"I put extra hardener in it so that it's extra thick" - this logic is not sound. As a chemical reaction, you want the ideal ratio. Adding more hardener can actually make it less hard.
While I agree extra hardener doesn't make it thicker, Polyester resin can be catalyzed from 1.0 to 3,0 percent to adjust the cure time for temperature. Epoxy is not adjustable by ratio. The real question is why use carbon with polyester or carbon for the mold.
hay Nick. spot on it wont make it thicker. what I think he is referring to is that it will cure faster, reducing the resin running. Steve only reason to use polyester would be to save money... carbon may be used if you are temperature curing the part. this is due to thermal expansion of the part and the mold.
I don't understand why all the hate in the comments, he gave us a good breakdown of the process, even leaving in the part where he messed up the flange so that someone watching could avoid that issue... thanks for the video dude.
Wow okay, the guy made a helpful how-to video with the best intentions and all the comments are all about “this is a mold and not forging” ...really guys!? ...this look is called “forged carbon fiber” it has nothing to do with forging the parts, that’s just what the look is called! OP: I think you do a great job at explaining the process in a way that’s easy to follow and understand. So thank you for the upload and for providing links to the products used in your video. 👍
He did a decent job in some aspects. However, supporting the wankers trying to pass off "forged carbon" as something other than the cheapest and lousiest way to use carbon is not something we should be expected to tolerate. Lambo and others need to be called out for these lies.
I'm guessing the reason he made this mold from carbon fiber is he didn't have fiberglass. And since this is a very small mold, it doesn't really use much carbon. Carbon prices have come waaayyy down compared to a few years ago. BUT, there is actually a reason that many molds are made from carbon fiber. When you're creating large parts which will be cured in an autoclave, you must make the molds from carbon. The rate of thermal expansion is different for carbon fiber and fiberglass, so if you make your mold from fiberglass and then lay it up in carbon fiber, you may have problems with the parts. But this probably would not have been a problem with this small part. There is no appreciable difference in the strength or durability of fiberglass when used in a mold. Carbon fiber is stronger for a given weight (which is what makes it so popular for lightweight applications) but fiberglass can be made just as strong. It will simply weigh more, but this is not a concern when making a mold.
THAT WAS AWESOME!! The mold making process was very straightforward and for most DIY guys would be possible. The fact that you took it all the way to the finished product was even better because no one had to guess what it would look like. Someone below commented "why not use fibergalss as the mold backing"...and I thought the same thing. Especially since fiberglass will harden the same as carbon fiber but be less expensive. I would ignore the "this not true forged carbon fiber" comments because all you're doing is going for the look. You're putting it on a motorcycle engine for crying out loud...not the interior or your Lamborghini to drive your super model girl friend around like some of the other commenters are surely doing (yeah, sure)!!
Why? WHY? wHy? WHy? whY??? WHYYYY??? wHy? (etc...etc...e-fucking-tc!) No matter how many of you ask it and no matter how many different ways you do, how about simply because..... "This effing cool ass UA-camr (not any of you NoTuber's) wanted to and did!" What is wrong with all of these miserable people? I am sitting here at 4am because I can't sleep. Why? Because I am recovering from my 3rd spinal fusion and I'm in an extreme amount of pain but yet I can see the excitement and joy JBellz here is getting from doing something he is obviously enjoying and his energy alone made me forget about my pain! To everyone that took the time to type out all the hateful uninspiring shit, I'm so sorry it didn't ease all your pain(s). I'm guessing you all live a worse life that me (I also have not been able to work in 2.5 years....this hurts a LOT too BTW) because to sit down and methodically point out faults that I couldn't have found in 1000 years, is an OBVIOUS indicator that your pain scale must be an 11 out of the possible 10! I didn't care 2 flying fooks if it was called forged or molded.....and what is "moulded"? Are you so self absorbed you had to include "u" into our word "mold"? LOL! I believe this was this gentleman's first time at this as well. If so, holy hell, I can't wait to watch more because I have some parts that I would like to make some molds of. I love that you went for it and chose to use a more permanent part to cast from instead of the floppy, few uses and you're done, silicone molds I'm use to seeing. Plus, silicone isn't cheap. Ok, Ok, OKKKKK! I could go on finding all the positive things I got from this video. I'm glad I don't read the comments first because I would have never had thought this video would have been as great as it was!!!! Thanks sir!
Good frist attempt...I would recommend when making the part apply a thicker expoy coat let it almost be tacky... also I get a old blender and mix the carbon with expoxy in blender good then add harder after blending it..the roll this dough out into a sheet of wax paper ie similar to a DIY preg preg but uses chopped fiber .freeze it for 1-2 h this will give u a longer working time... then apply in mold several layers then vaccum bag part no need for carbon fiber back up
@@gabedebaltz490yes prepreg required a special resin also a autoclave chamber ect. WE know that... we are discussing way to recreate the appearance and texture and look of forged carbon fiber which was developed jointly by Lamborghini and Callaway. If you ever watch the how they make parts they a blended woven carbon fiber mixture that is then roll out in a sheet then made into a pre peg sheet and then use die-cast mold...and press or vaccum formed into place and autoclave it.
@@772777777777777 Exactly the issue. Do not call it something it is not. The "forged" moniker is due to the process of extreme pressure both the press and the autoclave pushing and pulling pressure. This is casting. Calling something forged gives the impression that your "case cover" might survive a crash better than it will. I think it is a pretty part and he is learning a fun skill but this is how you ruin the reputation of certain things.
Lamborghini and Calloway trademark a process " forged carbon fiber" The word forged is gimik....made up trademarked nonsense word for a process which is "basically " woven carbon fiber and other composite mixtures pressed in to mold and vaccum bag in a autoclave oven to cure. There is no forged or forging of parts
I skinned the interior dash pieces for my sti and it was such a pain. I am differently going to be trying this. Great video. Liked, saved and subscribed.
J D hey JD....I have Wrx and am tired of trying to find forged carbon pieces for it...thinking of making some. Really want the look, want real carbon and more than a vinyl wrap.
I work on carbon fiber and fiberglass daily for the airforce. And as a hobby. My suggestion (2 cents) would be after you lay up the part vacume bag it and it will eliminate most all voids. Maybe even do resin infusion for the least amount of resin. Great looking part though.
Where'd you get the chopped fiber? Just cut it yourself? This part is a cover, no need to be super strong, its just for looks. I dont see why people are complaining it's not truly forged lol he said it in the video. Its just for looks and it looks perfect
Just a DIY tip. You can use hairspray in place of PVA...much cheaper. You can also use masking tape around the edge of the "part" and trim the shape of the said part...transfer said masking tape to foam board and cut for a flange.
I am not sure i like the look of the chopped CF but kudos for not just covering it on a single layer and resin or vinyl! Nice mould making used as well.
awesome video! yeah I was nervous thinking to my self there aint no way hes gonna get that part out with the way you had the first flange lol. Looks awesome dude good job making mold is so easy its fun!
I was really sceptical when the video started, but i must say it looks pretty good! I like the visual texture of the graphics. It doesn't look like the normal criss-cross look of carbon fiber. Great job! 👏👏
you need to do two sided mold to fit your motor inner parts its seams it will not sit in perfect snug on the bike those parts are made best using double sided mold use silicone for the other side
For the people calling this click bait. Lamborghini and a golf club manufacturer made up the term "forged carbon". Its basically the same thing JBelz just made, minus the extreme pressure used by the manufacturers.
Funny thing is anyone who does this on a high level sees this guy knows nada. First off we use s glass its much more stiff also we never use poly resin for a mold or a strong light carbon part. This isnt forged at all in any way.. You even layed the weive in a not very strong way let alone light... You didnt even vac it... The outer layers are the most critical to strengthen so the chop on the outside is not a strong idea at all... This doesnt have to cost much money but you gotta use your engineering brain. Worst your making it seem like you know something and furthering the availability of junk in the motorcycle community for profit... Your also very obviously very green to composites im pretty sure if you drop the bike these will crack let alone tighten the bolts abit too much since you forgot to add those metal sleeves in the part.. Ill give you a hint the factory one is a composite thats well made see how they have these sleeves? That covers the biggest of this but theres so much more so wrong here go to your local community college and take a boat building class it wont teach you alot but atleast youl learn the basics and you dont like your gel was too soft when you did that lay up. You can see carbon poking through on the part side because the resin you put on it had thinners in it you want the gel to be tacky not soft and sticking to your glove.. Sooooo much wrong just please go inform yourself and stop putting out shit. Someone who knows wayyyyyyyy more about all this. Oliver
@@oliverscorsim When I saw him making the mold out of carbon, I'm here having a full brain aneurysm trying to figure out why, I have watched more than a dozen videos from boat builders airplane builders, hot rodders, and bike builders..I have zero first hand experience, mainly cause I'm too poor to afford the time and materials to do what I would want to do.... As he was chopping up that pretty carbon I almost cried...it would have made a pretty Engine cover for my Lincoln...Or Trunk lid, doors, fenders...Anything but as junk used in a mold....
@@BlackTownie999 He probably didn't have any glass around. No reason at all to waste that carbon other than ease of use. Ultimately it is no more a waste of carbon than that incredibly weak part he made. If he got a part that looks the way he wants it to, and if he can get it mounted to the bike without it cracking around the bolt holes, then fine. If he can find dupes to buy it, fine. Personally I almost gagged at the appearance of it, but that's why it won't be on my bike.
...reading all the replys i was thinking, Perhaps make a 2 part mold and pressure the carbon fibre inbetween, can maybe use a big table bench set-up for keeping it under pressure for 24 hours old the good old fashion way with with 4 to 6 50kg wheight plates on it
Wouldn't the chopper carbon fibre have been enough on its own to make the part? You added another layer of carbon fibre cloth. Did you have to do that?
this was an awesome video. very cool. might try it out myself to get the forged carbon look on some parts. I get that forged carbon is the aesthetic and that this doesn't come from a billion dollar factory process unlike most of this comment section
That part turned out great! To make it look even better I’d invest in a WichiTech composite repair system. You can put the part under vacuum and get cleaner parts.
Or u could build an autoclave for less then £200 if your smart enough! Do you work for whatever company you just mentioned, how much is their system, what size parts can it accommodate?
theres normal carbon fibre (that you have that stretches and frays) then theres a pro finish carbon that doesnt stretch or fray. recommend using the pro finish carbon if you plan on making more parts
Okay, maybe he wrong when he said "forged" but, man!! Can you just focus on what the real thing that this man try to do. It's the most important thing more than his false when he said it was "forged"
MuffinMan0521 he was trying to achieve a forge carbon look. Forge carbon is made with a different technique and is stronger than regular molded carbon due to the heat and compression.
Get a harbor freight vacuum pump 90$ and you will be able to get some really good results with it. If you vacuum it you will also get stronger parts than a open air mold, and lighter parts too.
"I put extra hardener in it so that it's extra thick" - this logic is not sound. As a chemical reaction, you want the ideal ratio. Adding more hardener can actually make it less hard.
While I agree extra hardener doesn't make it thicker, Polyester resin can be catalyzed from 1.0 to 3,0 percent to adjust the cure time for temperature. Epoxy is not adjustable by ratio. The real question is why use carbon with polyester or carbon for the mold.
hay Nick. spot on it wont make it thicker. what I think he is referring to is that it will cure faster, reducing the resin running. Steve only reason to use polyester would be to save money... carbon may be used if you are temperature curing the part. this is due to thermal expansion of the part and the mold.
So for small parts, its not possible to use carbon fibre with poliester resin?
@@stevemccormick4938 carbon for the mold: free stuff. nobody paying this shit him self uses carbon fibre for the mould (of such a non critical part).
@@FragBenitez you can use polyester resin with carbon fiber. Its just personal preference i guess, depending on what you re making
I don't understand why all the hate in the comments, he gave us a good breakdown of the process, even leaving in the part where he messed up the flange so that someone watching could avoid that issue... thanks for the video dude.
Awesome ! I work in the composites industry and people will over analyze why they can't do that, you just did in a couple days. Thanks for sharing !
That was crazy how easy it was..just time consuming. Can't wait to start making my own parts too. Thanks for the share!
Wow okay, the guy made a helpful how-to video with the best intentions and all the comments are all about “this is a mold and not forging” ...really guys!? ...this look is called “forged carbon fiber” it has nothing to do with forging the parts, that’s just what the look is called!
OP: I think you do a great job at explaining the process in a way that’s easy to follow and understand. So thank you for the upload and for providing links to the products used in your video. 👍
He did a decent job in some aspects. However, supporting the wankers trying to pass off "forged carbon" as something other than the cheapest and lousiest way to use carbon is not something we should be expected to tolerate. Lambo and others need to be called out for these lies.
@@bvcxzgt5451 have you send them a letter yet?
Why make the mold from carbon fiber? Wouldn't fiberglass be cheaper?
It would, but it wouldn't be as strong or last as long.
Glass moulds last fine if you do them right. Using carbon fibre is just a waste.
@@8145dwerdna hmmm not true
Then explain and give reason as to why.
It's a known fact carbon is much stronger of a material than fiberglass.
I'm guessing the reason he made this mold from carbon fiber is he didn't have fiberglass. And since this is a very small mold, it doesn't really use much carbon. Carbon prices have come waaayyy down compared to a few years ago. BUT, there is actually a reason that many molds are made from carbon fiber.
When you're creating large parts which will be cured in an autoclave, you must make the molds from carbon. The rate of thermal expansion is different for carbon fiber and fiberglass, so if you make your mold from fiberglass and then lay it up in carbon fiber, you may have problems with the parts. But this probably would not have been a problem with this small part.
There is no appreciable difference in the strength or durability of fiberglass when used in a mold. Carbon fiber is stronger for a given weight (which is what makes it so popular for lightweight applications) but fiberglass can be made just as strong. It will simply weigh more, but this is not a concern when making a mold.
THAT WAS AWESOME!! The mold making process was very straightforward and for most DIY guys would be possible. The fact that you took it all the way to the finished product was even better because no one had to guess what it would look like. Someone below commented "why not use fibergalss as the mold backing"...and I thought the same thing. Especially since fiberglass will harden the same as carbon fiber but be less expensive. I would ignore the "this not true forged carbon fiber" comments because all you're doing is going for the look. You're putting it on a motorcycle engine for crying out loud...not the interior or your Lamborghini to drive your super model girl friend around like some of the other commenters are surely doing (yeah, sure)!!
best video on youtube on this topic. thanks. i feel confident remaking some parts now
Why? WHY? wHy? WHy? whY??? WHYYYY??? wHy? (etc...etc...e-fucking-tc!)
No matter how many of you ask it and no matter how many different ways you do, how about simply because.....
"This effing cool ass UA-camr (not any of you NoTuber's) wanted to and did!"
What is wrong with all of these miserable people? I am sitting here at 4am because I can't sleep. Why? Because I am recovering from my 3rd spinal fusion and I'm in an extreme amount of pain but yet I can see the excitement and joy JBellz here is getting from doing something he is obviously enjoying and his energy alone made me forget about my pain!
To everyone that took the time to type out all the hateful uninspiring shit, I'm so sorry it didn't ease all your pain(s). I'm guessing you all live a worse life that me (I also have not been able to work in 2.5 years....this hurts a LOT too BTW) because to sit down and methodically point out faults that I couldn't have found in 1000 years, is an OBVIOUS indicator that your pain scale must be an 11 out of the possible 10!
I didn't care 2 flying fooks if it was called forged or molded.....and what is "moulded"? Are you so self absorbed you had to include "u" into our word "mold"?
LOL!
I believe this was this gentleman's first time at this as well. If so, holy hell, I can't wait to watch more because I have some parts that I would like to make some molds of.
I love that you went for it and chose to use a more permanent part to cast from instead of the floppy, few uses and you're done, silicone molds I'm use to seeing. Plus, silicone isn't cheap.
Ok, Ok, OKKKKK!
I could go on finding all the positive things I got from this video. I'm glad I don't read the comments first because I would have never had thought this video would have been as great as it was!!!!
Thanks sir!
Can you use a mold release and use liquid urethane and trim accordingly?
Although I have never spray gel coat I never had luck brushing it on either. In due time I will get the sprayer and try that method
Looks great, thank you for taking the time to show us the steps.
you're a real one for posting this video imma start adding some parts on my bike too
Good frist attempt...I would recommend when making the part apply a thicker expoy coat let it almost be tacky... also I get a old blender and mix the carbon with expoxy in blender good then add harder after blending it..the roll this dough out into a sheet of wax paper ie similar to a DIY preg preg but uses chopped fiber .freeze it for 1-2 h this will give u a longer working time... then apply in mold several layers then vaccum bag part no need for carbon fiber back up
But doing so you're not gonna see the full carbon sheet, are you?
blended carbon with resin is not prepreg. You guys are doing diy nonsense. chopped or "minced" strand matt being slathered with resin is not prepreg.
@@gabedebaltz490yes prepreg required a special resin also a autoclave chamber ect. WE know that... we are discussing way to recreate the appearance and texture and look of forged carbon fiber which was developed jointly by Lamborghini and Callaway. If you ever watch the how they make parts they a blended woven carbon fiber mixture that is then roll out in a sheet then made into a pre peg sheet and then use die-cast mold...and press or vaccum formed into place and autoclave it.
@@772777777777777 Exactly the issue. Do not call it something it is not. The "forged" moniker is due to the process of extreme pressure both the press and the autoclave pushing and pulling pressure. This is casting. Calling something forged gives the impression that your "case cover" might survive a crash better than it will. I think it is a pretty part and he is learning a fun skill but this is how you ruin the reputation of certain things.
Lamborghini and Calloway trademark a process " forged carbon fiber"
The word forged is gimik....made up trademarked nonsense word for a process which is "basically " woven carbon fiber and other composite mixtures pressed in to mold and vaccum bag in a autoclave oven to cure.
There is no forged or forging of parts
I skinned the interior dash pieces for my sti and it was such a pain. I am differently going to be trying this. Great video. Liked, saved and subscribed.
J D hey JD....I have Wrx and am tired of trying to find forged carbon pieces for it...thinking of making some. Really want the look, want real carbon and more than a vinyl wrap.
I work on carbon fiber and fiberglass daily for the airforce. And as a hobby.
My suggestion (2 cents) would be after you lay up the part vacume bag it and it will eliminate most all voids. Maybe even do resin infusion for the least amount of resin.
Great looking part though.
I like this look, this is briliant!
Do those engine covers actually hold oil and fluid in or are they just added protection for the engine case?
Incredible patience and craftsmanship....... awesome stuff
Sick work! Congratulations! Regards from Argentina.
Where'd you get the chopped fiber? Just cut it yourself? This part is a cover, no need to be super strong, its just for looks. I dont see why people are complaining it's not truly forged lol he said it in the video. Its just for looks and it looks perfect
You can chop it with a mini robot for kitchen
Just search google for "chopped carbon tow". Lots of composites supply houses will sell you the stuff, pre-chopped to accurate lengths.
www.venomcarbon.com
Awesome work! Really cool of you to show the moulding process!
Just a DIY tip. You can use hairspray in place of PVA...much cheaper. You can also use masking tape around the edge of the "part" and trim the shape of the said part...transfer said masking tape to foam board and cut for a flange.
Or Elmer's glue ,aka pva glue
hello, i'm french sorry for my english but where do you found the "forged carbon" in your tube ? thank's
I am not sure i like the look of the chopped CF but kudos for not just covering it on a single layer and resin or vinyl! Nice mould making used as well.
Dude Nice job , Well done
Beautiful looking part. Awesome work, keep learning!
You showed where to get the carbon fiber and resin kit, what website for the rest: gel coat, PVA film and paste? Thanks
My dad molded one for my yz out of 6 tubes of JB weld. That was 20 years ago and it’s still on my bike
Super like the "not how you do it part", without you showing I am going to do the same way!
awesome video! yeah I was nervous thinking to my self there aint no way hes gonna get that part out with the way you had the first flange lol. Looks awesome dude good job making mold is so easy its fun!
People here sayin it’s not forged.... yes it’s moulded but it still looks good and do it’s function
I was really sceptical when the video started, but i must say it looks pretty good! I like the visual texture of the graphics. It doesn't look like the normal criss-cross look of carbon fiber. Great job! 👏👏
This is forged carbon not the regular carbon fiber weave everyone is use to
F the haters man, you did good work here! don't quit keep going!
What about galvanic corrosion?
What if you mix that with glass fiber next time? Or coloured kevlar fibers?
Do you need to use the carbon that’s not chopped or can you just use chopped
How was your clearances inside? I’m curious if you had rubbing issues
Did you weigh it and compare it to the original part? It looks like you don't need that many layers
How do you get screw threads to go into it?
you need to do two sided mold to fit your motor inner parts
its seams it will not sit in perfect snug on the bike
those parts are made best using double sided mold use silicone for the other side
For the people calling this click bait. Lamborghini and a golf club manufacturer made up the term "forged carbon". Its basically the same thing JBelz just made, minus the extreme pressure used by the manufacturers.
Hey @JBellz, part looks great and so does the mold. Did you use carbon to create the mold because you had a lot of carbon or because its cheaper ?
Subscribed! That looks so sick man! look forward to seeing the other parts
for the part process..do you used gel coat for the first layer? or do you just used epoxy?
Why carbon for your mold instead of fiberglass? Much cheaper and still very rigid
Jerry Inman complete light weight
@@lluciferl9276 why does the mold need to be light weight?
Funny thing is anyone who does this on a high level sees this guy knows nada. First off we use s glass its much more stiff also we never use poly resin for a mold or a strong light carbon part. This isnt forged at all in any way.. You even layed the weive in a not very strong way let alone light... You didnt even vac it... The outer layers are the most critical to strengthen so the chop on the outside is not a strong idea at all... This doesnt have to cost much money but you gotta use your engineering brain. Worst your making it seem like you know something and furthering the availability of junk in the motorcycle community for profit... Your also very obviously very green to composites im pretty sure if you drop the bike these will crack let alone tighten the bolts abit too much since you forgot to add those metal sleeves in the part.. Ill give you a hint the factory one is a composite thats well made see how they have these sleeves? That covers the biggest of this but theres so much more so wrong here go to your local community college and take a boat building class it wont teach you alot but atleast youl learn the basics and you dont like your gel was too soft when you did that lay up. You can see carbon poking through on the part side because the resin you put on it had thinners in it you want the gel to be tacky not soft and sticking to your glove.. Sooooo much wrong just please go inform yourself and stop putting out shit.
Someone who knows wayyyyyyyy more about all this. Oliver
@@oliverscorsim When I saw him making the mold out of carbon, I'm here having a full brain aneurysm trying to figure out why, I have watched more than a dozen videos from boat builders airplane builders, hot rodders, and bike builders..I have zero first hand experience, mainly cause I'm too poor to afford the time and materials to do what I would want to do....
As he was chopping up that pretty carbon I almost cried...it would have made a pretty Engine cover for my Lincoln...Or Trunk lid, doors, fenders...Anything but as junk used in a mold....
@@BlackTownie999 He probably didn't have any glass around. No reason at all to waste that carbon other than ease of use. Ultimately it is no more a waste of carbon than that incredibly weak part he made. If he got a part that looks the way he wants it to, and if he can get it mounted to the bike without it cracking around the bolt holes, then fine. If he can find dupes to buy it, fine. Personally I almost gagged at the appearance of it, but that's why it won't be on my bike.
Where do you get your resin and other supplies? What products do you use for this project? Thanks
it's it fully semi auto?
Forging?
No vacuum bagging?
...reading all the replys i was thinking, Perhaps make a 2 part mold and pressure the carbon fibre inbetween, can maybe use a big table bench set-up for keeping it under pressure for 24 hours old the good old fashion way with with 4 to 6 50kg wheight plates on it
Wouldn't the chopper carbon fibre have been enough on its own to make the part? You added another layer of carbon fibre cloth. Did you have to do that?
Is there any specific reason you choose to make the mold with CF and not fiberglass?
Great job man 👍👏 love it
Nice job making that part.
this was an awesome video. very cool. might try it out myself to get the forged carbon look on some parts. I get that forged carbon is the aesthetic and that this doesn't come from a billion dollar factory process unlike most of this comment section
this is to forged carbon fiber, what a vinyl wrap is to regular carbon fiber.
Was the part very hard?
What's the weight difference between the original part and the carbon part?
What color pigment did you add to the Gel Coat?
So its just a forged carbon skin?
not sure why this is on my recommened page. but it was awesome and got you a sub!
That part turned out great! To make it look even better I’d invest in a WichiTech composite repair system. You can put the part under vacuum and get cleaner parts.
Or u could build an autoclave for less then £200 if your smart enough! Do you work for whatever company you just mentioned, how much is their system, what size parts can it accommodate?
I don’t work for that company. We just use their products. I’m not sure how much they cost tho lol
theres normal carbon fibre (that you have that stretches and frays) then theres a pro finish carbon that doesnt stretch or fray. recommend using the pro finish carbon if you plan on making more parts
It's beautiful 😭 excellent/quality work 👍😎
Nice! I like your style.
Yoo that looks sick!
Glad you caught your flange setup mistake! I was watching along and just thinking the mold would lock on with the negative draft angle.
I want to ask. Why the molding need carbon fiber at the outside? :/
Did you actually fit it on the bike?
What product do I have to look for if I want to buy the carbon flakes used in this video?
I appreciate this thank you dont let the comments get to you keep it up as you said for looks i was wondering how to achieve this look myself
Okay, maybe he wrong when he said "forged" but, man!! Can you just focus on what the real thing that this man try to do. It's the most important thing more than his false when he said it was "forged"
He knows its not real forged he said it near the start of the video he said he was just going for that Forged look
Awesome job man! 👏👏
I think ive just had a crisis in my pants 😬
That looks awesome bro! Sick bike too, love it
How hard will the parts be?
..why would you use CF for a MOULD???
Well done mate
are you using 1/4 inch or 1/8 inch chopped carbon ?
was it a special clay or just any clay
That's very creative of you! 👍👍
Can you suggest a website that has a starter kit (partal paste, partl film#10)? Thanks
Was the chopped carbon just for aesthetic purposes or was there another reason?
MuffinMan0521 he was trying to achieve a forge carbon look. Forge carbon is made with a different technique and is stronger than regular molded carbon due to the heat and compression.
Hi! Where can I get a molding clay or whatever you use there?
About what was the cost of all the materials needed to do a small project like this?
What is PVA?
why not put a layer of kevlar in there? just in case you drop the bike
Hi , you applied two coats of tooling gel coat, did you apply them straight after one another or once the first one dried ??
How much did it cost total to do it yourself?
Came out great. I think I'll find use for this on lots of projects. I like seeing these from start to finish, along with the mistakes. Sub'd.
Get a harbor freight vacuum pump 90$ and you will be able to get some really good results with it. If you vacuum it you will also get stronger parts than a open air mold, and lighter parts too.
the foam i used dissolved when it touched the gel coat, what kind of foam should i use? does anyone have a link?
Use a foam board, not styrofoam
would you be willing to sell the mold?
what do you use to clean the carbon after sanding ?
Very nice. Especially the name.
I think if he use infusion process the final product can be more rigid n nice look😍😍
Excellent work, mate but i have a question: what about the screw casing?
My compliments for your bike by a Ducatista!
Interesting stuff and very cool - interested to know how they hold up to high temps.
When you were making this.. Was the chopped up pieces of carbon just the normal weave just chopped up into little pieces?
Being a metal work forged is very different. But im into carbon and make carbon fiber welding hoods. That could be a cool look on the hoods!