If the crater current is too low, setting the crater time to 4 seconds may cause the melting pool to float because the current is instantaneously reduced.
I am not sure whether u r talking about pin-hole or just dot. If pin-hole is your case, then I would say that even if you are speeding up and ur down slope is 4sec, rapid cooling will cause the same problem.
@@ciwoong84 yes, exactly, pin hole is my case when I am welding root on stainless pipe. I am welding pipe in the vice, I weld quarter by quarter in diagonal pattern to avoid pipe from twisting. And after each section of root I got pin hole that is visible both inside and outside. Crater time is 4sec, and I tried more, still pin hole is there(( Before I stop, I take welding rod from the puddle and continue slight wiggling movement on one place until the arc is fading out
너무 잘하시는데 겸손하시네요.. 좋은 영상과 친절한 설명 감사합니다! 👍 👍 👍
분발해야겠네요 감사합니다
내가원하는 영상이네요 소재 부터 전압 그리고 방향 갭이줄어드는거 까지 배관 회사에다니고있지만 용접은 못하고있지만 점심때나 두시간정도일찍가서 연습하기시작했습니다
이런영상 정말 많이도움됩니다
많이올려주세요 그리기 훌치기 6g같은거 정말현장 위주에용접 감사합니다
오래 댓지만 보실련지 몰르겟지만 지금 연습중이라 ㅠ 전진이 잘안되는데 갭이 좁아서 쇳물이 많이 올라와서 세라믹이 양스라에 걸치는 느낌이 안드는데.. 이럴때는 그냥 파이널 내듯이 모서리 안타고 가야 되는지유?
목소리 너무 좋아요.
얼굴도 존잘일꺼 같은 느낌인데 꼭 그렇게 다 가져야만 속이 후련했냐?!
내가 원하는 영상 초보들에겐 이런 영상이 필요함 감사합니다
현장 참 깔끔하네요 ㅎ
저희쪽 일있을때도 좀 도와 주세요~^^
뭍어가야지요.
이제 더이상의 사부님은 유선생님이 다하네요..
항상 수고하십니다~~
그래도 윱보다 손잡아 주는게 중하긴하죠^^
파이널 위빙손동작과 연습하는방법도부탁드려요 다른영상을 봐도 잘모르겠어요
다른 영상도 많아서 고민하고있었는데 한번 찍어 볼께요.
카~ 목소리 좋고, 화질 좋고, 음악이 안 깔려서 알곤새는 소리도 좋고....ㅎㅎ👍
감사합니다. 🙏
가접부분 끝에서 용가재를 대고 바로 직행하지 말고, 가접부분 끝에서 용가재를 한번 찍고 난 다음에 용가재를 이어서 가면 연결부분이 표 안나고 매끄럽게 됩니다. 좋은 동영상 감사합니다.
좋은 가르침 감사합니다. 이렇게 또하나 알아감니다.^^
맞아요 저 알곤소리 너무 좋쵸 내가 뭔가 하고 있다는.. 나를 알려주는 소리 ㅋㅋ
용접물이 뒤로넘어간다는게 어떤느낌인지 설명부탁드려효
와이어감으로잡아도되고쇳물이진하게 앙쪽융착부가 빛나면 내려앉는거임
현장이 어디세요? 되게 깔끔하네요
크린룸 샵입니다. 😁
그런곳 저도 취업하고 싶네요 ㅠㅠ
자리 없나요
많은도움되었습니다.
감사합니다.
도움이 되셨다니 다행입니다.
영상잘봤습니다!
항상 봐주셔서 감사합니다.^^
보통알곤은15정도두고하시나용,
질소퍼지에 알곤이 안날릴정도로 합니다 ^^
여쭙고싶은데 가스배관 mp 안에 그라인더 못대는걸로 아는데 눌러떼우다 터지면(용락시)어떻게 수정 하시나요??❤
음.. 용락시킬일이 많이 없긴한데 용락한다해도 용락 부위를 하지로 퍼트려 주면 이쁘게 수정 가능해요^^
영상 잘봤습니다 👍
감사합니다^^
구독 누르고 갑니다. 영상 감사합니다.
구독 정말 좋아합니다. 감사해요ㅎ
very usefull video. thank you
용접은 기능직입니다~ ^^숙련도의 차이에요 파이팅
영상 잘 보았습니다. 촬영 영상이 깔끔해서 보기 좋네요. 카메라 고정은 어떻게 하신건가요?
거치대로 각도 맞춰놓고 촬영했어요ㅎ
너무좋다 이런거 ㅎㅎ
감사합니다 ~
Good job. How to avoid dot in the root when I terminate arc? Crater time is 4 sec, I speed up when finishing but very often dots are where I stopped
If the crater current is too low, setting the crater time to 4 seconds may cause the melting pool to float because the current is instantaneously reduced.
@@ciwoong84 thank you for reply, but I didn't quite understand what you mean, should I make more seconds?
I am not sure whether u r talking about pin-hole or just dot.
If pin-hole is your case, then I would say that even if you are speeding up and ur down slope is 4sec, rapid cooling will cause the same problem.
@@ciwoong84 yes, exactly, pin hole is my case when I am welding root on stainless pipe. I am welding pipe in the vice, I weld quarter by quarter in diagonal pattern to avoid pipe from twisting. And after each section of root I got pin hole that is visible both inside and outside. Crater time is 4sec, and I tried more, still pin hole is there(( Before I stop, I take welding rod from the puddle and continue slight wiggling movement on one place until the arc is fading out
When u are stopping, u should not wilggle on one spot but weave forward while arc is fading out to dissipate heat so that u can prevent rapid cooling.
목소리가 성우급~!!
good job!👍
Thank you.😆
파이널 전류는 몃인가요 ?
3.2파이 용접봉으로 120정도 줬던거 같아요
전진이잘안되는느낌이들때는 자세문제인가요?아님융용풀이커서그런건가요
여러가지 상황이 있는데 전류가 높을경우에 와이어를 밀어 넣어도 융융지가 인사이드로 밀려들어가서 전진은 안되고 백이 크게 형성되는 경우도있어요. 백이 많이 나오시나요? 아니면 전진만 안되는 느낌이신가요?
@@ciwoong84 전진이안되는느낌요 저는전기를 좀 강하게쓰는편이라 ㅠㅠ
아.. 제가 아직 기량이 부족해 답변을 못드리겠네요 ㅜ.ㅡ
사람이 문제라고..다들 이야기하죠...ㅎ
텅스텐 길이나, 토치의 각도등에따라 위빙폭을 조절한다는 느낌, 또는 반전기 잡아가며 물크기를 조절하며 진행해보세요 어차피 손은 한번에 바뀌는게 아니니ㅠㅠ
@@bantam5111 넵~~감사해요ㅎ저는텅스텐길게빼고해욤ㅎ
ㅅㄷ 안성샵인가요? ㅎㅎ
텅스텐을 길게해야 유리하지않나요?
적당히가 좋겠죠 좁은갭에 3시부터 텅스텐을 길게 뽑아서 가기에는 무리가 있어보여요
텅스텐길이는 상황에따라 다름
Nice one
Beautiful
영상을 위해서 반반으로!!.. 감사합니다
볼품없는 영상에 칭찬 감사합니당
용락부위 수정법부탁드려요 ㅎㅎ
조선 스탈 반도체 스탈 어느거용?
@@ciwoong84 다른가요?둘다해주심 ㄱㅅㄱㅅ용ㅋ
질 보고 갑니다
감사합니다
감사합니당
@@ciwoong84 그.....용접을 못하면
배관이 함몰되거나
없던 단차가 생기기도 합니까???
@@user-xd7gx4rt1q 네 입열량이 높아지면 서스 특성상 비틀리고 휘어지는 특징이있어서 함몰뿐 아니라 없던 단차도 생길수있어요.
@@ciwoong84 큭....... 제가 못해서 그랬던 것이군요 ㅜㅜㅜㅜ
이에대한 강의 영싱 만들아주시면
초짜한테 많은 도움이 될거 같습니다 !
더 노력하면 결과가 좋겠네요