Eryone Standard Resin Vs. ABS-Like Resin

ABS-Like Vs. Standard Resin
A quick comparison (breaking 110mm long, properly cured samples with bare hands) between #Eryone Standard and ABS-Like resins, and it shows that the ABS-like resin has a higher toughness than the standard one and it tends to bend for more than (150° degrees) angle rather than breaking.
keep in mind, this is just a simple rough test, different users may experience different results according to various parameters and conditions.
#3d #3dprint #3dprinted #3dprinter #additivemanufacturing
""""""""""""""""""""""""""""""""
إنضموا الى مجموعتنا الخاصة بالثري دي برنتنك لتبادل المعلومات والنقاشات والمشاركات على الفيس بوك :
■ / 377990969602721
""""""""""""""""""""""""""""""""
تابعونا على منصات وسائل التواصل الإجتماعي :
■ / iraq3dp
■ / iraq3dp
■ / iraq3dp
■ / iraq3dp
■ / iraq3dp
■ t.me/Iraq3DP_C...
""""""""""""""""""""""""""""""""
أرحب بكافة الآراء والمقتراحات على الأيميل التالي :
■ [e-mail]
""""""""""""""""""""""""""""""""
ثري دي برنت ثري دي برنتنك #DIY #XYZee #xyzee_maker #3d #print #3dprint #3dprinted #3dprinter #3dprinting #additivemanufacturing #trend #trending #odd #satisfying #technology #ثري_دي #ثريدي #طباعة_ثلاثية_الابعاد #العراق #بغداد #طابعة_ثري_دي #الطباعة_ثلاثية_الابعاد #طابعات_ثلاثية_الابعاد #طابعة_ثلاثية الابعاد #طباعة_ثلاثي_الابعاد #طابعة

[@theyodicoyote]

Thank you, thank you, thank you! This is just the comparison I have been looking for.

[@Iraq3DP]

You're welcome, this a just a simple comparison just to make it easier for the users to decide which material best fits their applications.

[@adityarizky3713]

what company resin like abs is ?

[@Iraq3DP]

Both are Eryone

[@PedroSilva-wt6lw]

On your previous video regarding the ABS like resin (the partial vs fully cured one) the part breaks and this one doesn't! Is there any difference between them that allows this one to bend further? Thanks.

[@Iraq3DP]

You're right, on the previous video the samples were shorter (around 75mm) and both of them broke but in different degrees, the first one was under-cured one, and as I've observed it tended to shatter into crystal-like pieces, meanwhile the second one which was over-cured (harshly) it tended to break into two segments only, But in this test the samples were longer (around 110mm) and I've properly cured them (20-30 mins) which gave the perfect results (around 150° angle bending), anyway please never mind the previous video, I was referring to a very specific point, now it has been removed to prevent any misleading.