Wow. Love the subject matter expert sharing his immense understanding of ac welding and most importantly helping me develop my understanding of aluminum itself.
Hi, that was great video. cong.s. i wanna ask a question, what is the cause micro cracks (mainly located interpass borders), if i have chance to put a photo (but not) , u can see easly.
Thanks for the info. Great knowledge on the subject. In your professional opinion, could acetone work as a degreasing agent in place of ZeroTri? Thanks
Two things, you sound like your native country is England, so why say that word incorrectly?! And secondly you look like hack you up with a hatchet Harry from Lock Stock And Two Smoking Barrels. Top video though, good tips!
Wow. Love the subject matter expert sharing his immense understanding of ac welding and most importantly helping me develop my understanding of aluminum itself.
Great information! I had always wire brushed the oxide off then used acetone!
Hi, that was great video. cong.s.
i wanna ask a question, what is the cause micro cracks (mainly located interpass borders), if i have chance to put a photo (but not) , u can see easly.
Thanks for the info. Great knowledge on the subject. In your professional opinion, could acetone work as a degreasing agent in place of ZeroTri? Thanks
Hi there. Yes, our team has confirmed it is alright to use acetone as a degreasing agent.
i did not know this so thank you
very useful sir
Good video
Very useful information. Thank you.
Great clip Thanks Guv
Indeed sir abrade the weld surface with clean ss brush and wipe vigorously with acetone. Also flux the bottom of butt joints.
I would say he is from Scotland
👍👌🙂👍👌🙂👍👌🙂👍👌🙂
Two things, you sound like your native country is England, so why say that word incorrectly?! And secondly you look like hack you up with a hatchet Harry from Lock Stock And Two Smoking Barrels. Top video though, good tips!
@@somethingbritis1 don’t cry