Thank you, please keep in mind that compounding is just physical mixing, so the temperature should not be too high, otherwise the reaction will be activated. Therefore, please keep the temperature below 100°C to avoid hardening or vulcanization during compounding.
@@Vijay-n7l In this video, the initial temperature used was 50 °C. Due to internal friction, it sharply raised around 80-90 °C. After homogenization, it reduced continuously. Please watch carefully, it was shown in the graph. I mean changing of temp and torque with mixing time.
I was doing this in the mill. Why didn't you use epdm for water gasket?
Sir can you please help me for formula of rubber compound for bellow autoparts
We probably did our practical lab here! Good job. 👍
Totally!😃
Good 💯
Wat about temperature
Thank you, please keep in mind that compounding is just physical mixing, so the temperature should not be too high, otherwise the reaction will be activated. Therefore, please keep the temperature below 100°C to avoid hardening or vulcanization during compounding.
Thanks for ur reply sir ,but where the temperature is connected to dat process, I mean I didn't see any temperature up and downs in video
@@Vijay-n7l In this video, the initial temperature used was 50 °C. Due to internal friction, it sharply raised around 80-90 °C. After homogenization, it reduced continuously. Please watch carefully, it was shown in the graph. I mean changing of temp and torque with mixing time.
only sulphur where tmt mbts😂😂😂
sir give epdm curing agent persentage. zdbc, sulphur, tmt, zdc, mbt.
@@navinjain903can you please help me for rubber compound formula. Bellow auto parts nitrile