Superb Information in the Beginning about Ampere and MM thickness of Rod Please Make Some Tutorials too so that we can Get Technical Knowledge Like this Which helps in Welding Works Thanks Once Again and God Bless You !! Superlike 👍👍
Thanks. Have to repair my trailer this week and that will involve some vertical welding. I don't have much experience as I only got a 1-night a week course some years ago.
Of course 6012 & 6013 can be used vertical up. UP - is the ONLY way to weld vertical. Down is only any good for cosmetics. With the exception of pipeliners of course, and that's an entirely different discussion.
👍 genial mi amigo.me gustaría que hagas videos con soleras o ángulos de espesor finos que es para hacer trabajos de hobbies y es lo cuesta más para uno que está aprendiendo okey.gracias✌️
Just know that this is a "Cover Pass" technique and not meant for the "Root Pass" especially on a fillet. You need to use the Whip N' Pause, Inverted "T", Inverted "V" or Triangle rod manipulation to get any kind of root fusion since E6013 has low penetration characteristics. The "U", "W", or "Z" weaves are fine for uphill covers and stringers work equally well with a circle motion. Any other position requires you to stay on the leading edge of the puddle to keep the slag at bay. Like most stainless steel electrodes, E6013 requires some type of weave motion with a slightly longer arc length to blow the heavy slag back to make the puddle visible. The increased arc force also helps prevent wormholes too. Remember, E6013 is a slow deposition electrode hence you need to spend more time on the toes and go a little slower than E7018 😉
You need to go up to get root penetration and then across as you are doing but with longer pauses at each side to avoid the slight undercut you are getting. If you break that weld, you will find low root penetration with some slag inclusion pockets
I always understood that you should go low on amps when welding vertical up because the heat rises ahead of where you're welding. But 150 is nothing like low on amps. And it still looks really nice!
Im new to welding and have a hard time figuring out the puddle distance ive been told roughly 1/16 or 1/32 of an inch away but thats about it. Is there more to it than that or do you also have to do additional steps to keep your puddle flat. (Mine rise like a mountain and finish like a bb size. ) any criticism or help is appreciated
Di bidang welder(las) yg paling penting skil (keahlian). Izin bertanya bos... Apakah di media yg tipis (0.7 mm,)apakah bisa di terap kaya zig zag nya bos?
Though good elburg for most aplicationd. Tour welde Souls be more flat right and more consultant. When going up i would hold your ro single slightly mor flat and work fromthe wrist more.
Came here to comment section, cause i saw the arc was low. And wantes to see who else thinks the same. That is 10mm steel plate, he is going up with about 90-110 max. 6013 3.2 is burning with big arc already with 125amps...
@@robylv5720 I agree with the amps figures you mention. Welding machines are not consistent when it comes to indicating amp settings. If I ran 3.25's on 150 amps, I would be dealing with some serious edge undercutting. I run 3.25 - 6013 at around 115 amps for vertical up, using a Fronius Transpocket 1500.
Hello👋🙋♂️ there... Amazing and very interesting video Good information and very helpful Do keep posting Warm regards and best👍💯 wishes The UnknownManCub 👍😎👨🏭
От аппарата, зависит тоже многое. На производстве, сжёг тысячи электродов уони 13-55, трансформатор ВДМ 1200, производства 70-х годов прошлого века. Пол тонны ржавого железа и пыли, металл, идеально сваривает тройкой, при 60 А на баластнике Попробуй на любом бытовом инверторе поставить ток 60 ампер, электроды уони, будут тупо залипать. Дома, есть 3 фазы, поэтому ещё лет десять назад купил трехфазный аппарат EWM 300, производства Германии Он, промышленного класса, работает идеально с любыми типами электродов. Но стоит довольно дорого. Все хорошие источники сварочного тока, стоят прилично.
Excelente explicación, mi amigo. Te felicito, has aclarado muchas dudas que yo tenia. Muchas gracias.
Excelente aplicación y resultado, muy bueno para practicar. Felicidades!!! Saludos desde México.
Man those are some nice welds!
Thank you for posting this great tutorial!
Thanks for your teaching ! It really helpful
Superb Information in the Beginning about Ampere and MM thickness of Rod
Please Make Some Tutorials too so that we can Get Technical Knowledge Like this Which helps in Welding Works
Thanks Once Again and God Bless You !!
Superlike 👍👍
You are a excellent professor of welding....Good job🇦🇱
Thanks. Have to repair my trailer this week and that will involve some vertical welding. I don't have much experience as I only got a 1-night a week course some years ago.
Si esto fuera moda, vos hacés alta costura. 👏👏👏👏👏
Incredible. Youre a smart guy. Thank you for sharing your knowledge and may God bless you more.
Excellent best vertical I’ve seen wish I could do the same
Obrigado por compartilhar seu conhecimento parabéns.
Браво чудесен урок!
You're the only welder I haven't judged on UA-cam so far 😂 beautiful work
Thank you for teaching me such wonderful techniques for free
6013s look awesome!
Mais uma vez um belo vídeo 👏👏🇧🇷🇧🇷
Panini n
Muy buen video amigo gracias por tus buenos videos se aprende 👍👍👍👍
Thank you, I didn't think that 6013 could be used for vertical up. I had been using low amperage settings . A big thumbs up.
Of course 6012 & 6013 can be used vertical up. UP - is the ONLY way to weld vertical. Down is only any good for cosmetics. With the exception of pipeliners of course, and that's an entirely different discussion.
@@tandemwings4733 I'm glad you said that. Uphill for 3F position is the norm...and for any vertical. Not really is "secret trick of the trade" lol.
Hi,watching from Romania, nice welding ✌️
You are very good!
Thanks!
Excellent vertical welding bud,excellent !👍🏻
Mate. You are an artist.
We need more videos on this, it is very important for us, wherever we go, a test is taken about this.
👍 genial mi amigo.me gustaría que hagas videos con soleras o ángulos de espesor finos que es para hacer trabajos de hobbies y es lo cuesta más para uno que está aprendiendo okey.gracias✌️
Foarte bine aplicata in practica,meserie🦾🦾
Buenos trucos amigo
Just know that this is a "Cover Pass" technique and not meant for the "Root Pass" especially on a fillet. You need to use the Whip N' Pause, Inverted "T", Inverted "V" or Triangle rod manipulation to get any kind of root fusion since E6013 has low penetration characteristics.
The "U", "W", or "Z" weaves are fine for uphill covers and stringers work equally well with a circle motion. Any other position requires you to stay on the leading edge of the puddle to keep the slag at bay.
Like most stainless steel electrodes, E6013 requires some type of weave motion with a slightly longer arc length to blow the heavy slag back to make the puddle visible. The increased arc force also helps prevent wormholes too. Remember, E6013 is a slow deposition electrode hence you need to spend more time on the toes and go a little slower than E7018 😉
I envy to see those weld seams. I can't do anything like that
Super, l always struggle for verticals, ll do more practice. Excelente!
Nice stick welding!
👍👍👍👍👍🔥🔥🔥🔥🔥
You need to go up to get root penetration and then across as you are doing but with longer pauses at each side to avoid the slight undercut you are getting. If you break that weld, you will find low root penetration with some slag inclusion pockets
Especially with a 6013
100%
And for the roots,I change my polarity (electrode negative)
Iron man : you're the best one!!! Congratulations from Romania!
Awesome work sir 👌
I always understood that you should go low on amps when welding vertical up because the heat rises ahead of where you're welding. But 150 is nothing like low on amps. And it still looks really nice!
Exactly..i think so,usually 120 A for 3.25 mm
Not true. Amps depends on welding stick size and material + thickness and material welding is being performed on
En unos 100 años llegó a ese nivel, que genial soldadura
Pekne video som tiež zvarac bud zdravy pozdrav zo slovenska🇸🇰🇸🇰🇸🇰🇸🇰
Genial Bro. 😸👍, Saludos desde Cusco 🇵🇪🙋🏻♂️
Esse manja e entendi do assunto já fui soldador conheço o bão e u ruim 👍👍nata 10
الله ينور يا باشا
I try vertical up with 6013 low or high amp my weld doesn't look like this. Vertical down look very good
Im new to welding and have a hard time figuring out the puddle distance ive been told roughly 1/16 or 1/32 of an inch away but thats about it. Is there more to it than that or do you also have to do additional steps to keep your puddle flat. (Mine rise like a mountain and finish like a bb size. ) any criticism or help is appreciated
Mình Xin được cảm ơn tác giả.bài chia sẻ rất hay và hữu ích.
Great video, thank you
Thanks you videos tutorial next brother 👏👏👏💯👍
Membantu saya dalam belajar tentang pengelasan vertikal..Terima kasih temanku
Me e quedado sin palabras
Excelente aporte
Thank you for posting this great tutorial!
Great welding job
Muito boa dica ! Show !!
El movimiento ascendente en zig zag es lo de menos, lo mas importante es la potencia, el amperaje seleccionado para que el charco no se caiga.
The vertical T weld was one of my favourite position weld back in the day, this guy has done a good job nice one bro
Hah. I just realised what a "vertical T" weld could be. That would be what we called a "vertical fillet". Does that look right to you?
@@tandemwings4733 yup that's right, over 35 years since I did those sort welding jobs back then
Mối hàn rất đẹp và cũng chắc cảm ơn chia sẻ cách hàn của bạn
جزاك الله خيرا
great video .
(* in europe - milimeter = mm / mililiter = ml )
In Australia - millimetre = mm / millilitre = ml.
Hi very nice and professional 👌
thanks for the knowledge you share 👌👌
Boa noite qual operagen que você usou para fazer essa soda.👍👍😔
Great! Thanks
Sure! Convex bead and uneven bead height will come with this technique
Eu sou a Yola Gosto muito dos vossos videos ,soldo a quase um ano mais tenho muita dificuldade de soldar vertical e 4f gostaria que me ajudacem
Thank you sir, good tips
joss tnan. posisi vertikal hsile koyo lasan bawah tangan👍👍
laying dimes , good, is this DC delder?
What is the amperag(current) for vertical up
Di bidang welder(las) yg paling penting skil (keahlian).
Izin bertanya bos...
Apakah di media yg tipis (0.7 mm,)apakah bisa di terap kaya zig zag nya bos?
Hi to all, regards from Venezuela
this is very important for me, thank my friend
Though good elburg for most aplicationd. Tour welde Souls be more flat right and more consultant. When going up i would hold your ro single slightly mor flat and work fromthe wrist more.
Merci beaucoup.
Is weaving bad for penetration?
Vertical acendente dá maior penetração, ótima para soldar chassi e estruturas que exigem maior responsabilidade.
thanks for sharing👌
Espectacular 💪💪
that low penetration cant be 150A. Personaly i think you have used like 110A, or 100 for this welding.
Came here to comment section, cause i saw the arc was low. And wantes to see who else thinks the same.
That is 10mm steel plate, he is going up with about 90-110 max.
6013 3.2 is burning with big arc already with 125amps...
@@robylv5720 I agree with the amps figures you mention. Welding machines are not consistent when it comes to indicating amp settings. If I ran 3.25's on 150 amps, I would be dealing with some serious edge undercutting. I run 3.25 - 6013 at around 115 amps for vertical up, using a Fronius Transpocket 1500.
Qual a inversoura que vc está usando
I like this video.
thanks
Nicely 😊☺️❤️
It's easy to weld thick metals. I would appreciate if you do the same job on thin metal...
Thin metal with 6013 would be best done running the bead down in a straight pass, rather than upward with a weave pass.
Super super robota 👍👍👍
Kullandığın elektrot bazikmi yoksa rutilmi ?
I use Vodex rods They have been available since my apprenticeship 1961 to 1967 ? 60 years ago where did the time go?
เยี่ยมเลยคับๆๆๆๆๆๆ
ща прохожу практику на заводе, мастер говорит что лучше него заебашил. Красава чел, спасибо!
Nice 👍
Assalamualaikum brother
Metal thickness, Electrode and Amp please?
en esta posicion deberias bajar la fuerza 20 %
Verynice welding works
Монстр!! Супербизон!!!
Im sorri sir,homany voltase for capping 3g smaw ??
Hello👋🙋♂️ there...
Amazing and very interesting video
Good information and very helpful
Do keep posting
Warm regards and best👍💯 wishes
The UnknownManCub 👍😎👨🏭
What brand of your welding machine
Your pretty good young brother
แล้วแนวตั้ง7016เป็นอย่างไรครับ
How do i stop the weld pool droping
GOOG job👍
how many volt amperes for vertical welding?
Класс забор будет супер неужели только токе сварщики остались
такэ.. и других "учат"..
Years back 6013 was called the electrician rod. Because it was so easy an electrician could do it.
That's really dumb.
@@tandemwings4733 apparently you are too.
@@plainlogic What makes you think that?
@@plainlogic Actually, I'm a qualified welder, and the easiest electrode/s I have ever used are 6010/6011.
6013 is not an easy rod to weld my freind. Especialy vertical or horizontal. Not even on flat surface.
Nice my friends 👍👍👍, terimakasih atas tutorial nya 🙏,salam satu las👍👍👍
+62 hadiiir🖐🖐
Siapppp☕👈🤝
Отлично сделано👍! Я думаю многое зависит от сварочного аппарата. Подскажите как выбрать сварочный аппарат в магазине?
От аппарата, зависит тоже многое.
На производстве, сжёг тысячи электродов уони 13-55, трансформатор ВДМ 1200, производства 70-х годов прошлого века.
Пол тонны ржавого железа и пыли, металл, идеально сваривает тройкой, при 60 А на баластнике
Попробуй на любом бытовом инверторе поставить ток 60 ампер, электроды уони, будут тупо залипать.
Дома, есть 3 фазы, поэтому ещё лет десять назад купил трехфазный аппарат EWM 300, производства Германии
Он, промышленного класса, работает идеально с любыми типами электродов.
Но стоит довольно дорого.
Все хорошие источники сварочного тока, стоят прилично.
Rwanda ❤ good technician