International welding engineer exam questions: Material and their behavior for CWI and CSWIP

Поділитися
Вставка
  • Опубліковано 29 жов 2024

КОМЕНТАРІ • 28

  • @manjunathsk6467
    @manjunathsk6467 4 роки тому +1

    Thank you so much for the efforts sir.
    I am learning a lot from you sir.

  • @mohindersingh502
    @mohindersingh502 4 роки тому +1

    Thanks for this important module questions. They are similar to our iwe exam questions

    • @manjunathsk6467
      @manjunathsk6467 4 роки тому

      Sir pls share your e mail id.
      I want to do IWE.
      I need your guidance sir. Please help me

  • @sandy001987
    @sandy001987 4 роки тому

    Useful questions

  • @hopefullysoonaweldingengineer
    @hopefullysoonaweldingengineer 11 місяців тому +1

    Hello, Thank you for all you beatitul efforts teacher. Are you sure that question 6 answer is correct? Because as far as my deep knowledge in metallurgical sicence hardness of the base metal can be affected all of the above? Am I missing something? Could you please assist?

    • @MaterialWelding
      @MaterialWelding  11 місяців тому

      Answer is correct. You can also practice latest IWE questions here. cwindtexams.com/courses/iwe-iwt-iws-exam-question-bank/

    • @hopefullysoonaweldingengineer
      @hopefullysoonaweldingengineer 7 місяців тому

      Can you explain why? Because all of them are true.@@MaterialWelding

  • @nickbriane
    @nickbriane 5 місяців тому +1

    Sir ,can i buy the text book for explaining these questions in electronic edition?

    • @MaterialWelding
      @MaterialWelding  5 місяців тому

      Check this out cwindtexams.com/courses/iwe-iwt-iws-exam-question-bank/

  • @algirbo
    @algirbo 3 роки тому

    thank you, sir, I really learned a lot from these questions. But could you review the answer to question 36 again, please?

  • @sanjeevanpv6437
    @sanjeevanpv6437 4 роки тому +1

    Which is the correct answer for Q36 NDT full form? Non Destructive testing or Nil Destructive Testing?

    • @MaterialWelding
      @MaterialWelding  4 роки тому

      Thanks. in material science, its called Nil Ductility Temperature.

    • @sanjeevanpv6437
      @sanjeevanpv6437 4 роки тому

      @@MaterialWelding thanks for the clarification

  • @zachariasrohithjoseph5154
    @zachariasrohithjoseph5154 4 роки тому

    Question no 18. is the answer provided correct. ?
    Any person would say that high carbon steels are tough to weld without a 2nd thought.

    • @zachariasrohithjoseph5154
      @zachariasrohithjoseph5154 4 роки тому +1

      A low HI process may assist in welding high carbon steel. but does that mean the weldability is Good?
      Pls advice

    • @MaterialWelding
      @MaterialWelding  4 роки тому

      Thank you for your feedback. This question is for IWE exam and right answer is C.

    • @MaterialWelding
      @MaterialWelding  4 роки тому

      I will go with a high heat input to weld high carbon steel as it will help me to reduce the cooling rate, give more time for the hydrogen release and reduce the stresses, so help to eliminate three reason responsible for weld cracking.

    • @hopefullysoonaweldingengineer
      @hopefullysoonaweldingengineer 11 місяців тому

      High carbon steel's weldability is poor. So I Think there can be a mistake in the answers. Not notweldadble but yes poor welable.

  • @sunnydhiman665
    @sunnydhiman665 4 роки тому

    *GoOD

  • @LivingWordsStream24
    @LivingWordsStream24 4 роки тому +1

    Is there anyone who can reveal the answers?

    • @MaterialWelding
      @MaterialWelding  4 роки тому

      Thank you. Answers are given at the end of the video.

  • @naren18ify
    @naren18ify Рік тому

    Question no. 6 - why cant it be option E

    • @naren18ify
      @naren18ify Рік тому

      Also question no. 38 - any grain size below n equal to 65 (Astm gs no. 5 & above) microns is fine grains. Isn't it !?

    • @naren18ify
      @naren18ify Рік тому

      Question no. 17 - higher carbon content will increase the yield strength and reduce the elongation. Isn't it !?

    • @hopefullysoonaweldingengineer
      @hopefullysoonaweldingengineer 11 місяців тому

      I think question 6 should be E.

    • @hopefullysoonaweldingengineer
      @hopefullysoonaweldingengineer 11 місяців тому

      I think so. The answer should be c.@@naren18ifyfor question 17.