Hello, epoxy resins are sold as two components. A- Resin, B- Hardener. The mixing ratio should be done as stated on the package or in the manufacturer's instructions. The mixture is usually mixed in a 2:1 ratio, although some manufacturers may specify different mixing ratios (such as 2:1, 3:1 or 4:1) and should be made in the ratio specified by the manufacturer. You should prepare the mixture using a precision scale. Resins have types according to their area of use. Thin casting resins should be used for projects that are not thin or thick, and deep pour resins should be used for thicker and larger projects. If you have no experience in epoxy, I do not recommend that you start with such large works. You can start with necklaces and similar works with thin casting resins, and as you improve yourself, you can move on to deep pour resins and do larger works.
Thanks, yes that was very thick. This was my first wall clock project. That's why I couldn't adjust the thickness correctly. I did not thin it to avoid wasting material. I add my works to my etsy page. You can check the price from there.
Foi utilizada tinta epóxi em pó perolado. Você pode obter esses tipos de tintas de diferentes marcas e a preços mais acessíveis no país onde mora. Estou compartilhando um link de exemplo. resininresin.com/product/tone-powder/?v=ebe021079e5a
Yüzeydeki tozu pisliği silmek için su sıktım. Islanan bölge anlık parlar kuruduktan sonra tekrar matlaşır. Gerçek yarı parlaklığı ahşap koruyucu vermektedir. Tam parlaklık istenirse 3000 lik zımparaya kadar gidilir ve polisaj işlemi uygulanır veya 320 lik zımparaya kadar zımparalandıktan sonra yüzeye ince bir epoksi uygulanarak yüzeyin komple parlak olması sağlanabilir.
10 місяців тому
Yine harika bir çalışma olmuş. İçine keşke ufaktan da olsa led lamba eklenseymiş daha farklı olabilirmiş. Elinize emeğinize sağlık.
Sabit bir yerden almıyorum, google dan arama yaparak ulaşıyorum çoğunlukta. Arayıpta bulamadığınız birşey varsa ilgili videoda yorum yaparak sorunuz, ona göre yardımcı olmaya çalışırım.
Normal değil, eğer uygun ortam sıcaklığında yeterli süre beklemenize rağmen sertleşmeyip yapış yapış kalıyorsa karışımı iyi karıştırmamanızdan kaynaklanır. Karışımı homojen bir görünüm elde edene kadar hatta bir süre daha karştırmaya devam ederek çok iyi bir şekilde karıştığından emin olunuz. Bu güne kadar böyle bir problemle hiç karşılaşmadım. Birde hangi epoksiyi kullandınız, toplam kaç gram karışım hazırladınız ve reçine ne kadar sertleştirici ne kadar kullandınız.
@@atasoy mass pro toplam 500gram epoksi kullandım ama sitedeki hesabı anlayamadığım için 500gram için /2.5 yapıp 300 epoksi 200 aktivatör yaptım sanırım
Karışım oranınız hatalı bu yüzden bu sorunu yaşıyorsunuz. Ayrıca karışımı çok iyi karıştırdığınızdan emin olunuz. Hesaplama için sitedeki bu aracı kullanınız. epoksimarket.com/karisim-orani-hesaplama
Hocam mrblsr epoksiyi ölçüsünü ona göre koyuyoruz fakat bir türlü şu ahşap görüntüyü tam yakalamıyoruz ya 😮 baya bir canlı gözğkmesi için zımparamı yapmamız gerekiyor
Ahşaba ahşap koruyucu uyguluyormusunuz, canlı gözükmesi için en son ahşap koruyucu uyguluyorum. Epoksiyi 800 zımparaya kadar zımparaladım ahşap ta aynı şekilde.
Merhabalar, Epoksi karşımında pigment oranı ne kadar olmalı ? Bir diğer sorumda dakika 4:06-4:11 de verdiğiniz deseni bende yapıyorum fakat pigment bir süre sonra dibe çöküyor gibi oluyor desen kalmıyor bozuluyor nerede yanlış yapıyorum. Döküm yaptiktan ne kadar süre sonra desen veriyorsunuz acaba ? Teşekkürler (kullandığım epoksi epoksimarket mass pro )
Pigment kullanım oranı %1 - %2.5 civarlarında tavsiye edilir, ben göz karırı ekledim. Desen verme işi için epoksinin biraz jelleşmesini beklemelisiniz. Jelleşmeden verilen desen bir süre sonra dağılır. Bende mass pro kullanıyorum ama bunun için bir süre vermek doğru olmaz, epoksi konusunda tecrübe kazandığınızda bunu daha iyi anlayacaksınız. Kullanılan epoksi miktarı + döküm kalınlığı + ortam sıcaklığı bu süreyi değiştirecektir. Doğru jelleşme süresini zamanla tecrübe edinerek kazanacaksınız.
@@atasoy boya markası olarak ne kullanıyorsun hocam eleyerek gidelim belki buluruz, ben vallejo kullandım açık renklerde sorun çıkarttı ama hazır diorama da kullanılan yosun da boya bıraktı, rich mastermix akrilik boya tavsiye edildi epokside kullanmış hiç sorun yaşamamış. Mavi - siyah - gümüşte- kahverengi sağlam . Vallejo Yeşil - sarı- kremde çözülme oluyor
vallejo, artdeco, nova denedim. Daha çok problemler derin dökümlerde ortaya çıkıyor. Artdeco (siyah, mavi, beyaz) ile ağaç boyuyorum ama epoksiden hiç etkilenmiyor. Vallejo epoksiden çok çabuk etkileniyor. Diaroma da kullanılan yosunlar boyandığı için renk salıyor ana dökümden önce reçine ile kaplamalı kuruduktan sonra ana döküm yapılmalı.
Atasoy hocam bu zımpara izlerinin oluş sebebi nedir ? 13:00 -17:00 arası zımpara ile uğraştım 80-3000 arası 600 ile sulu zımparaya başladım polisaj yapacaktım ama bir baktım her tarafta dairesel zincir izleri oluşmuş. Standart 125mm delikli zımpara kullanmadım elek zımpara kullanıyorum ve çıkartıp takarken mutlaka hava püskürtüp temiz kalmasına dikkat ediyorum. Erbauer Eksantrik Zımpara makinası ile zımpara yapıyorum
Bunun olması normal bunu bende yaşıyorum. Pasta cila uygulandığında bir çoğu gidecektir. Zımpara geçişlerine dikkat edin, bir önceki zımparanın izleri kalmamalı. Kalın pasta işleminde kademeli bir şekilde devir arttırarak yüksek devirde uygulandığında bu izler yok olacaktır.
Hocam çok iyi güzel yapıyorsunuz severekte takip ediyorum lakin, ben bu epoksi dökümünde karışımı yaptıktan sonra köpürmenin önüne geçemiyorum, yavaşta karıştırıyorum ama olmuyor bunun bir püf noktası varmı teşekkürler
Teşekkürler beğendiğinize sevindim. Karışım sonrası sertleşme sırasında köpürüyorsa bunları bilmem lazım. Döküm yaptığınız reçine ince döküm mü kalın döküm mü? Ne kadar reçine hazırlıyorsun ve kalıbınızın derinlik ölçüsü nedir ? Karışım sırasında köpürüyorsa Epoksi bu soğuk havalarda biraz yoğunlaşır ve karıştırma sırasında da bolca baloncuk oluşumuna sebep olur, karışım yapmadan önce epoksiyi biraz sıcak suda bekletip öyle karışım hazırlarsanız epoksi daha akışkan olacaktır ve daha az baloncuk yapacaktır. Karışım sonrası az daha sıcak suda bekleterek karışım sırasında oluşan kabarcıkların da bir kısmının hızlı bir şekilde yukarı çıkmasını sağlayabilirsiniz. Not:Aşırı sıcak suda ve uzun süreler bekletmeyin, epoksi sıcaklıktan dolayı hızlı tepkimeye girebilir ve hızlı sertleşme, kabarcık veya sararma gibi problemlere yol açabilir.
Ben yarı parlak bir görünüm elde etmek için 800 lük zımparaya kadar zımparaladım. Ardından çift komponentli ahşap koruyucu uyguladım. Ahşap koruyucu epoksiye soft bir parlaklık veriyor. Videoda da kullandığım zımparaları gösteriyorum ama o kısmı atladınız sanırım. Sırası ile 80, 120, 240, 320, 400, 600 ve 800 zımparaları kullandım.
Bu saat ilk denemem oldukça kalın oldu, malzeme çöp olmasın diye bilerek kalın bıraktım. İdeal saat kalınlığı tam olarak nedir bilmiyorum ama 2 - 2.5 cm gayet estetik duracaktır.
@@atasoy saat kadraninin 5,5*5,5 ebatlarında ve 1,5cm derinlikte olduğunu düşünürsek ve 1cm civarı da akrep ve yelkovanı taktıgımız vidalı kısımla birlikte aslında toplamda 2,5cm hatta 3cm bile olabilir ideal gözüküyor. Bilgilendirme için teşekkür ederim.saygilarimla
When you made the hole for the clock with the router in auto and moving it by the base with just 4 fingers... man... isn´t that extremely dangerous.... safety first!! Other than that, astonishing job.
Bu arada çok güzel çalışmalarınz sizin sayenizde hazırlayacağım alt kısımları mdf üzerine bant kenarlara silikon kesinlikle akıtmıyor ozaman doprumu? İyi çalışmalar
Alt kısmı mdf veya başka birşey kullanılabilir, çıplak mdf den bant kolay söküldüğü için çıplak mdf kullanıyorum. Bant kullanmamızın sebebi ise epoksi bant yüzeyinden kolay ayrıldığı için bant kullanıyorum. İyi bir şekilde de silikon uygularsanız akıtma yapmayacaktır. Eğer epoksi ile tecrübeniz yok ise bu kadar kalın ve büyük çalışma denemeyin. Hatta ince döküm epoksi ile ufak kolye ve benzeri çalışmalar ile başlangıç yapmanızı, epoksi konusunda tecrübe kazandıkça kalın döküm epoksilere geçiş yaparak çalışmalarınızı adım adım büyütmenizi tavsiye ederim.
Hocam merhaba ben evde kolye vesaire şeylerle uğraşmak istiyorum vonroc ve ferm CMT gravür makinası almak istiyorum bütçeme uugun olarak sizce hangisi iyi olur ? Bunun yanında rknolarak nelere ihtiyacımız olabilir bilgilendirebilir misiniz rica etsem ... yaptığınız eserler çok guzel muhteşem emeğinize sağlık.
Bütçenize hangisi uyuyorsan onu tercih ediniz. Gravür daha kolay kullanabilmek adına yanında uzatma esnek mil olan bir model veya extra olarak almanızı tavsiye ederim. Gravür hangi amaçlarda kullanacaksanız o işe uygun uçları da temin etmelisiniz. Kolye yapımında köşelerin yuvarlatmak ve kaba şekli vermek için zımpara ucu, kolye deliği açmak için uç, bu uç ihtiyacı modele göre daha da genişletilebilir. Siz bir başlangıç yapın ihtiyacınıza uygun ekipmanları buna göre temin edersiniz. Hazır setler içinde birçok şey var ama çoğu gereksiz yada çok nadir kullanılıyor.
Eğer bu işi sever ve sabırlı olursanız çok iyi işler çıkarabilirsiniz. Takıldığınız yerlerde yazarsanız elimden geldiğince yardımcı olmaya çalışacağım. Çalışmalarınızda başarılar ve kolaylıklar dilerim.
@@atasoy teşekkür ederim , bana ilk başta epoksi olarak nasıl bir tercih yapmam gerek , dikkat etmem gereken önemli hususlarda akıl verirseniz sevinirim .... Güvenlik personeli olarak çalışıyorum zamanım müsait gece nöbetlerine videolarınızı izleyerek sabah ediyorum:))
Kolye için İnce döküm epoksi kullanmalısın, ben epoksimarket.com Resinin slim veya slim extra kullanıyorum. Tavsiye ederim. Epoksi soğuk havalarda beklediğinde kristalleşme yapar bunu normal hale getirmek için reçineyi 70-75C° sıcak suda 15-20 dk. kadar bekletmelisin. Eğer kristalleşme yapmış reçineyi direkt kullanırsan ne kadar karıştırırsan karıştır hep buğulu bir görünüm olacaktır. İlk satın almada bu işlemi uygulayıp oda sıcaklığında bekletirsen bir dahaki sefere tekrar uygulaman gerekmez. Birde soğuk havalarda epoksi biraz yoğunlaşır daha akışkan bir hal alması için az sıcak bir suda bekletebilirsin. Bu sana karıştırma sırasında daha az hava kabarcığı oluşmasını sağlayacaktır. (Not: sıcak suda bekletme işlemini için şişenin ağzı sıkı bir şekilde kapalı olduğundan emin olmalısın kesinlikle reçineye su temas etmemeli) Karıştırma sırasında çok yavaş bir şekilde homojen bir görünüm elde edene kadar yavaşça karıştır. Aklıma çok fazla şey gelmiyor gelenleride burada yazmak çok uzun sürecek. Siz bir başlangıç yapın aklınıza gelen soruları soru cevap şeklinde sorarak ilerleriz. Elimden geldiği kadar yardımcı olmaya tecrübelerimi paylaşmaya çalışırım.
Yes, you are right, I tried a watch for the first time, I did not thin it so that the material would not be trash. I will be making my future watch projects thinner.
Kardeşim, öncelikle yaptığın duvar saati çok kalın.Keşke zeytin ağacını epoksiden önce biraz inceltseydin.Bir diğer hususta şu ingilizce açıklama kısmı.Kardeşim,ürünlerini yurtdışına satıyor olabilirsin.Ama bizim Türk 'ün ne günahı var?Açıklamaları Türkçe de yazki bu işi bilmeyenler neyi neden yaptığını öğrensin.
İlk saat denemem biraz kalın oldu, harcadığım malzeme çöp olmasın diye kalın bıraktım. Açıklama ve altyazılar Türkçe de bulunmakta, cihazınızın dil ayarları ile ilgili bir problem olabilir, altyazı dil seçeneğinden Türkçeyi seçmeniz yeterli. Biz Türklerin günahı yok ne yapıyorsak kendi kendimize yapıyoruz, herşeyi hazır önümüze istiyoruz.
Pela primeira que vejo um vídeo onde, sem uma palavra, me mostrou como posso fazer qualquer coisa com resina. Claro que sera dentro de minhas limitações. Pois seu maquinário e absurdamente rico. Obrigada ❤
Its just gorgeous. I love it. You did great as always.
Thank you very much, I'm glad you liked it. Also thank you for your continued support.
Какая кропотливая работа, но результат превосходный. Спасибо мастер, лайкаю.
Спасибо, я рад, что вам понравилось.
Bonne année à tous. Elle est très jolie cette horloge. J'apprécie beaucoup le bois et surtout l'olivier. A bientôt pour d'autres projets.
Bonne année à toi aussi, je suis contente que mon travail te plaise. J'espère vous voir dans le prochain projet.
Thank you for sharing the process. It’s a beautiful clock
Thanks, I'm glad you liked it. 👍👍
Absolutely Stunning
Thank you, I'm glad you liked it.
Bellissimo, l'amore per la resina ci accomuna 😂👍
Grazie, sono felice che ti sia piaciuto. Lavorare con la resina è difficile ma divertente e piacevole.
Güzel çalışma, ellerine sağlık Ustam👍👏
Teşekkürler, dostum, seninde çalışmalarını bekliyorum. 👍👍
@@atasoy yakın zamanda gelecek bir sıkıntı olmazsa 👍
@bahtiyar-craft 👍👍👍
Amazing job as always!!!
Thank you very much, I'm glad you liked it.🙏👍👍😊
Bravo , come sempre , complimenti .
Grazie mille, sono felice che ti sia piaciuto. Grazie anche per il vostro supporto.
Ive definitely got buy my self a vacuum pump n chamber pot i know that as im done with micro bubbles in my pieces 👌👍
If you use a vacuum machine, you will get rid of most of the bubbles.
Beautiful art work.
Thank you, I'm glad you liked it.
I wish i have materials like you😂 great work bro thanks for sharing it with us
Thank you very much, I'm glad you liked it.
By starting with small necklaces like me, you can progress by expanding your equipment over time.
That's amazing 👏👏👏👏👏👏
Thanks, I'm glad you liked it. 👍
Hi , this clock is beautifull and I would like to try. Can you please tel me how to make the thinning epoxy resin.
Hello, epoxy resins are sold as two components.
A- Resin, B- Hardener.
The mixing ratio should be done as stated on the package or in the manufacturer's instructions.
The mixture is usually mixed in a 2:1 ratio, although some manufacturers may specify different mixing ratios (such as 2:1, 3:1 or 4:1) and should be made in the ratio specified by the manufacturer.
You should prepare the mixture using a precision scale.
Resins have types according to their area of use.
Thin casting resins should be used for projects that are not thin or thick, and deep pour resins should be used for thicker and larger projects.
If you have no experience in epoxy, I do not recommend that you start with such large works.
You can start with necklaces and similar works with thin casting resins, and as you improve yourself, you can move on to deep pour resins and do larger works.
Ellerine sağlık üstad
Eyvallah başkan 👍
Très jolie réalisation !
Merci, je suis content que ça vous plaise.👍👍
Amazing❤
Thanks ❤
Beautiful beautiful beautiful. Very thick so I imagine a lot of product went into this project. How much do you sell it for?
Thanks, yes that was very thick.
This was my first wall clock project.
That's why I couldn't adjust the thickness correctly.
I did not thin it to avoid wasting material.
I add my works to my etsy page.
You can check the price from there.
Would you think of doing this same clock but, with mirror polished aluminum pins instead of black resin?
Yes, I may do something like this in the future.
Hello. I'm watching your video. all is cool. please tell me what and how do you wash containers after epoxy resin?
You can clean it with cellulosic thinner or isopropyl alcohol.
Amazing as always. Just checking what is the thickness and did you pour the epoxy with single pour? How many kg was that. Thanks
The thickness I poured is approximately 4.5-5 cm.
I used 1.5 kg of epoxy and poured it in one go.
Show! Que tipo de corante vc colocou?
Foi utilizada tinta epóxi em pó perolado.
Você pode obter esses tipos de tintas de diferentes marcas e a preços mais acessíveis no país onde mora.
Estou compartilhando um link de exemplo.
resininresin.com/product/tone-powder/?v=ebe021079e5a
Elinize emeğinize sağlık. Zımpara bittikten sonra fıstıs ile ne sıktınız parladı sonrada ahşap verniği kullandınız
Yüzeydeki tozu pisliği silmek için su sıktım. Islanan bölge anlık parlar kuruduktan sonra tekrar matlaşır. Gerçek yarı parlaklığı ahşap koruyucu vermektedir. Tam parlaklık istenirse 3000 lik zımparaya kadar gidilir ve polisaj işlemi uygulanır veya 320 lik zımparaya kadar zımparalandıktan sonra yüzeye ince bir epoksi uygulanarak yüzeyin komple parlak olması sağlanabilir.
Yine harika bir çalışma olmuş. İçine keşke ufaktan da olsa led lamba eklenseymiş daha farklı olabilirmiş. Elinize emeğinize sağlık.
Teşekkürler beğendiğinize sevindim.
@@atasoy Rica ederim. Yoruma cevap verdiğiniz için bende size teşekkür ederim.
Parabéns meu amigo trabalho de luxo
Estou querendo trabalhar com rezina e
Difícil
Obrigado, que bom que você gostou.👍
Hocam kusura bakmayın çok sordum :) kurutulmuş çiçekleri ve elektrik devrelerini nerden alıyorsunuz link atma şansınız var mı
Sabit bir yerden almıyorum, google dan arama yaparak ulaşıyorum çoğunlukta.
Arayıpta bulamadığınız birşey varsa ilgili videoda yorum yaparak sorunuz, ona göre yardımcı olmaya çalışırım.
Ustam bu tarz ağaçları nerden temin ediyosunuz
instagram.com/zeytinhammade
www.n11.com/magaza/asiawoods
Atasoy hocam elinize sağlık, bu epoksi de yüzeyin bant gibi parmağımızı değdirdiğimizde yapışma hissi normal mi
Normal değil, eğer uygun ortam sıcaklığında yeterli süre beklemenize rağmen sertleşmeyip yapış yapış kalıyorsa karışımı iyi karıştırmamanızdan kaynaklanır. Karışımı homojen bir görünüm elde edene kadar hatta bir süre daha karştırmaya devam ederek çok iyi bir şekilde karıştığından emin olunuz. Bu güne kadar böyle bir problemle hiç karşılaşmadım.
Birde hangi epoksiyi kullandınız, toplam kaç gram karışım hazırladınız ve reçine ne kadar sertleştirici ne kadar kullandınız.
@@atasoy mass pro toplam 500gram epoksi kullandım ama sitedeki hesabı anlayamadığım için 500gram için /2.5 yapıp 300 epoksi 200 aktivatör yaptım sanırım
Karışım oranınız hatalı bu yüzden bu sorunu yaşıyorsunuz.
Ayrıca karışımı çok iyi karıştırdığınızdan emin olunuz.
Hesaplama için sitedeki bu aracı kullanınız.
epoksimarket.com/karisim-orani-hesaplama
Hocam mrblsr epoksiyi ölçüsünü ona göre koyuyoruz fakat bir türlü şu ahşap görüntüyü tam yakalamıyoruz ya 😮 baya bir canlı gözğkmesi için zımparamı yapmamız gerekiyor
Ahşaba ahşap koruyucu uyguluyormusunuz, canlı gözükmesi için en son ahşap koruyucu uyguluyorum.
Epoksiyi 800 zımparaya kadar zımparaladım ahşap ta aynı şekilde.
Merhabalar,
Epoksi karşımında pigment oranı ne kadar olmalı ? Bir diğer sorumda dakika 4:06-4:11 de verdiğiniz deseni bende yapıyorum fakat pigment bir süre sonra dibe çöküyor gibi oluyor desen kalmıyor bozuluyor nerede yanlış yapıyorum. Döküm yaptiktan ne kadar süre sonra desen veriyorsunuz acaba ? Teşekkürler (kullandığım epoksi epoksimarket mass pro )
Pigment kullanım oranı %1 - %2.5 civarlarında tavsiye edilir, ben göz karırı ekledim.
Desen verme işi için epoksinin biraz jelleşmesini beklemelisiniz. Jelleşmeden verilen desen bir süre sonra dağılır.
Bende mass pro kullanıyorum ama bunun için bir süre vermek doğru olmaz, epoksi konusunda tecrübe kazandığınızda bunu daha iyi anlayacaksınız.
Kullanılan epoksi miktarı + döküm kalınlığı + ortam sıcaklığı bu süreyi değiştirecektir.
Doğru jelleşme süresini zamanla tecrübe edinerek kazanacaksınız.
Atasoy Hocam akrilik boyanın dağılma sorununa bir çözüm bulabildiniz mi ?
Pratik ve kalıcı bir çözüm bulamadım.
Şimdilik boyanın üzerine iki kat ince reçine uyguluyorum. Sertleştikten sonra ana dökümü yapıyorum.
@@atasoy boya markası olarak ne kullanıyorsun hocam eleyerek gidelim belki buluruz, ben vallejo kullandım açık renklerde sorun çıkarttı ama hazır diorama da kullanılan yosun da boya bıraktı, rich mastermix akrilik boya tavsiye edildi epokside kullanmış hiç sorun yaşamamış. Mavi - siyah - gümüşte- kahverengi sağlam . Vallejo Yeşil - sarı- kremde çözülme oluyor
vallejo, artdeco, nova denedim.
Daha çok problemler derin dökümlerde ortaya çıkıyor.
Artdeco (siyah, mavi, beyaz) ile ağaç boyuyorum ama epoksiden hiç etkilenmiyor.
Vallejo epoksiden çok çabuk etkileniyor.
Diaroma da kullanılan yosunlar boyandığı için renk salıyor ana dökümden önce reçine ile kaplamalı kuruduktan sonra ana döküm yapılmalı.
Atasoy hocam bu zımpara izlerinin oluş sebebi nedir ?
13:00 -17:00 arası zımpara ile uğraştım 80-3000 arası 600 ile sulu zımparaya başladım polisaj yapacaktım ama bir baktım her tarafta dairesel zincir izleri oluşmuş. Standart 125mm delikli zımpara kullanmadım elek zımpara kullanıyorum ve çıkartıp takarken mutlaka hava püskürtüp temiz kalmasına dikkat ediyorum. Erbauer Eksantrik Zımpara makinası ile zımpara yapıyorum
Bunun olması normal bunu bende yaşıyorum. Pasta cila uygulandığında bir çoğu gidecektir. Zımpara geçişlerine dikkat edin, bir önceki zımparanın izleri kalmamalı.
Kalın pasta işleminde kademeli bir şekilde devir arttırarak yüksek devirde uygulandığında bu izler yok olacaktır.
Renklendirme için gıda boyası kullanılır mı
Hiç denemedim, gıda boyası zamanla uv ışınlarından dolayı rengini kaybedebilir.
Hocam çok iyi güzel yapıyorsunuz severekte takip ediyorum lakin, ben bu epoksi dökümünde karışımı yaptıktan sonra köpürmenin önüne geçemiyorum, yavaşta karıştırıyorum ama olmuyor bunun bir püf noktası varmı teşekkürler
Teşekkürler beğendiğinize sevindim.
Karışım sonrası sertleşme sırasında köpürüyorsa bunları bilmem lazım.
Döküm yaptığınız reçine ince döküm mü kalın döküm mü?
Ne kadar reçine hazırlıyorsun ve kalıbınızın derinlik ölçüsü nedir ?
Karışım sırasında köpürüyorsa
Epoksi bu soğuk havalarda biraz yoğunlaşır ve karıştırma sırasında da bolca baloncuk oluşumuna sebep olur, karışım yapmadan önce epoksiyi biraz sıcak suda bekletip öyle karışım hazırlarsanız epoksi daha akışkan olacaktır ve daha az baloncuk yapacaktır. Karışım sonrası az daha sıcak suda bekleterek karışım sırasında oluşan kabarcıkların da bir kısmının hızlı bir şekilde yukarı çıkmasını sağlayabilirsiniz.
Not:Aşırı sıcak suda ve uzun süreler bekletmeyin, epoksi sıcaklıktan dolayı hızlı tepkimeye girebilir ve hızlı sertleşme, kabarcık veya sararma gibi problemlere yol açabilir.
Merhabalar bende şuan bir tane yapmaya çalışıyorum kaç tane zımpara kullanmam lazım ve hangi zımparalari almam lazım teşekkürler
Ben yarı parlak bir görünüm elde etmek için 800 lük zımparaya kadar zımparaladım. Ardından çift komponentli ahşap koruyucu uyguladım. Ahşap koruyucu epoksiye soft bir parlaklık veriyor.
Videoda da kullandığım zımparaları gösteriyorum ama o kısmı atladınız sanırım. Sırası ile 80, 120, 240, 320, 400, 600 ve 800 zımparaları kullandım.
İdeal saat kalinligi icin icine yerleştirilen ahşabın kalinlığı ne olmalıdır hocam
Bu saat ilk denemem oldukça kalın oldu, malzeme çöp olmasın diye bilerek kalın bıraktım.
İdeal saat kalınlığı tam olarak nedir bilmiyorum ama 2 - 2.5 cm gayet estetik duracaktır.
@@atasoy saat kadraninin 5,5*5,5 ebatlarında ve 1,5cm derinlikte olduğunu düşünürsek ve 1cm civarı da akrep ve yelkovanı taktıgımız vidalı kısımla birlikte aslında toplamda 2,5cm hatta 3cm bile olabilir ideal gözüküyor. Bilgilendirme için teşekkür ederim.saygilarimla
Rica ederim kolay gelsin.
Vidalı kısımlar boyut boyuttur satın alırken buna dikkat ediniz.
When you made the hole for the clock with the router in auto and moving it by the base with just 4 fingers... man... isn´t that extremely dangerous.... safety first!! Other than that, astonishing job.
Üstad ince döküm ile kalın döküm reçine nedir ? Aralarında yapı olarak fark var mı
İnce döküm reçineler ile 1 cm kalınlıkta döküm yapılabiliyorken kalın döküm ile 5-7 cm kalınlıkta dökümler yapılabiliyor.
@@atasoy anladım hocam. Teşekkür ederim
Rica ederim.
👍👍👍💪💪
🙏👍👍👍
Diğer el frezeleri ile açılıyormu kare ? Küçük olan modelle
Sorunuzu anlayamadım biraz daha net bir şekilde yazarmısınız.
@@atasoy diğer ufak kenar el frezeleri ile de saatin arkası için kare veya başka bir şey için kare açılıyor mu yoksa kullandığınz freze mi gerekli
Bu arada çok güzel çalışmalarınz sizin sayenizde hazırlayacağım alt kısımları mdf üzerine bant kenarlara silikon kesinlikle akıtmıyor ozaman doprumu? İyi çalışmalar
Tüm frezeler ile açılabilir.
Alt kısmı mdf veya başka birşey kullanılabilir, çıplak mdf den bant kolay söküldüğü için çıplak mdf kullanıyorum.
Bant kullanmamızın sebebi ise epoksi bant yüzeyinden kolay ayrıldığı için bant kullanıyorum.
İyi bir şekilde de silikon uygularsanız akıtma yapmayacaktır.
Eğer epoksi ile tecrübeniz yok ise bu kadar kalın ve büyük çalışma denemeyin. Hatta ince döküm epoksi ile ufak kolye ve benzeri çalışmalar ile başlangıç yapmanızı, epoksi konusunda tecrübe kazandıkça kalın döküm epoksilere geçiş yaparak çalışmalarınızı adım adım büyütmenizi tavsiye ederim.
🎉
Hocam merhaba ben evde kolye vesaire şeylerle uğraşmak istiyorum vonroc ve ferm CMT gravür makinası almak istiyorum bütçeme uugun olarak sizce hangisi iyi olur ? Bunun yanında rknolarak nelere ihtiyacımız olabilir bilgilendirebilir misiniz rica etsem ... yaptığınız eserler çok guzel muhteşem emeğinize sağlık.
Bütçenize hangisi uyuyorsan onu tercih ediniz.
Gravür daha kolay kullanabilmek adına yanında uzatma esnek mil olan bir model veya extra olarak almanızı tavsiye ederim.
Gravür hangi amaçlarda kullanacaksanız o işe uygun uçları da temin etmelisiniz.
Kolye yapımında köşelerin yuvarlatmak ve kaba şekli vermek için zımpara ucu, kolye deliği açmak için uç, bu uç ihtiyacı modele göre daha da genişletilebilir.
Siz bir başlangıç yapın ihtiyacınıza uygun ekipmanları buna göre temin edersiniz.
Hazır setler içinde birçok şey var ama çoğu gereksiz yada çok nadir kullanılıyor.
@@atasoy teşekkür ederim cevabınız için ... Sizi taklit etmeye çalışıp öğrenecğim inşalalh
Eğer bu işi sever ve sabırlı olursanız çok iyi işler çıkarabilirsiniz. Takıldığınız yerlerde yazarsanız elimden geldiğince yardımcı olmaya çalışacağım.
Çalışmalarınızda başarılar ve kolaylıklar dilerim.
@@atasoy teşekkür ederim , bana ilk başta epoksi olarak nasıl bir tercih yapmam gerek , dikkat etmem gereken önemli hususlarda akıl verirseniz sevinirim .... Güvenlik personeli olarak çalışıyorum zamanım müsait gece nöbetlerine videolarınızı izleyerek sabah ediyorum:))
Kolye için İnce döküm epoksi kullanmalısın, ben epoksimarket.com Resinin slim veya slim extra kullanıyorum. Tavsiye ederim.
Epoksi soğuk havalarda beklediğinde kristalleşme yapar bunu normal hale getirmek için reçineyi 70-75C° sıcak suda 15-20 dk. kadar bekletmelisin. Eğer kristalleşme yapmış reçineyi direkt kullanırsan ne kadar karıştırırsan karıştır hep buğulu bir görünüm olacaktır. İlk satın almada bu işlemi uygulayıp oda sıcaklığında bekletirsen bir dahaki sefere tekrar uygulaman gerekmez.
Birde soğuk havalarda epoksi biraz yoğunlaşır daha akışkan bir hal alması için az sıcak bir suda bekletebilirsin. Bu sana karıştırma sırasında daha az hava kabarcığı oluşmasını sağlayacaktır.
(Not: sıcak suda bekletme işlemini için şişenin ağzı sıkı bir şekilde kapalı olduğundan emin olmalısın kesinlikle reçineye su temas etmemeli)
Karıştırma sırasında çok yavaş bir şekilde homojen bir görünüm elde edene kadar yavaşça karıştır.
Aklıma çok fazla şey gelmiyor gelenleride burada yazmak çok uzun sürecek.
Siz bir başlangıç yapın aklınıza gelen soruları soru cevap şeklinde sorarak ilerleriz. Elimden geldiği kadar yardımcı olmaya tecrübelerimi paylaşmaya çalışırım.
Класс!!!
Спасибо, я рад, что вам понравилось.👍
Show 🎉🎉🎉
❤️❤️
Berberdeki çocuğum ben saygılar hocam:)💖🤡
Biliyorum kardeşim saygılar 😉
Abi bana da öğretirmisin yapmayı
Merhaba epoksi markası nedir
epoksimarket.com ürünlerini kullanıyorum.
Bu projede Resinin Mass Pro kullanıldı.
but resin epoxy are dangerous for the lungs is not?
Protective equipment should be used during mixing, there is no harm after the epoxy hardens.
He knows what he is doing. He's done this for a long time now.
👍👍😉
Be very careful when sanding it as well.
A mask should be used, and if possible, a dust absorber unit should be used.
very nice but too thick, no need to make it so thick
Yes, you are right, I tried a watch for the first time, I did not thin it so that the material would not be trash.
I will be making my future watch projects thinner.
Kardeşim, öncelikle yaptığın duvar saati çok kalın.Keşke zeytin ağacını epoksiden önce biraz inceltseydin.Bir diğer hususta şu ingilizce açıklama kısmı.Kardeşim,ürünlerini yurtdışına satıyor olabilirsin.Ama bizim Türk 'ün ne günahı var?Açıklamaları Türkçe de yazki bu işi bilmeyenler neyi neden yaptığını öğrensin.
İlk saat denemem biraz kalın oldu, harcadığım malzeme çöp olmasın diye kalın bıraktım.
Açıklama ve altyazılar Türkçe de bulunmakta, cihazınızın dil ayarları ile ilgili bir problem olabilir, altyazı dil seçeneğinden Türkçeyi seçmeniz yeterli.
Biz Türklerin günahı yok ne yapıyorsak kendi kendimize yapıyoruz, herşeyi hazır önümüze istiyoruz.