i just started welding in school and i hope to make it my future job once i graduate. Thank you so much for the help. I already feel good about my welding, my teacher says im in the same area as the elite welders in other schools. but your video will help me so much. theres always room for improvements even when your already set straight forward. Anyways enough of my rambling. Thank you so much
@@harrysweld8280 Thank you. Yeah, its that actual van I am repairing. The chassis at the rear is all rusted through so working on getting it back to perfect standard.
Iv been trying this with stainless steel 304 using 308 flux core but having real problem with penetration on the bottom plate it bonds to the edge of top plate perfectly but does not stick or even melt into the bottom plate anyone know what I’m doing wrong about the same current 23 on 1.5mm stainless
Hi sorry for the slow reply. I would be looking at between 24-25 volts at around 9-10 mpm depending on your machine. This may want to be higher if your looking for spray transfer rather than dip.
i just started welding in school and i hope to make it my future job once i graduate. Thank you so much for the help. I already feel good about my welding, my teacher says im in the same area as the elite welders in other schools. but your video will help me so much. theres always room for improvements even when your already set straight forward. Anyways enough of my rambling. Thank you so much
Glad to be of some help. Good luck with your future career.
Thank you dude i have an interview today and have to do some test pieces your videos help a lot so thank you for your time!
I hope the interview went well and you get the job.
Great vid, my college shows me nothing so this is great thank you
Cheers mate. Just starting out and your video is great. Ta
Not a problem, glad to be of help. Your planned journey looks like an
exciting adventure. Good luck.
@@harrysweld8280 Thank you. Yeah, its that actual van I am repairing. The chassis at the rear is all rusted through so working on getting it back to perfect standard.
Advice for welding laps with pulse spray? I get edgemelt bad or my weld is concave. Lap is thin to thick its easy to edge melt.
Iv been trying this with stainless steel 304 using 308 flux core but having real problem with penetration on the bottom plate it bonds to the edge of top plate perfectly but does not stick or even melt into the bottom plate anyone know what I’m doing wrong about the same current 23 on 1.5mm stainless
Hello bro. What volts and wire speed do you use for 1mm MIG filler wire? Thanks
Hi sorry for the slow reply. I would be looking at between 24-25 volts at around 9-10 mpm depending on your machine. This may want to be higher if your looking for spray transfer rather than dip.
Hallo brother i from indonesia
That’s wrong buddy, your bead isn’t flush with the bottom one
This video says nothing
3/16" to 1/4". and your weld sounds like that... you do not know how to set your machine...
I hope it's a joke ! When you hear when you're welding , damn , that's not good setings !! Wirespeed and voltage ...
exactly. Too much wirespeed....or it needs more voltage....