Really nice materials. The plating on the stainless will probably be a really good cell. Ya I'm fighting leads and the connection on my charger . Like you say it makes a big difference . I like the frog he is like a mascot. I'm in no hurry to see the results.Would probably be more accurate results. Thanks Dan and look forward to see the results.
Nice work mate! im in the process of making an electric kiln to do similar things with batteries, I've got a lot of ideas from robert murray smith's channel you might find it helpfull too.
Dennis Kramer about 800 decrees c. I think this burn was a bit hotter the co2 cylinder was glowing red hot. It lowered the ohms to about 7. The first small bit of felt was not as hot and measured 26 ohms there about. Hotter the better I think with in reason.
@@danp1224 Thanks Dan - I just got a little used kiln going. Will start experiments at 800C. Want to try some wool felt, Rayon (PAN?), and Oasis foam....all for cathode materials...
Dennis Kramer Hi. Are you using a container to limit the air. I also put carbon bbq brick in there. Not sure what material it is made from. It just said felt.
@@danp1224 I have a section of 2" I'd pipe closed off with caps...1/16" vent hole...like RMS...worked great for oasis foam carbonization....I think the wool felt I was using was a synthetic blend and at 800 C evaporated away...the carbon ash was very conductive though
on the negative side negative release less negative space and posetive is tacing from the medium that taces from the carbon and carbon taces from the negative side. electric we see pasetuve (less negative as negative and posetive where there is more thention towart energy behavieures for that particles to to be more exeterated for men to masser small chainces 🙏💜🙏 I am amazed you use oil😍 how dit you come to use oils behavieure of the medium 👀¿😍🙏😍 the carbon tisheu is leaking in to the olisch and the Flux of there cores is bilding op more external thentional behavieures of the medieum for it to start gentiles pulling releasing pulling releasing for the elongated structures to apeure😍💜😍 when you make a coil around it like the cathode ray tube you probebley with the right tuning wil create conditions for it to seaside to become tunneled structures. carbon wil behave as the coherence resonance of the coil🤣😍🛸
I cleaned op carbon with a coper nanolayers foil around the jar to translate eurths coherence in a dna motional behavieure . I ended ip with microdaimands and the blackers carbons this way💜 notice ........ dinamic motion of directional polarization of the nano coper foil has to bee in line with eurths infiseble eurth ring its coherence towart eurths behavieure of existance . other wishes you get smashing and bumping radiation to disturbed the stations of the cells trout the gravatron translations of cosmic informations of the total set of conditions to provoce the desistion of its behavieures😍😃😍 🐒🌀
I've heard that heavy denim makes the best carbon felt.
Awesome Dan! I can't wait to see how your carbon felt performs. Thanks for sharing. :) :)
Really nice materials. The plating on the stainless will probably be a really good cell. Ya I'm fighting leads and the connection on my charger . Like you say it makes a big difference .
I like the frog he is like a mascot. I'm in no hurry to see the results.Would probably be more accurate results.
Thanks Dan and look forward to see the results.
Very good work Dan, you should try to soak the felt in zinc chloride or iron chloride before calcination
That carbon felt looks interesting Dan looking forward to that .
nicely done! Have you 'flame tested' the carbon felt you've made?
No.
Nice work mate! im in the process of making an electric kiln to do similar things with batteries, I've got a lot of ideas from robert murray smith's channel you might find it helpfull too.
Thank you
Do you have a reference for that??
Hi there. Reference for what part. ???
Nice Dan - was that 800 C or F
Dennis Kramer about 800 decrees c. I think this burn was a bit hotter the co2 cylinder was glowing red hot. It lowered the ohms to about 7. The first small bit of felt was not as hot and measured 26 ohms there about. Hotter the better I think with in reason.
@@danp1224 Thanks Dan - I just got a little used kiln going. Will start experiments at 800C. Want to try some wool felt, Rayon (PAN?), and Oasis foam....all for cathode materials...
Hi Dan.....do you know what the fabric content was for those sheets of cloth......so far my tests have just produced melted ash
Dennis Kramer Hi. Are you using a container to limit the air. I also put carbon bbq brick in there. Not sure what material it is made from. It just said felt.
@@danp1224 I have a section of 2" I'd pipe closed off with caps...1/16" vent hole...like RMS...worked great for oasis foam carbonization....I think the wool felt I was using was a synthetic blend and at 800 C evaporated away...the carbon ash was very conductive though
Ok please carry on.
no queda unido, se deshace.
Your drifting stay in the right lane.
on the negative side negative release less negative space and posetive is tacing from the medium that taces from the carbon and carbon taces from the negative side.
electric we see pasetuve (less negative as negative and posetive where there is more thention towart energy behavieures for that particles to to be more exeterated for men to masser small chainces 🙏💜🙏
I am amazed you use oil😍
how dit you come to use oils behavieure of the medium 👀¿😍🙏😍
the carbon tisheu is leaking in to the olisch and the Flux of there cores is bilding op more external thentional behavieures of the medieum for it to start gentiles pulling releasing pulling releasing for the elongated structures to apeure😍💜😍
when you make a coil around it like the cathode ray tube you probebley with the right tuning wil create conditions for it to seaside to become tunneled structures.
carbon wil behave as the coherence resonance of the coil🤣😍🛸
I cleaned op carbon with a coper nanolayers foil around the jar to translate eurths coherence in a dna motional behavieure .
I ended ip with microdaimands and the blackers carbons this way💜
notice ........
dinamic motion of directional polarization of the nano coper foil has to bee in line with eurths infiseble eurth ring its coherence towart eurths behavieure of existance .
other wishes you get smashing and bumping radiation to disturbed the stations of the cells trout the gravatron translations of cosmic informations of the total set of conditions to provoce the desistion of its behavieures😍😃😍
🐒🌀
and in this rheal of dimentional understanding 0 DC is feading and plus DC is pulling🙏😍🙏