Reads title... DIY... Expects some half assed hill billy welding job... Ends up inspired by the work of art you constructed.... Keep up the good work m8!
Pretty decent welds but you need a 12 or even bigger furick cup they work a charm and don’t do more than 7 dips at a time and let that section cool down weld a different part of the pipe and have about 4.5 seconds of post flow
@@RuskiWeldFab no problem bro, last time I got my first ss big project, it wasn't perfect in every inch of weld but anyway looks so cool, unfortunately I burnt my welder haha
hey mate , what amps are you running when welding this . im currently welding 1 1/4 sch10 . just over 3mm wall from memory and cant seem to penetrate through to the other side
Honestly i am not the authority on this as this was my very first mani. but i believe it was around 110amps peaks. but using pedal so anywhere between 80 and 110 i guess.
Your purge setup is backwards, purge from the lowest point as air will sit on top of argon, so you want the tape on the highest point to allow the air to escape
@@RuskiWeldFab ну да другой, но там готовое решение, накуя городить все это?? Я конечно понимаю, наши руки не для скуки, но мне кажется это лишнее!! В таком случае можно и ананизмом заняться!!🤣🤣🤣🤣🤣
Great video? How do you make sure the welds inside the exhaust are smooth?
Hey thanks for the comment! To achive smooth welds on the inside i use back purging. running flow of argon gas on the inside.
@@RuskiWeldFab I thought so, but wasn't sure. Looking forward to seeing the ceramic coating on it!
@@dougleturbo1 Me too! will look crazy good i think!
привет,мне бы сворил бы тоже ,толка нa 1.8 20 v turbo ,я как бы сам могу но тиг не имею,а миг для етого не катит
Reads title... DIY... Expects some half assed hill billy welding job... Ends up inspired by the work of art you constructed.... Keep up the good work m8!
wow thanks for the kind words! i did work out better than expected haha.
Hahaha. The bloopers at the end!!!
ha ha
Just found your channel. You have a new subscriber. Great work.
Welcome!
Nice work. I'm about the start my own header for a Toyota, first time.
You can do it!
Inspirational video! Makes me want to take up TIG welding and make my own. Is back purging necessary?
Go for it!
man i hope i can make a manifold because is sure cant find one for my 04 3.8 buick
you can do it!
Looks like a monster from my deepest nightmares. Good job.
Thanks!
Pretty decent welds but you need a 12 or even bigger furick cup they work a charm and don’t do more than 7 dips at a time and let that section cool down weld a different part of the pipe and have about 4.5 seconds of post flow
Thank you!! That’s a decent advice
But ohnestly I praise your good fitment and lack of gaps that’s the most important thing
Thank you! Yes prep is everything!
Really well made turbo and video. Best are the out-takes 😁
thank you Buddy! appreciate that
Good work man. 👍👍👍
Cheers
i want make a turbo on my clio 1.6 16v
Why not!
How much argon are you running thru manifold weld you welding?
Junior III hey thanks for the comment. Honestly not sure exactly but fill it up at 10-12cf for 1-2min than put on minimum around 4-5 while welding.
Pretty nice vid and whole project, but i think that your welds are a little overheated
Thanks! Would not be surprised! It was my first real experience with Tig stainless. Still holding tho
@@RuskiWeldFab no problem bro, last time I got my first ss big project, it wasn't perfect in every inch of weld but anyway looks so cool, unfortunately I burnt my welder haha
hahaha that end had me like , damn bro I can imagine
Hahah I am
A bit better now lol
Заебись!
Сколько трубы и отводов ушло ? берешь только 90" отводы и кусок прямой трубы? какой толщины стенка,4мм?
Уже не помню, 14-15 отводов и 2метра трубы по-моему. Стенка 2.77мм
@@RuskiWeldFab буду такой же мастерить только из черняхи
What material are those pipes made of?
Schedule 10 stainless.
Who makes your name plates?
PrestigeRacingMotorsports Hi. Speak to Gordon at www.jetcutit.com
What kind of pad and disc you are using at the end to polish the manifold
its just a scotch brite attachment for the drill. nothing fancy.
hey mate , what amps are you running when welding this . im currently welding 1 1/4 sch10 . just over 3mm wall from memory and cant seem to penetrate through to the other side
Honestly i am not the authority on this as this was my very first mani. but i believe it was around 110amps peaks. but using pedal so anywhere between 80 and 110 i guess.
V grooving the ends of the pipe can help with that. That way you can get away with less heat and still have fill penetration.
Your purge setup is backwards, purge from the lowest point as air will sit on top of argon, so you want the tape on the highest point to allow the air to escape
good to know! cheers
what diameter pipe ? Looks quite large , 2"
No its Schedule 10S 304 Stainless Steel - 1-1/2"
I was going to comment on the size of the runners in terms of air velocity and turbo lag but you beat me to it, they do look large
Your design and concept is really nice but you need to practice your Technique and better preparation..
200% this was my very first one. A test haha. If it cracks, next one will be better
@@RuskiWeldFab keep it up👍
@@eulisesacevedo4929 thank you! i know its not perfect! never meant to be. but it mine :)
Я единственно не понимаю, накуя эту шляпу ты варил, почему не взял готовое решение с Меган РС, там мотор такой же!!
Где он там такой же?
@@RuskiWeldFab ну да другой, но там готовое решение, накуя городить все это?? Я конечно понимаю, наши руки не для скуки, но мне кажется это лишнее!! В таком случае можно и ананизмом заняться!!🤣🤣🤣🤣🤣
Ну на готовом решение контент не построишь 😜
афигеть он длинный
That’s what sheee said 😂😂😂
@@RuskiWeldFab 🤣🤣🤣