the panning method brother, but you need to be careful because the tiny gold wires that are smaller than our hair will float in the water, I tried that and then the carbon was washed out, I looked under the microscope and there was a lot of gold that was carried in the water.
yes brother, but some very tiny wire can be taken into the water no matter how careful, you can try it your self to prove after the carbon is washed out in the water, remove the water and look through the carbon using magnifying glass and you will discover that there is a lot of gold wire that can be carried in the water.
nice work, I tried this method but I went straight to AR afterwards and it seemed that some PM was missing from my batch. In some conditions sulfuric can dissolve some gold possible, I've heard, if it is concentrated. Happy Holiday.
Thank you very much brother, sulfuric acid isn't dissolve gold wire, Sulfuric acid does not dissolve gold, brother, I have proven that a few more times, but it can discolor gold, if you look closely, it turns look like copper, but its color will change and return to the true gold color when you put concentrated nitric acid. Happy holiday too.
HNO3 Nitric acid that combined with HCl Hydrochloric acid (muriatic acid) make aqua Regia only mix that can dissolve gold, then he used SMB sodium metabisulfite to precipitate it from solution, u can also use many other percipitants, vitamin C, aluminum, zinc, some type of iron, even electrolysis, if no access to HNO3, u can use HCL and peroxide, even HCl and bleach, all methods VERY DANGEROUS need fume hood or proper mask, stay safe my friend!
Sorry about silver process, since this video is gold recovery only I didn't showed to our viewers, but here's what i have done, after aqua regia some silver chloride are precipitate, and capture to our filter paper together with few amount of carbon, then I add few ml of hydrochloric acid to our aqua regia to completelly precipitate some silver forming silver chloride, then capture to our filter again, since the silver is too small amount then I save the filter paper together with silver chloride's then we recover it soon.
I have a request to make PoorMiners....i have heard and read from a few sources that resistor arrays contain pgm. Do you have any experience extracting from resistor array? I would love to see a video lesson from you on these please. Onegaishimasu sensei
sir new subscriber here, sir kung wala available na nitric acid, tapos gagamitin lng AP solution, mga gano kaya ktagal mdisolve ung mga base metal ng isang kilong ic chips na naprocess na ng sulfuric acid? salamat and more power
Pina ka matagal na yung 20 days, maganda kung may bubler ka yung ginagamit sa aquarium ba, pero kung wala pwedi naman haluin mo lang dalawang bisis sa isang araw
да, брат, в других видео обычно можно увидеть, что соотношение царской водки у них 3:1, я прав? но для меня все по-другому, я действительно не хочу деноксировать свой раствор царской водки, чтобы избежать загрязнения, поэтому я медленно добавлял азотную кислоту, чтобы избежать избытка азотной кислоты, если ее избыток, не слишком много, поэтому, если вы деноксируете свой Царская водка: вы добавили лишь небольшое количество нейтрализующего агента, и ваша царская водка безопасна от загрязнений, в конце концов, золото легко осаждается.
Excellent video with detailed waiting times of procedures! I was surprised at the melt, I too was expecting more. Out of curiosity, how much cost in reagents (acids) and other material costs involved- and are all the buckets in the background different batches from the different products you are doing? Now I'm just being nosey- and don't answer that, thank you!
I spent less brother than you expected, because the drain cleaner I bought is only php105 pesos a liter, $1.9 usd, I purify it, and potassium nitrate 1 kilograms worth php500 $9.09 produces 500ml hno3 I consume only 40ml of this video maybe 50ml about 50php It's only $0.9 USD, in total we spend php100 but our hardwork worh 500php thats okay..
So, you aren't disposing of the carbon disolved by the sulfuric acid because it also contains minute sized particles of gold. Crushing the silicon wafers and adding them back to the carbon and larger bond wires for processing with nitric acid in one batch. Add HCl to drop the silver chroride, filter, and process with AR. Get it all! How much gold do you attribute to the silicon wafers?
who told you that I did not dispose of the dissolved carbon? what was left in my beaker was the pcb fiber, silicon wafers, gold wires and few amount of carbon just few amounts only, Adding hcl after nitric acid to precipitate silver chlorude? Then you dissolved tiny gold wire, if you were in my situation, you would be able to calculate the gold contained in the silicon wafers?
@PoorMiners321 I'm just trying to follow along with what process you used. My mistake about disposing of the dissolved carbon. I was under the impression it also contained particles of gold. I'm just curious. Since you crushed the silicon wafers and processed them, by doing that, how much extra gold does that yield? In most other refiners You Tube videos, they just throw away the silicon wafers left after dissolving the IC chips in sulfuric acid. Of course, if they pyrolize the chips, those wafers get ground up along with everything else.
The dissolved carbon brother need to dilute more water in a bucket to control some tiny gold wire floating, always allowed few seconds to settle down tiny gold wire. the gold in the silicon wafers brother is very small amount, the others have no gold. Based on the examination that I have done through a microscope, so I did not separate what was there and what was not, this procedure has a little less losses compared to dry ashing, panning, and also to direct aqua regia which is silicon carbon. it absorbs soluble metals such as silver and gold.
@@PoorMiners321save the IC dies and sell them for arts and crafts. The gold bond wires can be removed with a mix of HCl and enough bleach to make it have chlorine in it. ❤
Boss dapat sayo pag aralan mo muna wag kang basta basta lang gagawa sa ganitung experiment mahirap to kung wala kang alam, wala kang makukuhang ginto dito ipapakita ko sayo ang kaibahan sa brass copper silver at gold e babad natin sa nitric acid tingnan natin anong mangyayari sa copper at brass.
😂😂 thats a good one but no for real tho, i think the hardest part using wet method i faced in the past is trying to decant the sulfuric without losing gold bonding stuck to the carbon. After a few batches it gets better. Believe me reading, learning, keeping to clean and meticulous method like Poor Miners will help you get more gold and less copper.
Boss dapat talaga kasi yung nerecover ko na halos 1kilo na mga plated pins na galing pa sa mga nokia ayon nuong lumabas tanso ang narecover ko ay may halong ginto nasayangan ako sa mga ginamit ko na muriatic acid at hydrogen peroxide
It's very amazing tutorial on gold recovery. Job well done Sir!❤
Thanks
Komusta pare, very nice. Thanks for that
Okay lang pare, salamat pare.
You’re my favorite UA-cam-refiner👍
Keep on going bro 😃
Thank you very much brother..
Thanks for sharing from Australia well done
Thanks brother
Nice amount of gold for those ic's
yes brother, I think the losses are less than other procedures.
nice recovery. I wonder what the recovery would have been if burning the IC chips instead ie the more traditional way
the panning method brother, but you need to be careful because the tiny gold wires that are smaller than our hair will float in the water, I tried that and then the carbon was washed out, I looked under the microscope and there was a lot of gold that was carried in the water.
Even with jet dry in the water?@@PoorMiners321
@@PoorMiners321 did you try the dish soap method to break the surface tension of the water will stop the gold from floating?
Yes
yes brother, but some very tiny wire can be taken into the water no matter how careful, you can try it your self to prove after the carbon is washed out in the water, remove the water and look through the carbon using magnifying glass and you will discover that there is a lot of gold wire that can be carried in the water.
Another informative video demonstrating an excellent method of refining ;) thank you !
Thank you brother..
Nice work!
Always nice to see that button after 😂
Thanks
Nice video. Very informative
Thank you very much brother..
Thanks brother❤
very well done my brother!
Thanks brother..
nice work, I tried this method but I went straight to AR afterwards and it seemed that some PM was missing from my batch. In some conditions sulfuric can dissolve some gold possible, I've heard, if it is concentrated. Happy Holiday.
Thank you very much brother, sulfuric acid isn't dissolve gold wire,
Sulfuric acid does not dissolve gold, brother, I have proven that a few more times, but it can discolor gold, if you look closely, it turns look like copper, but its color will change and return to the true gold color when you put concentrated nitric acid. Happy holiday too.
Leçons intéressantes merci beaucoup et j'espère qu'il y aura des autres merci encore
Merci beaucoup frère
Very good to see this video dear only i dont understand the 2nd chemical name plz after dissolving carbon what chemical you pour write name here
Thanks brother after dissolving carbon I add only distilled water bother to wash out dissolve carbon.
HNO3 Nitric acid that combined with HCl Hydrochloric acid (muriatic acid) make aqua Regia only mix that can dissolve gold, then he used SMB sodium metabisulfite to precipitate it from solution, u can also use many other percipitants, vitamin C, aluminum, zinc, some type of iron, even electrolysis, if no access to HNO3, u can use HCL and peroxide, even HCl and bleach, all methods VERY DANGEROUS need fume hood or proper mask, stay safe my friend!
What did u use to precipitate silver
Sorry about silver process, since this video is gold recovery only I didn't showed to our viewers, but here's what i have done, after aqua regia some silver chloride are precipitate, and capture to our filter paper together with few amount of carbon, then I add few ml of hydrochloric acid to our aqua regia to completelly precipitate some silver forming silver chloride, then capture to our filter again, since the silver is too small amount then I save the filter paper together with silver chloride's then we recover it soon.
I have a request to make PoorMiners....i have heard and read from a few sources that resistor arrays contain pgm. Do you have any experience extracting from resistor array? I would love to see a video lesson from you on these please. Onegaishimasu sensei
I trying hard before brother but in the end nothing, only alloy of nickel and chromuim in the resistor brother.
Yes, usually palladium or platinum, but not a lot unless you got several kilos worth.
Resistors are usually nickel mostly. Capacitors have a variety of pgms
Muito top,gostei do seu trabalho.
muito obrigado irmão
Wow...thankyou for the information greatly appreciate. Question was that urea before the SMB?
In this video I use sulfamic before smb, but if you want to use urea before smb then you can do also.
sir new subscriber here, sir kung wala available na nitric acid, tapos gagamitin lng AP solution, mga gano kaya ktagal mdisolve ung mga base metal ng isang kilong ic chips na naprocess na ng sulfuric acid? salamat and more power
Pina ka matagal na yung 20 days, maganda kung may bubler ka yung ginagamit sa aquarium ba, pero kung wala pwedi naman haluin mo lang dalawang bisis sa isang araw
@@PoorMiners321 maraming salamat sir, try ko sir, ganda ng mga vid nyo
Я что то не совсем понял царская водка ,ты наливаеш 200мл соляной кислоты ,и всего 9мл азотной кислоты ?
да, брат, в других видео обычно можно увидеть, что соотношение царской водки у них 3:1, я прав? но для меня все по-другому, я действительно не хочу деноксировать свой раствор царской водки, чтобы избежать загрязнения, поэтому я медленно добавлял азотную кислоту, чтобы избежать избытка азотной кислоты, если ее избыток, не слишком много, поэтому, если вы деноксируете свой Царская водка: вы добавили лишь небольшое количество нейтрализующего агента, и ваша царская водка безопасна от загрязнений, в конце концов, золото легко осаждается.
Excellent video with detailed waiting times of procedures! I was surprised at the melt, I too was expecting more. Out of curiosity, how much cost in reagents (acids) and other material costs involved- and are all the buckets in the background different batches from the different products you are doing? Now I'm just being nosey- and don't answer that, thank you!
I spent less brother than you expected, because the drain cleaner I bought is only php105 pesos a liter, $1.9 usd, I purify it, and potassium nitrate 1 kilograms worth php500 $9.09 produces 500ml hno3 I consume only 40ml of this video maybe 50ml about 50php It's only $0.9 USD, in total we spend php100 but our hardwork worh 500php thats okay..
Good work. You got US$240 and only spent around US$10 on materials. Your work is the difference. On the Philippines that should be plenty
Bro, Pwede magtanong? Kung ok lang sayo.Sa Davao region area po ba kayo? Salamat
Hindi bro malayo tayo.
💎⛏️🇧🇷. 👏👏👏👏👏👏
Thanks brother..
Kaibigan anu ang ginagawa mu na stanous chloride
15 grams of tin metal tutunawin sa 50ml 29 or 35% hydrochloric acid known us muriatic acid.
Ilang buwan Ang expiry nya kc gumawa Ako one week lang Wala na
@bonsaifesway432 oh ganun lang talaga mga 4 days
I have some doubts sir can you please clear ?
What do you mean?
@@PoorMiners321 how long and at what temperature should aquaregia process should get heated?
Have you heard of dissolving quartz using 35% Hydrogen peroxide?
Yes but 35% hydrogen peroxide is not available in our country.
@@PoorMiners321 That's to bad I was wondering if it really works
❤🎉❤❤❤
So, you aren't disposing of the carbon disolved by the sulfuric acid because it also contains minute sized particles of gold. Crushing the silicon wafers and adding them back to the carbon and larger bond wires for processing with nitric acid in one batch. Add HCl to drop the silver chroride, filter, and process with AR. Get it all! How much gold do you attribute to the silicon wafers?
who told you that I did not dispose of the dissolved carbon? what was left in my beaker was the pcb fiber, silicon wafers, gold wires and few amount of carbon just few amounts only, Adding hcl after nitric acid to precipitate silver chlorude? Then you dissolved tiny gold wire, if you were in my situation, you would be able to calculate the gold contained in the silicon wafers?
@PoorMiners321 I'm just trying to follow along with what process you used. My mistake about disposing of the dissolved carbon. I was under the impression it also contained particles of gold. I'm just curious. Since you crushed the silicon wafers and processed them, by doing that, how much extra gold does that yield? In most other refiners You Tube videos, they just throw away the silicon wafers left after dissolving the IC chips in sulfuric acid. Of course, if they pyrolize the chips, those wafers get ground up along with everything else.
The dissolved carbon brother need to dilute more water in a bucket to control some tiny gold wire floating, always allowed few seconds to settle down tiny gold wire. the gold in the silicon wafers brother is very small amount, the others have no gold. Based on the examination that I have done through a microscope, so I did not separate what was there and what was not, this procedure has a little less losses compared to dry ashing, panning, and also to direct aqua regia which is silicon carbon. it absorbs soluble metals such as silver and gold.
@@PoorMiners321save the IC dies and sell them for arts and crafts. The gold bond wires can be removed with a mix of HCl and enough bleach to make it have chlorine in it. ❤
ผมมาจากไทยแลน ผมอยากทราบว่ส ใช้น้ำยากี่ชนิด และใช้ปรมาณขนาดไหนครับ คุณเบี่ยมมาก
👍
Wel that is a 22k gold beed.
Yes brother,
Boss tanso ata yan hindi tunay na ginto yung narecover ko nuon nabubura sa bato pag pinatakan mo ng acido
It is not the color of copper; if anything, it would be brass, which has copper in it, but no. Copper would never survive all the acid baths!
Boss dapat sayo pag aralan mo muna wag kang basta basta lang gagawa sa ganitung experiment mahirap to kung wala kang alam, wala kang makukuhang ginto dito ipapakita ko sayo ang kaibahan sa brass copper silver at gold e babad natin sa nitric acid tingnan natin anong mangyayari sa copper at brass.
😂😂 thats a good one but no for real tho, i think the hardest part using wet method i faced in the past is trying to decant the sulfuric without losing gold bonding stuck to the carbon. After a few batches it gets better. Believe me reading, learning, keeping to clean and meticulous method like Poor Miners will help you get more gold and less copper.
Boss dapat talaga kasi yung nerecover ko na halos 1kilo na mga plated pins na galing pa sa mga nokia ayon nuong lumabas tanso ang narecover ko ay may halong ginto nasayangan ako sa mga ginamit ko na muriatic acid at hydrogen peroxide
Paki detalye daw sa procedure na ginamit, nag tataka ako bakit copper nakuha mo haha
Bossing asa inyoha dapit ? Kay naa unta koy mga stock nga carbon ba.
Nasa kabilang kunteninte po ako bro.
Ok sige bro salamat
Kunin ko contact mo bossing ako na bahala sayo