I fell in love with this model, as soon as you throwed it and flew flawless, I will buy the files! Pls is there any chance to make a version with a center landing wheel and maybe two small others on the wings, I don't have the luxury of a grass strip😢.
Shame that no one asking in your Contact page on your website. Ive asked if its possible to feet a 4s in your pod motor? With some 4s 1100-1500? This pod can feet a 28mm motor?
do you mean fit? Yes, a 28mm diameter motor will fit. And yes a 4S lipo will fit too. As you increase speed and desire to pull hard turns the material and design need to match. The LW foaming materials are great for sub 80 mph, but will need more stiffness for higher speeds... The Juicy wing, that will fit this fuselage, has been recorded at 187mph (300kph) doing dynamic soaring printed from PLA and hope to go faster.
Havent been impressed with the PLA HT. Less foaming means a higher flow rate, putting it in the weight range of PP-CF, which is more durable, rigid, and withstands higher temperatures
do you mean the no-foaming PLA-HT (now called PLA-HP)? I love the idea of CF materials, but they have never been worth the effort and cost.. I will have to look at PP-CF. I don't think you can get PP-CF to a .6g/cm^3 density... best I could find was 1.0g/cm^3.
@@soarkraft the foaming HT foams less than the non HT. To achieve the same volume you need more flow compared to normal active foaming, in my experience, .15 more. The pp cf spool is 750g. My LW foaming pla natural at .5 flow rate produces a given plane at 86 grams, the same plane from pp cf, 115g, HT would be about 98-100g - i'll take the half ounce for significantly improved durability
Your lw prints are ok, but far from perfect in my book.. I'm getting much better results on a 7yr old tevo bw with plain pla-lw from colorfab.. (no banding, stringing or artefacts on outside skin). A part that takes 3hrs to print only has 15 seconds of travel in total.. this is because the models are not optimized for pla-lw/spiral mode printing and tons of wrong settings in default profile for filament...
Hi, This is sarah.Your content is quite a match with our brand's service and application scene. I would like to invite you to experience our 3DPrinting service and test our materials. May I ask about your interests?
yeah buddy a great job but u want u to support u in by giving money for 3d print filaments but in that case u should make the files free to use also for everyone out there
another nice build ! Wow, so many options now !
Nice model design improvements. Great to hear details on LW-PLA-HT material properties.
Thanks for the video, I enjoyed it.
Such beautifull gliders ! What about a 2m wingspan one ?
on the list, but have lots of distractions... 1.6M coming soon
I fell in love with this model, as soon as you throwed it and flew flawless, I will buy the files! Pls is there any chance to make a version with a center landing wheel and maybe two small others on the wings, I don't have the luxury of a grass strip😢.
been thinking about doing this. Skids on the wings.
Another chance to the taranis? Hehe
Shame that no one asking in your Contact page on your website. Ive asked if its possible to feet a 4s in your pod motor? With some 4s 1100-1500? This pod can feet a 28mm motor?
do you mean fit? Yes, a 28mm diameter motor will fit. And yes a 4S lipo will fit too. As you increase speed and desire to pull hard turns the material and design need to match. The LW foaming materials are great for sub 80 mph, but will need more stiffness for higher speeds... The Juicy wing, that will fit this fuselage, has been recorded at 187mph (300kph) doing dynamic soaring printed from PLA and hope to go faster.
@@soarkraft thanks for your asking. Have you got some customers tried the 6s setup ?
Havent been impressed with the PLA HT. Less foaming means a higher flow rate, putting it in the weight range of PP-CF, which is more durable, rigid, and withstands higher temperatures
do you mean the no-foaming PLA-HT (now called PLA-HP)?
I love the idea of CF materials, but they have never been worth the effort and cost.. I will have to look at PP-CF.
I don't think you can get PP-CF to a .6g/cm^3 density... best I could find was 1.0g/cm^3.
@@soarkraft the foaming HT foams less than the non HT. To achieve the same volume you need more flow compared to normal active foaming, in my experience, .15 more. The pp cf spool is 750g. My LW foaming pla natural at .5 flow rate produces a given plane at 86 grams, the same plane from pp cf, 115g, HT would be about 98-100g - i'll take the half ounce for significantly improved durability
Your lw prints are ok, but far from perfect in my book.. I'm getting much better results on a 7yr old tevo bw with plain pla-lw from colorfab.. (no banding, stringing or artefacts on outside skin). A part that takes 3hrs to print only has 15 seconds of travel in total.. this is because the models are not optimized for pla-lw/spiral mode printing and tons of wrong settings in default profile for filament...
Hi, This is sarah.Your content is quite a match with our brand's service and application scene. I would like to invite you to experience our 3DPrinting service and test our materials. May I ask about your interests?
yeah buddy a great job but u want u to support u in by giving money for 3d print filaments but in that case u should make the files free to use also for everyone out there
I only make money from files, I don't make anything from filaments. I just like trying new materials and showing how well my files work with them.
What radio did you go with? Is the more important question
I have a couple I'm considering, but it has been a huge distraction from what I want to work on.