribers, make subtitles in Russian! ++
Привет Коля ....я так понял он снимает золото свинцом , а потом растворяет свинец азоткой и с золотом работает как обычно ...смущает лишь -- сколько кислоты надо чтоб растворить 400 грамм свинца ??
سلام استاد در مرحله اول تناسب قطعات با سرب ونقره چه مقداری با چه مقدار از قطعات و زمان واکنش اول و کوپیلاسیون مرحله بعدی چه زمانی یا ساعتی طول کشید متشکرم از استاد جهت راهنمایی شاگردان خودشون .
Уважаемый автор ролика , мне кажется это под силу только вам -- у вас есть ролик как вы плавите горелкой платину палладий , больше в ютубе ничего вразумительного на этц тему я не нашел .......подскажите пожалуйста как лучше плавить платину и палладий ??
Процессы альмагальмирования стары как мир. Меня поражает, что люди колотящие пяткой в грудь на химфорумах здесь делают восторженные и восхищенные лица. Типа не знали! Или плохо книги читали? Еще больше поражает что люди говорят на процессы альмагальмирования, что это процесс купелирования. Ну это явный бред и незнание профессии. Тот же принцип применим для олова, тот же принцип применим и для ртути (только плавить не нужно). Температуры достаточно, даже более чем. Процесс ведется при пониженных температурах, как только основной металл перешел в расплавленое состояние. Это порядка 400-500 град. Вам господа нужно внимательнее читать книги. Этот процесс описан во многих учебниках.
Амальгама - сплав какого-либо металла с ртуть, "альмагальмирования" не подходить на это процесс, сплавильные с последующее купелирование думаю лучшем. КУПЕЛИРОВАНИЕ - извлечение благородных металлов (см.) в чистом виде из свинца путём окислительного плавления. Процесс основан на том, что свинец и др. неблагородные металлы при высокой температуре легко окисляются кислородом воздуха и переходят в глет, который плавает на поверхности жидкого сплава и легко удаляется, при этом благородные металлы не изменяются. Процесс ведут до тех пор, пока вся ванна не заполнится золотом, серебром и т. п. Метод К. используют и в пробирном анализе. ua-cam.com/video/MwDfUxgNxeA/v-deo.html
На одной ртути весь мир клином не сходится. По мимо ртути есть ещё ряд металлов способный образовывать те же принципы взаимодействия с металлами. К методам амальгамной металлургии относятся наряду с другими обменные реакции на границе раздела фаз, а также электролиз с образованием амальгам. Туда как раз входят такие металлы как Олово и Свинец. При этом Золото (как и другие драгоценные металлы) не просто сплавляются, а именно растворяются образуя новые соединения. В припое ПОС61 растворяются все металлические покрытия, за исключением сплава олово-никель. При температуре 250 °С скорость растворения золота в припое ПОС61 составляет около 4 мкм/с (по некоторым данным - до 1 мкм/с). При растворении золота в припое образуются интерметаллические соединения золота с оловом трех типов - AuSn, AuSn2, AuSn4 и бинарный сплав со свинцом AuPb2. На прочность слоя припоя оказывают влияние в основном хрупкие дендриты AuPb2 и игольчатые кристаллы AuSn4. Механическая прочность паяных соединений существенно снижается при повышении температуры и очень резко - с увеличением толщины покрытия . Но и не могу не согласиться Купелирование так же подходит под это, но всё же более правильное название всему этому Амальгамная металлургия. Мало о ней что известно и основное применение в ней как раз ртути для производства довольно редких и дорогих металлов, а так же очень чистого свинца. Ртуть чуть позже была заменена на олово и свинец ( это собственно очень удобно особенно при производстве твердых электродов амальгамы).
Купелирование это не процесс сплавления, а разделение драгметаллов из основных металлов, которые заранее были сплавлении (процесс который вы называете альмагальмирования)
Ну бог с Вами. Купелирование - так купелирование. Для меня это не единичная методика очистки, а ряд технологий под названием Амальгамная металлургия, которая довольно широко применяется на производстве особенно развитых западных странах.
кроме этого, купелировать ( если говорить о золоте) - можно и с медью и с цинком. Но вы выбрали свинец, потому как металл в нём растворяется как в ртути не достигая температуры плавления золота. На этом же принципе происходит разделение многих других металлов, и не только драгоценных.
Your work is excellent bro, First time ever seen someone working in a professional way with a different recipe, easy simple with excellent results. You are winner bro. thank you for great share
Thanks for your video . Your videos teach me many things. You don’t hide anything , you show all true process and now i’m using your lead bath method. Thank you very much..
For the lead bath 800 degrees celcius is enough? Or what must be max heat for the lead bath? Thank you
800 is more than enough
@@OwlTech333 thank you
have never seen a refine done like that before! this video is very inspiring my friend,thank you so much for posting this! definately subbed and a huge like for your efforts✌
Thank you! It means a lot to me!
Exelent proces man, im glad you post it! Super result and purity, im recheve you pump yestrday, thanx for that gift brother, ceep going and dont care about bad coments on the groups, do it in you way! Once again, super video mate!
Hvala tebe Dusane! Nadam se da ćemo uskoro videti pumpu u акцији :) Let me know if you have any problems with the power supply
Heya !
Thanks for sharing your work !
Gold Mushrooms appears when job is done perfectly...
( Perfect denox with sulfamic, good pregnancy of the solution, an almost saturated SMB solution and... Heat ! )
You started apprentice and now you are a master...
Working, working and working is the ultimate Secret of Achemist !!! ;)
Have fun...
I'm flattered!
It's amazing watching how good you've become. Great vid friend.
Steven Shiner Thank you! Really appreciate your comment
Smart guy, this is more like what i love to see, youre using 2 separate materials needed refining and combining, rather than 2 separate recovery processes.
thanks
You seem to be a master of the processes used to recover all types of metals in many different ways, I'm curious if you have ever retrieved the palladium and silver from surface mounted monolithic capacitors?
I have some videos on the mlccs the process is the same, skipping the incineration part
Hello, really great videos and from an experienced person. I really enjoy watching your videos. Can you tell me what is the chemical composition of sulfamic acid? Thank you very much
👍Интиресно замутил😀вот бы глянуть что в шлаке,на железе осталось.800 градусов маловато думаю,в тигле на горне это бы плавить,щолочи для флюса.Азотки много ушло наверно что бы растворить свинец😀да и всё в его солях потом было?Бывает с рудами полиметаллическими мутю,солей потом его при остывании кучи,очень ядовитая хрень.Интиресный метод,используется для бедной эликтроники,только там медь как купилирующий метал из самой эликтроники и эликтролизом разделяют медь с палладием в начале,что осталось на дне уже царём.Шикарный выход👍
Я не растворял свинца! Свинец после купелирование (на ролике не показано) превращается в PbO, оставляя только сплав AgAu, который обрабатывают азотной кислотой
OwlTech ага,выпарил значит его,в шлак превратил
так точна
Very nice rare method,! Do you use coal to produce heat
Coke
@@OwlTech333 thanks you
Sorry to ask can I replace coke with coal which one is Better
Video wonderful nice and awesome thanks for such a video sir
Thank you Anis!
Hello. Why do you do it in this way, why you don't use standard procedure. Smash it and direct in Aquaregia? What is the difference ? Thank you.
Speed, less chemicals, less waste, refining silver at the same time...
your video is the most complete video in you tube for cpu gold recovering .
i hope you explain the cupellation part in more detail.
i have done this process just with litharge but i didn't get any conclusion,but when i add some lead it went OK.
do you know why?
You need to add a reducing agent in order to convert the the litharge to lead. Flour, wood chips, sugar to name a few
thanks.what do these materials do? i mean what do they reduce?
carbon source they reduce litharge to lead
I tryed refining jewellry with aquaregia...but i dont get the aim of using cupellation...it's to extract the gold from ceramic? What about crushing all ceramic and add all to aquaregia?
AR works too, it just takes longer
@@OwlTech333 I dont remeber if it was your chanel video or from some one else...but he was ading HF, maybe to dissolve the glass inside the chips...what do you think about that?
@@arte47 Not my channel, I don't use HF
@@OwlTech333 Thank you for your advice!
I liked it did some things slitly different got rite to it .(Down an Derty ) good job .👍
Super'anlatimin ve durustce ugulaman 10 kilo işlemciden nekadar golt ve ne kadar sılver çıktığını biliçli bir sekilde labaratuvar kıvamında bilgiledirme övguye layik tır
Привет! Отличный и полезный фильм получился! Огромный лайк!
Благодарю! Я с нетерпением жду твоих видеороликов!
Спасибо! Уже вышел)))
Заметил, уже смотрю! :) Лайк!
Great video, how much lead did you place into the bath?
About 5kg
@@OwlTech333 Cool, thanks 👍
@@OwlTech333 sorry me again, been doing some research I have read the alloy needs to be roughly 25% gold and 75% silver. With this in mind would 400 grams of silver be enough for the leaching process? Many thanks
Ian Blaza more than enough
How many degrees celcius should the temperature be for the molten lead bath? Thank you ..i think have problem my furnace’s heat because my stainless steel is pierced(it’a burned)
700-800C the melt should be runny like water
@@OwlTech333 thank you so much
Question, where do you find these ceramic cpu's?
How u do with lead if all process was shown it would be great thanks
ua-cam.com/video/1dW8_-9NODg/v-deo.html
اذا كان في المحلول نحاس يترسب الذهب او لا او الابلاديوم يترسب اولا
where did you buy all those processors sir?
Just 1 question please, if you not braking cpus, what abut the bonding wires from inside?
I like videos of you. So.. where your buy cpu?
I don't buy them they were given to me
Oh thanks you
Hello, good morning.
where did you buy the e-scrap from?
can you give a recommendation of a trusted seller to send to Indonesia.
thank you
Sir, what is the concentration of nitric acid you used?
60%
@@OwlTech333 Thank you,sir.
Hi. Thank for sharing. Just want to know, is it worth it money-wise?
Poor Man Juan's Tek4Ebriwan depends on how cheap you can get the CPUs
круто.. вот только я не понял как вы от свинца избавились..?
купелирование
то есть в цементном тигле плавили пока не остались только серебро и золото, а свинец и т.п впиталось в цемент.. я правильно понял..?
точна :)
VERY Fascinating! I've been very interested in this new hobby. You know your stuff! I have dozens of old junk 486 computers and electronics. Is there a reliable resource to learn the basics, materials and tools needed, and techniques without the beginner fails? Thanks! SUPER COOL Video!
Интересно сколько для этого нужно кислоты и возможен ли этот расплав без серебра ??
серебра есть 400гр серебрение контактов
есть некоторое количество осадка платина палладий через алюминий из КМ , .....обязательно ли нужно серебро чтоб купелировать этот осадок ?? и зачем оно ??
а зачем надо купелировать PdPt?
Вообще то я знаю как их разделить , но вы когда то показывали купелирование конденсаторов с палладий платина плюс серебро под огнем лампы , и опыт меня заинтересовал .....вот думал повторить
Можно и без серебра, только оно тут присутствует как коллектор, хотя и свинец тоже коллектор, но тут разница температур в плавлении даёт преимущество в несколько раз.
Можно использовать и цинк и олово, кто что , в данном случае серебро достаётся как бонус, не надо тратить кислоту для отдельной переработки. Почитай...
chem21.info/info/1165402/
Подскажи пожалуйста, а купелирование ты делал в капели или просто окислял на воздухе?
Habib Nurmag в данном случае окислял на воздухе
OwlTech , это получается что у тебя постоянно собиралась корочка из оксида свинца и ты очищал постоянно от сплава, или как это выглядело?
Habib Nurmag точно как ты сказал
How to reduce silver from water aqua regia solution before lowering the palladium master.
Хороший выход, но под шляпкамы ЧПУ были крышки с золотым волосками🤔. Думаю что через кислоты было бы лучше.
свинец достигает золотых проводов и растворяет их
I swear i was already subscribed to you! Wtf youtube
Yeah! I remember! One of my first subscribers
OwlTech thanks for confirming...so now we know for certain that youtube drops subs off channels!
May i know the link where you can buy 10kg cpu
If I knew it I would have bought them already
А как расчитываете количество свинца? И подходит ли этот метод для другого вида сырья, нп. позолоченные контакты на магнитной основе?
счет простой: на 1кг процессоров 1-1.5кг свинца и 0.1-0.15кг серебро.На магнитной основе процесс проходит на ура. Очень важно что там медь не была. Если она там присуствует надо добалят на 20 раза больше свинца чем меди.
Спасибо, очень занятно, надо попробовать. А сплавлять со свинцом или оксидом свинца? И для купелирования достаточно температуры пропан-бутановой горелки или надо автогеном?
Температура из пропан-бутановой горелки хватит. Свинца для металла, а оксид свинца, бура, мучной и пещевая сода для породьй
@@OwlTech333 получается 10% свинца, заранее плявится со снинцом?
I was hoping to see how you cupelled that much alloy
The cupellation was done in the same stainless still pan from the video. Air was blown above the molten lead, forming solid litharge crust around the metal. The crust was periodically removed to allow further oxidation of the lead. After the "flash" the DORE was left to cool and was moved to a cement cupel to remove the last traces of lead. Finally the litharge from the cupelling was reduced back to lead by melting it with flour.
similar to @1:36 ua-cam.com/video/Ttv-qLxTs90/v-deo.html
OwlTech ah ok so initial lead removal is not done in a big concrete bowl loke i see the indians doing
it can be done either way, without the big cupel you have to remove the litharge periodically, while with the big cupel it gets "sucked" in. For me its easier to recover the lead directly from the collected litharge than it is from the litharge cake (soaked cement)
سلام عليكم ورحمة الله وبركاته ممكن ان تكتب نواع المرسبات او رموزهن خاص بل ذهب او الابلاديوم
What kind of material did you take to smelting please sir
Ceramic CPUs, silver contact points and lead.
Почему золото коричневого цвета после HNO3, а не золотистое полностью?
Лайк ...у вас ролики крайне интересные ....переведите их на русский , а то онлайн переводчик не совсем точно переводит комменты , трудно понять смысл
да поэтому мне нужна помощь
Maaf guru.mau tanya nah sistem mandi timbal seperti itu tapi tampa di beri tambahan perak nah bisa tdk dengan timbal timah saja?
Hello every body, can tell me where I can buy a ceramic cpu processor scrap?
مقدار سرب در هر کیلو بر چه اساس وچقدره متشکرم استاد
Купелирование, так называется этот метод по русски.
Kupelirovanie, this method is called in Russian.
To attract subscribers, make subtitles in Russian!
++
Спасибо! Спервом слияние, потом купеллирование :)
уже делаю
Вам можно отвечать и комментировать только по русски?
английскому тоже
Привет Коля ....я так понял он снимает золото свинцом , а потом растворяет свинец азоткой и с золотом работает как обычно ...смущает лишь -- сколько кислоты надо чтоб растворить 400 грамм свинца ??
سلام استاد
در مرحله اول تناسب قطعات با سرب ونقره چه مقداری با چه مقدار از قطعات و زمان واکنش اول و کوپیلاسیون مرحله بعدی چه زمانی یا ساعتی طول کشید متشکرم از استاد جهت راهنمایی شاگردان خودشون .
Здравствуйте вы гаси азотную кислоту при высаживании серебра?
нет
is this video really real
Yes
who is your supplier ??
Уважаемый автор ролика , мне кажется это под силу только вам -- у вас есть ролик как вы плавите горелкой платину палладий , больше в ютубе ничего вразумительного на этц тему я не нашел .......подскажите пожалуйста как лучше плавить платину и палладий ??
ua-cam.com/video/7eXCDVB4mW0/v-deo.html
То есть наиболее приемлимый способ для этого ---- купелирование ??? Я правильно понял ??
Огромное спасибо
ua-cam.com/video/1CIPOarELbU/v-deo.html
Спасибо ...у меня тоже желтый порошок как и в ролике
What is needed
فيديو رائع جدا
Such buttons!!😛😛😛
Is there a way i can talk to you?
Процессы альмагальмирования стары как мир. Меня поражает, что люди колотящие пяткой в грудь на химфорумах здесь делают восторженные и восхищенные лица. Типа не знали!
Или плохо книги читали?
Еще больше поражает что люди говорят на процессы альмагальмирования, что это процесс купелирования. Ну это явный бред и незнание профессии.
Тот же принцип применим для олова, тот же принцип применим и для ртути (только плавить не нужно).
Температуры достаточно, даже более чем. Процесс ведется при пониженных температурах, как только основной металл перешел в расплавленое состояние. Это порядка 400-500 град.
Вам господа нужно внимательнее читать книги. Этот процесс описан во многих учебниках.
Амальгама - сплав какого-либо металла с ртуть, "альмагальмирования" не подходить на это процесс, сплавильные с последующее купелирование думаю лучшем.
КУПЕЛИРОВАНИЕ - извлечение благородных металлов (см.) в чистом виде из свинца путём окислительного плавления. Процесс основан на том, что свинец и др. неблагородные металлы при высокой температуре легко окисляются кислородом воздуха и переходят в глет, который плавает на поверхности жидкого сплава и легко удаляется, при этом благородные металлы не изменяются. Процесс ведут до тех пор, пока вся ванна не заполнится золотом, серебром и т. п. Метод К. используют и в пробирном анализе. ua-cam.com/video/MwDfUxgNxeA/v-deo.html
На одной ртути весь мир клином не сходится. По мимо ртути есть ещё ряд металлов способный образовывать те же принципы взаимодействия с металлами. К методам амальгамной металлургии относятся наряду с другими обменные реакции на границе раздела фаз, а также электролиз с образованием амальгам. Туда как раз входят такие металлы как Олово и Свинец. При этом Золото (как и другие драгоценные металлы) не просто сплавляются, а именно растворяются образуя новые соединения.
В припое ПОС61 растворяются все металлические покрытия, за исключением сплава олово-никель. При температуре 250 °С скорость растворения золота в припое ПОС61 составляет около 4 мкм/с (по некоторым данным - до 1 мкм/с). При растворении золота в припое образуются интерметаллические соединения золота с оловом трех типов - AuSn, AuSn2, AuSn4 и бинарный сплав со свинцом AuPb2. На прочность слоя припоя оказывают влияние в основном хрупкие дендриты AuPb2 и игольчатые кристаллы AuSn4. Механическая прочность паяных соединений существенно снижается при повышении температуры и очень резко - с увеличением толщины покрытия .
Но и не могу не согласиться Купелирование так же подходит под это, но всё же более правильное название всему этому Амальгамная металлургия. Мало о ней что известно и основное применение в ней как раз ртути для производства довольно редких и дорогих металлов, а так же очень чистого свинца. Ртуть чуть позже была заменена на олово и свинец ( это собственно очень удобно особенно при производстве твердых электродов амальгамы).
Купелирование это не процесс сплавления, а разделение драгметаллов из основных металлов, которые заранее были сплавлении (процесс который вы называете альмагальмирования)
Ну бог с Вами. Купелирование - так купелирование. Для меня это не единичная методика очистки, а ряд технологий под названием Амальгамная металлургия, которая довольно широко применяется на производстве особенно развитых западных странах.
кроме этого, купелировать ( если говорить о золоте) - можно и с медью и с цинком. Но вы выбрали свинец, потому как металл в нём растворяется как в ртути не достигая температуры плавления золота. На этом же принципе происходит разделение многих других металлов, и не только драгоценных.
Sir can I do this at home
Who am I to tell you what you can do or what you can't do at your home?! I can only advise you: DON'T!
how many processors?
10kg
@@OwlTech333 tanks
@@ackrapovic0169 welcome
Bom dia amigo muito bom
show! How much would you sell me 20 kg of intel i 386 and i 486 ceramic processors with shipping to Brazil?
I don't sell, sorry!
@@OwlTech333 thank you!
The first step i canot understand
Лайк видос зачётный
Спасибо!
Красиво.
Спасибо!
AFTER God Na u more wisdom in JN
Класс!!!!
Спасибо!
Ну уж прям добыча' , но и на демонстрацию не похоже. Нарушается закон об обороте д.м.
закон об обороте д.м?
в шлаке наверное полно золота ...
нет, проверял
:)
MantaP
How to overcome leat