this is a great method, i am using this method and getting gold on daily basis, but i am using 2.5 volt and 6 ampere with iron nail on both terminal as your old video showed, thanks a lot for too much easy method
I do this method but backwards my machine told me the cords were backward so i switched them. There was very little happening when i had the connections on either way. so i remembered when I used epson salt to remove silver plating you needed a catalyst so i put smb as the catalyst and the gold started coming out in sponge form.
Great method. I've used stannous chloride, and the first, solutions is changed the clear, and after, the precipitation shall be conducted (about from 20 to 30 minutes), it is more quickly if a little heating for the solution but is not over 50 Celsius degrees. By XRF machine, I've find the metal mixture powder with 10% gold, 21% copper and PGMs remain. So, gold is still in solution, however, the colors of mother solution have not changed the black or other colour, It is only to change the clear color at the first. What do you think about this matter.
@@myadventure7069 Since you're applying voltage , why not displace the gold with copper? Wikipedias' "Reactivity series of metals" states there are many other metals between iron to copper that might get in the way. Oh , And if you just tie the iron and copper wire together , wont it form a sort of galvanic cell so you dont even need to add DC ?
Copper is less reactive than iron, and will only precipitate silver, gold, and PGM. If you treat the ore/rock/material with nitric before hand, there’s a good chance you’ll remove all the copper before dissolving the gold. Unless it’s an alloy of gold that has more than 50% gold. Also, it’s hard to get gold into solution if copper or other metals are present (remember, it drops gold). The solution will just sit there and cycle, leaving the gold behind. Lastly, Iron is easier to separate and remove than copper is. Magnets, HCl, H2SO4, etc. hope this helps :)
this is a great method, i am using this method and getting gold on daily basis, but i am using 2.5 volt and 6 ampere with iron nail on both terminal as your old video showed, thanks a lot for too much easy method
I ask you if the aqua regia does not dissolve the iron nails
Aqua regia dissolves the iron very little as iron chloride, but stays in liquid and displaces gold
@@mohammadusmani5351 That is, it dissolves it but does not precipitate it. thank
Big great from Morocco to California.
Stay safe Sir.
I do this method but backwards my machine told me the cords were backward so i switched them. There was very little happening when i had the connections on either way. so i remembered when I used epson salt to remove silver plating you needed a catalyst so i put smb as the catalyst and the gold started coming out in sponge form.
Great method. I've used stannous chloride, and the first, solutions is changed the clear, and after, the precipitation shall be conducted (about from 20 to 30 minutes), it is more quickly if a little heating for the solution but is not over 50 Celsius degrees. By XRF machine, I've find the metal mixture powder with 10% gold, 21% copper and PGMs remain. So, gold is still in solution, however, the colors of mother solution have not changed the black or other colour, It is only to change the clear color at the first. What do you think about this matter.
Stay safe my friend.
That’s fire retardant being dropped. Stay safe my friend
An evacuation notice was issued for the area. I hope you are safe.
I am ok .
Good you are safe. I would offer to help but my truck is broken.
@thisoldminewithlars5324 I just need to Cary my gold 😝😜😝😜
Good video, U don't need electricity for that
No you don't but the electricity speeds it up that's the whole point
I love you thank you❤
Thank you for sharing 🤗 But I am qurious does that method precipitate 24k gold
First you get any gold then you refine that gold to 24 carats .
Mere pass iron ki bahut milati hai usmein se gold Kaise recover kiya jaaye ji Iske bare mein thoda bataiye ji🎉❤
good work
Just nail that gold..!
Then iron out .👍👍👍
موجب حديد وسالب ايش؟
Positive
@@myadventure7069 ليش مافيش مترجم. لم يفتهملي عذرا
ايش تقضد في إيجابي
؟
انتة اعمل كل الطرفين حديد لاانة في واحد من المشتركين في التعليق الذي قبل قال انة عمل كل الاطراف حديد واستخرج الذهب
Why not 2 copper wires? iron is higher on the reactivity series of metals and would precipitate other things too.
Iron going in solution and precipitate the gold . Iron is more reactive .stay away from copper !
@@myadventure7069 Since you're applying voltage , why not displace the gold with copper? Wikipedias' "Reactivity series of metals" states there are many other metals between iron to copper that might get in the way. Oh , And if you just tie the iron and copper wire together , wont it form a sort of galvanic cell so you dont even need to add DC ?
@wageslaveuranus9596 what do you want ? I don’t like copper !!!!!
Copper is less reactive than iron, and will only precipitate silver, gold, and PGM. If you treat the ore/rock/material with nitric before hand, there’s a good chance you’ll remove all the copper before dissolving the gold. Unless it’s an alloy of gold that has more than 50% gold. Also, it’s hard to get gold into solution if copper or other metals are present (remember, it drops gold). The solution will just sit there and cycle, leaving the gold behind. Lastly, Iron is easier to separate and remove than copper is. Magnets, HCl, H2SO4, etc. hope this helps :)
@brandonwells1287 I make video about that
😪😪😪geçmiş olsun