Vielen Dank für die Vorführung Ihrer Handwerkskunst! Von einem wirklichen Könner wie Ihnen lerne ich in einem Augenblick unglaublich viel. Ich weiß das zu schätzen. (Ich bin kein gelernter Goldschmied, aber ich setze kreative Ideen um und manchmal komme ich nicht weiter, weil man kann eben nicht dauernd das Rad neu erfinden.Natürlich sind meine Arbeiten viel einfacher und weniger anspruchsvoll, aber um Technische Vollendung geht's mir ja auch nicht.) Dankeschön
finally i got an basic idea about how the ring pattern came to be lol :) iv watched a lot of videos, and this is the first that i actually could use for anything :) thank you a lot :)
Yes, that is possible. With silver hard solder. The size of the blank should be maximum 20 x 100 mm. The surfaces must be sanded with 240 sandpaper and lie perfectly flat on top of each other. The contact surfaces must be cleaned with borax (do not use any other flux) and then coated before they come to rest on top of one another. The material is tied together with iron wire. Solder only 2 sheets at a time. Use wide, long strips of solder. The solder is fed in from one long side until it visibly flows out on the other side. If you don't work fussy, clean and correct, you will end up disappointed. don't overheat the matterial. but make sure that you heat the two metal surfaces evenly on both sides. do not warm slowly. it has to be done quickly. be careful. good luck.
There is no constant number. Depending on the material combination, alloys with copper are very hard. Also be careful with very soft material. Use material with as identical a coefficient of expansion as possible. wish you good luck.
Hallo Armin. Danke für dieses tolle Video. Derzeit sitze ich selbst an einem Silber/Kupfer- Mokume Gane, aber ich habe mir immer die Frage gestellt, wie man seinen tordierten Block zu einem fugenlosen Ring bekommt... Die Antwort fand ich hier. Danke dir für deine Mühe und Arbeit. Liebe Grüße Jana
Nächstes Update: ich bin auf die Idee gekommen Silberlot dünn auszuwalzen und Lötfolien 0.15 mm zu versuchen. Bzw. Auch selbst geeignete Legierungen herzustellen. Beides funktioniert hervorragend, die Ergebnisse sind auch bei etwas weniger Sorgfalt (d.h. zügiger arbeiten) äußerst sauber. Ich habe entdeckt, es gibt auch industrielle Lötfolien für flächige Lötungen, was noch einfacher wäre, diese habe ich aber noch nicht genau unter die Lupe genommen. Jedenfalls ist das für mich ein Durchbruch in dieser Technik, um die Ergebnisse berechenbarer zu bekommen und Missgeschicke auszuschließen. 😅
Update: ich habe es jetzt schon 2 x versucht, es geht! Das 2e Exemplar hat 8 Schichten und wird fast perfekt 😊 Wenn ich demnächst ne Walze besitze, wird es vermutlich noch viel einfacher. Ganz herzlichen Dank, Sie haben mir wirklich sehr geholfen, es gibt immer noch genug zu rausfinden. (Zb die kleinen Störungen zwischen den Blechen, winzige schwarze Pünktchen, wo der Kontakt nicht so ganz da ist, sind kaum zu vermeiden. Aber das lässt sich noch korrigieren, zum Glück 😅. Das war am Ende nicht schwer, aber erstmal rausfinden...) Falls Sie das noch sehen sollten, ich kann es nicht oft genug sagen: Danke! Schöne Grüße!
hi armin, nice video. i want to try mokume gane myself, but i find it very hard to find the correct materials. because i want to give it a try i dont want to spend much money. any tips for metals to combine with copper?
Hi I was wondering if you could give me some advice in cutting perfectly straight down the billet as i always tend to cut one side more than another. Fantastic video would love to see more!!! Thanks
Hello sir its very beautiful piece you have done! And how do you calculate the ring size with this drilling and sawing technique and what is the name of this technique?
Hi Инко Н.О, This is Mokum Gane split technique and twist. First calculate the volume of the finished ring. add about 50% material. This gives the starting material. The final size is obtained by swaging or forging.
Нее, Иван, все понятно. Видимо ты не в теме. Он спек( спаял) два металла: серебро и палладий. Потом в определенном и контролируемом хаосе придал узор спаянным металлам. И в итоге изготовил две обручалки в стиле мокуме гане. В этой технике можно варьировать металлами разными, в зависимости от задумки и хотелки изготовителя и заказчика. Бывают весьма достойные узоры. Но! Приятно, что это тебе понравилось.
Vielen Dank für die Vorführung Ihrer Handwerkskunst! Von einem wirklichen Könner wie Ihnen lerne ich in einem Augenblick unglaublich viel.
Ich weiß das zu schätzen.
(Ich bin kein gelernter Goldschmied, aber ich setze kreative Ideen um und manchmal komme ich nicht weiter, weil man kann eben nicht dauernd das Rad neu erfinden.Natürlich sind meine Arbeiten viel einfacher und weniger anspruchsvoll, aber um Technische Vollendung geht's mir ja auch nicht.)
Dankeschön
Ich bin schwer beeindruckt. Vielen Dank für das Video.
finally i got an basic idea about how the ring pattern came to be lol :) iv watched a lot of videos, and this is the first that i actually could use for anything :) thank you a lot :)
Beautiful work.'
wish i had the tools to do it.
thanks for sharing
Yes, that is possible.
With silver hard solder.
The size of the blank should be maximum 20 x 100 mm.
The surfaces must be sanded with 240 sandpaper and lie perfectly flat on top of each other. The contact surfaces must be cleaned with borax (do not use any other flux) and then coated before they come to rest on top of one another. The material is tied together with iron wire.
Solder only 2 sheets at a time.
Use wide, long strips of solder.
The solder is fed in from one long side until it visibly flows out on the other side.
If you don't work fussy, clean and correct, you will end up disappointed.
don't overheat the matterial. but make sure that you heat the two metal surfaces evenly on both sides.
do not warm slowly. it has to be done quickly.
be careful. good luck.
Thank you Armin, very cool!
👍👏🍻весьма достойно! Респект!
hermoso trabajo , conociendo esta bella tecnica ,gracias.....
WOW BEAUTIFUL!
Wow nice metal work skills! :o
Thanks for the appreciation
There is no constant number. Depending on the material combination, alloys with copper are very hard. Also be careful with very soft material. Use material with as identical a coefficient of expansion as possible.
wish you good luck.
Wow great work, man and a lot of work. What do you charge for this beautiful artist ring.
Great tutorial! Thank you for sharing!
Hallo Armin. Danke für dieses tolle Video. Derzeit sitze ich selbst an einem Silber/Kupfer- Mokume Gane, aber ich habe mir immer die Frage gestellt, wie man seinen tordierten Block zu einem fugenlosen Ring bekommt... Die Antwort fand ich hier.
Danke dir für deine Mühe und Arbeit. Liebe Grüße Jana
Nächstes Update: ich bin auf die Idee gekommen Silberlot dünn auszuwalzen und Lötfolien 0.15 mm zu versuchen. Bzw. Auch selbst geeignete Legierungen herzustellen. Beides funktioniert hervorragend, die Ergebnisse sind auch bei etwas weniger Sorgfalt (d.h. zügiger arbeiten) äußerst sauber.
Ich habe entdeckt, es gibt auch industrielle Lötfolien für flächige Lötungen, was noch einfacher wäre, diese habe ich aber noch nicht genau unter die Lupe genommen.
Jedenfalls ist das für mich ein Durchbruch in dieser Technik, um die Ergebnisse berechenbarer zu bekommen und Missgeschicke auszuschließen. 😅
Is it possible just to solder the layers together without fusing them. Both rings came out great.
Very nice
Update: ich habe es jetzt schon 2 x versucht, es geht! Das 2e Exemplar hat 8 Schichten und wird fast perfekt 😊
Wenn ich demnächst ne Walze besitze, wird es vermutlich noch viel einfacher.
Ganz herzlichen Dank, Sie haben mir wirklich sehr geholfen, es gibt immer noch genug zu rausfinden. (Zb die kleinen Störungen zwischen den Blechen, winzige schwarze Pünktchen, wo der Kontakt nicht so ganz da ist, sind kaum zu vermeiden. Aber das lässt sich noch korrigieren, zum Glück 😅. Das war am Ende nicht schwer, aber erstmal rausfinden...)
Falls Sie das noch sehen sollten, ich kann es nicht oft genug sagen: Danke!
Schöne Grüße!
The metals are Silver 925/000 and Palladium 500
Hi David,Smithing compresses the material.
The layers are thereby better connected.
But beware. Do not forge too long in the same place.Armin
How many heats did that take
very nice, thanks for sharing
Fantastic work.
Can I ask how you increase the contrast on finishing the mokume, actualy with what you finish or polish?
Nice work.
Cool.
hello, I hold the saw slightly diagonally forward. Also, I often turn the part to be sawn that the bottom is up.
Cheap metal combinations are brass or gilding metal (95/5). Silver 925/000. But be careful. Copper next to silver melts at 770 C ° Eutectic point
hi armin, nice video. i want to try mokume gane myself, but i find it very hard to find the correct materials. because i want to give it a try i dont want to spend much money. any tips for metals to combine with copper?
Hi I was wondering if you could give me some advice in cutting perfectly straight down the billet as i always tend to cut one side more than another. Fantastic video would love to see more!!! Thanks
Hello Armin thats a beautiful ring!
May i ask what blowtorch are you using?
Would appreciate your answer.
Best regards!
Hello,
I have propane gas and the flame attracts air from the environment.
Also I have hydrogen with oxygen.
Greetings Armin
Hello sir its very beautiful piece you have done! And how do you calculate the ring size with this drilling and sawing technique and what is the name of this technique?
Hi Инко Н.О,
This is Mokum Gane split technique and twist. First calculate the volume of the finished ring. add about 50% material. This gives the starting material. The final size is obtained by swaging or forging.
Hi, it is best if the surface is not polished. use pumice stone powder and matt the surface fine. The surface is sealed with beeswax.
what kind of metals did u used?
In this work: Palladium 500/000 and Silver 925/000
Anyone know why he hammers it after he anneals it?
I've never worked w/ palladium. It looks like a very hard metal to work with...literally.
I work with 500/000 palladium. It's not that hard either. The glow between the individual forging steps is important.
جميل جدا جدا ممتاز احسنت
Нихрена не понятно!но в конце красивая вещь!!!
Нее, Иван, все понятно. Видимо ты не в теме. Он спек( спаял) два металла: серебро и палладий. Потом в определенном и контролируемом хаосе придал узор спаянным металлам. И в итоге изготовил две обручалки в стиле мокуме гане. В этой технике можно варьировать металлами разными, в зависимости от задумки и хотелки изготовителя и заказчика. Бывают весьма достойные узоры.
Но! Приятно, что это тебе понравилось.
Wow...