Beginners Guide To Annealing
Вставка
- Опубліковано 28 жов 2017
- When starting out making jewellery, whether it be in Silver, Gold or Copper, you will find that your metal gets harder the more you bend, hit, roll it. This is called work hardening. You need to return the metal to its original state and so you have to anneal it.
This films shows you how to anneal properly. Over heat the metal and you may have trouble later on.
THE EQUIPMENT I USE TO VLOG
Canon 70D, Body; tinyurl.com/j89...
Canon Lens 10-18mm; tinyurl.com/gnc...
Tripod for Canon; tinyurl.com/hdh...
Memory Cards; tinyurl.com/z8m...
Card Reader; tinyurl.com/z97...
Microphone, Cheap; tinyurl.com/hbx...
Microphone; tinyurl.com/zpj...
Canon G7X Camera; tinyurl.com/jkv...
Tripod for G7X; tinyurl.com/z27...
Mini Tripod; tinyurl.com/he9...
Mavic Drone; tinyurl.com/jfh...
360 Camera; tinyurl.com/jbm...
Andrew shows you many hints and tips that he has gained from his experience as a professional goldsmith.
Andrew Berry, a professional jeweller for 30 years, is the training director of www.AtTheBench.com, an award winning on line jewellery training website. - Навчання та стиль
The best UA-cam channel created ever. Andrew is purely God'sent. Thank you ~
In all my years of metalsmithing, this is the clearest and most helpful description of annealing, how to avoid over heating and how the chemical reaction when heated too much and too often leads to the metal fracturing - recommending to my friends, Thank you!
@Joaly nocontroly you should make this a comment and not a reply, so people have a greater chance of seeing it.
Does this overheating apply to ferrous metals? I was looking up annealing for some stainless steel wire and i keep getting stuff on gold, silver, and copper.
I am a newbie and have ben watching countless videos, reading/collecting books, following other peoples UA-cam channels and tutorials. I am so IMPRESSED with this video that I looked farther into what you do and WOW! FINALLY - CONCISE - INFORMATION! It's been frustratiing trying to find the perfect fit as someone who knows NOTHING about this, and is REALLY trying to learn. I WILL BE JOINING YOUR COURSE! Thank you!
First clip ive seen where someone explains what Borax does. Everyone else says to stop it sticking. I dont think they actually know about stopping it oxygenating. Andrew, you are a champion. I have learnt so much in your clip than watching hours of the popular ring makers. You also explain WHY it is so.
This video is fantastic .
Thank you dear Andrew and God bless you .
Yacov from Israel
I know we're talking about copper here, but this video is straight gold. Thank you.
Thanks Andrew.
Two questions from the video.
1) What happens if you overheat the silver? Is there any recovery from this?
2) It would have been nice to show by comparison how to use the Sharpie method of indicating when the silver is annealed.
Fantastic! Really interesting and useful about the lighting and it’s effect on your perception of temperature. Thanks very much!
Came across this video with little to no knowledge of chemistry. This video is really does welcome any regular joe to begin to grasp an understanding the annealing contacts. Very well done! Thank you so much for this video! (I'm writing this essay about annealing ovens for my chemistry class and this is going to help a lot!)
Thank you very much for this lesson, sir! Clear, well explained and very useful for me! 🙏
What a brilliant little film. I’m not a jeweller but just wanted to understand the annealing process. Many thanks.
Watched many jewelry making vids but this guy is one of the best as a teacher, direct and on point, Cheers Andrew
I have been watching your videos on UA-cam for only about a month now but I just wanted to say thank you! You are a wealth of knowledge! So many insights.
Thanks Andrew. This was one of the first films I watched, but I didn't comment on all of them. Sharing your knowledge, skills, experience etc is much appreciated.
Explained very well, the demonstration should help those who question when?
In response to some of the questions below, there is a product called Tempilaq, which is a temperature-sensitive indicating solution. You paint it on, direct the flame, and when the appropriate temperature is reached, the Tempilaq changes to a glossy (melted) appearance. It is available in a wide range of temperature indicators from 175 degrees to 1900 degrees Fahrenheit at 43 different temperature points. Seems to me that would be worthwhile to have when first getting a sense of where you need to go to anneal a variety of alloys with exactitude. The company that makes it is Tempil, and it is available in both small and large quantity.
Andrew you thoroughly explained the process so I now have a clear understanding of it. Thank you
Great video. I needed to watch this for my job and it described the process very succinctly. Thank you!
Hi, I'm a moderately experienced jeweler, but I've often experienced issues when annealing or soldering. This video, however, has certainly helped clear up quite a bit for me! Thank you!
Question what are good surfaces to do annealing on? Are using a certain type of tile, brick? Could you suggest or link a place I could order the tile ( plate ) your using. Thanks for the knowledge.
I am currently training to become an Aircraft Mechanic and this explanation does a better job at explaining annealing then the people at the school. We have to bend Copper and Aluminum alloy pipes. Thank you for this video and I hope to see more about how to deal with metal working.
This is a very helpful video which explained some of the problems I have had with annealing. Thank you.
Thank you Andrew. Very good tutorial. I anneal with no lights but is still a lot of light in my work area. So many times I try to guide after the first shadow that appear on the metal while I move the flame over. If the part I anneal is too thin ( a piece of thin wire or a slim bezel wire) I need to use a piece of plywood to block the light from the windows. For thin long wire I coil it as tight possible and I put it in a small metal box on some soldering board pieces (charcoal) and I move the flame around the exterior of the box. Now I have a kiln with digital controller but honestly is easier and faster with the flame.
Great tutorial. Thank you.
It's good to have a refresher course after a long hiatus. Thanks! 👍🙂
This is brilliant! I think you cleared up some confusion I had when I first began to study metalsmithing on my own this past yeat. I read so many things... things that seemed very contradictory because I would read that you apply heat to harden and then I'd read the opposite... that you apply heat to anneal. I became very confused about what annealing actually is. I finally just accepted the fact that applying heat would make the metal malleable without even knowing why and disregarded the bit about metal becoming hard when heated so thanks for a really good and clear explanation! 🙂
That's one of the most useful jewelry making videos i saw. Thank you!
Wow. Explained quite well. I do just a bit different with same result.
Lites out is great idea.
I learned this from an old blacksmith. Thank you for this
Andrew, I love all of your videos, your direction is clear and concise, you Sir ARE perhaps one of my favorite resources. I initially learned from Soham. Thank you for all that you do. 😊
My first attempt at annealing silver was my first lesson in reticulation! And, the piece was still not malleable! Still managed to turn my mistake into a fabulous piece of jewelry though...one of those "happy accidents" if you will.
I'm sure as a total novice I now know I've much to learn but already you stopped me doing it in daylight cheers mate + I enjoyed the video
Thank you Nancy, I had collected all the parts to do this type of etching, but had not gotten around to trying it. So glad you set me straight.
I was more interested in rust proofing bolts and restoring washers for my motorcycle but this has been really really helpful. Thank you. Very informative. :)
Thank you very much Andrew, since i started fallowing you my understanding of jewlwery making has changed dramaticllay.
No DOUBTS. Left.expert 's advice.tks.LONG LIFE.!!!
I am extremely glad that you gave that "long winded" explanation of annealing. I have watched seemingly hundreds of videos about jewelry making. No other video explained why or when to anneal.
I think I understand now. Because of your information, I will be obtaining a torch and ceramic block to protect my works.
Next suggestion, if you have not already done this, would you fully explain "pickling" and how and when that is done with and without annealing?
Only yesterday, did I finally see a video that explained a little of pickling, which is to acid wash the metal...
Would you include recipes for various types, and why the various types would be used?
Graciously yours,
Bethany
I work on guitars, know nothing about this side of the art world, really enjoyed the video. thumbs up.
Best explanation of annealing ever.
Thank you so much. I am a beginner and am working with hammered brass wire. 14 gauge. By the time I hammered a shape into it I could not puncture it with a much needed hole for a jump ring. I gather I shall be buying a Kilm. Thanks !!!
Thankyou very much appricate your lessons .back at the bench
As always, excellent videos. You should do a video showing the black magic marker method 'in action' on both thin wire and thick sheet. Keep up the terrific work Andrew.
Thank you so much for your clear and informative video! I am just getting started working with metal... I have watched several of your other videos! You have a lot of knowledge to share, thank you so much! 😊
Excellent video! This will definitely help me in the future. Thanks mate, keep up the good work.
Nice example of over heating, do you have a video showing the just-right red glow in dim light? I know it can be hard to catch on camera.
what is the correct temperature for silver and for copper for kiln annealing? You mention using a kiln several times but don't mention that important fact! Love your videos and often use them as references.
Learned quite a bit from this!
Oh, and when it gets overheated and then brittle, is there a turn around point, maybe just before it totally melts? Love the technical/physics part of learning all this.
Can you talk some time in the future about financial aspects of the jewelry business? How much money do you need to get started, how much do you have to spend on tools, hire someone or not, how fast can you grow, how profitable can it be, etc.
I soo appreciate this video, thank you for explaining this so clear. ive seen some other videos that are more foufou than substance.
Excellent lesson... I'm so inspired. Just getting started on setting up a studio... collecting tools, I've made a few pieces at art centers and am very eager to get set up. Which kiln do yo you recommend?
Excellent technical tutorial. Although the jury is stll out on the technical terms, "marshmallow molecule" and "brushy" or "hissy" flame. All kidding aside, thank you for making me feel a little more confident in metalsmithing.
Thank you for your Tipps and vor this Tutorial.
Excellent video as always Andrew. Thank you!
Thanks Andrew...this was just what I needed to see !
Hello
some jewelers recommend after the annealing is done to quench in water to fix the new cristallize structure and others recommend to let it cool at room temp.
what do you recommend?
best
daniel
doesnt matter unless its a ferrous metal
Awesome video! Thanks!
Cheers from California !
Great series really helpful as just getting into jewlry macking .
thank you for doing a great job explaining this
Hello
some jewelrs recommend after the annealing is done to quench in watch to fix the new cristallize structiue and other recommend to let it cool at room temp.
what do you recommend?
best
daniel
Thank you…..this is such a great channel? My question is about annealing brass… Cait be done? I ask because you didn’t mention it in this video so perhaos it is a soeialty. Thank you from the bottom of my torch.
Thankyou from NewZealand
Thank you for shering are your Tipps.
Thanks Mr Berry. Learning a ton from you.
Real good information. Thanks, Andrew. How can I find out the correct annealing temperature? And, what do I do if I overheat a piece of metal so that it is properly annealed?
Cheers from your new subscriber from California !
Thanks, good instruction.
clear, but round about way. technically annealing a specific material by temp is more precise and consistent. several charts on material properties are on the web and a digital temp gun is cheap nowdays. i look at them often since i'm coming from a machining background
Mr. Andrew Berry. I'm an old retired (1995) Air Force avionics instructor. Since leaving the Air Force I have studied and done many things and I focus mostly on art. In a manic moment, I pledged to create a unique college graduation gift for my best friends daughter. I gathered facts, observations, and opinions from numerous family and friends and from this future graduate, for nearly a year. I came up with what I feel would be the perfectly designed gift in the form of a medallion. I had several pieces of quality gold jewelry from my family estate. I used to have an art gallery and so most of my friends were either artists or musicians. One good friend at 85 years old gave me a small bag of all his old gold teeth. Well being new to working with metallurgy, I fear I have made a mistake. I bought a small crucible, tools, flux, etc., with the hope I could simply heat and create a small gold puddle which I could later shape and engrave into my gift. After many attempts, I am no closer to my goal. I have several small to medium blobs that refuse to combine. And your right hammering makes things brittle. Bigger hammers make them brittle faster. What if anything can I do. Thank you in advance.
Dental gold is a very different alloy than pure gold, i know that much. Unfortunately, I dont know enough to help you more than that. Hoping your project went well despite the challenges!
Hi Andrew, your videos are extremely helpful and clear! One question about annealing: Is it possible to anneal a silver piece without endangering any solder joins? If so, what would you recommend? Many thanks!
Great advise about quantity being annealed
Fantastic video Andrew , thank you !
Thank you!
Can we have a tour of your bench please?
Thank you for your tutorials for metalsmithing. I want to know if I am able to anneal silver, etc with a small propane torch?
Thank you for your video. How does depletion gilding work, and how do you do it?
Hi Andrew, any video's on domed locket hinges? Thanks keep up these great videos
Can you correct an over annealled project?
Thanks Andrew, this was very helpful
Hi Andrew, I love you videos thank you so much for sharing your knowledge - is there any chance of a video on the little smith torch? If you have already done one could you share the link. Thank you x
Very helpful.
Thank you, I mostly work copper and sometimes silver but annealing silver was a problem (bright lights etc) and had a hard time with it. so this helped a lot :)
Hiya Andrew, thank you this was very good.. I was wondering if the metal that has been over heated can be melted and reused?
If you overheat the metal to a very red hot, is it possible to anneal it again the right way, or is it damaged?
This was very informative, and it seems I have been annealing wrong all the time, overheating my metal.
That explains why even with regular annealing after some time cracks start to appear and also the effectiveness of the annealing seems to get less and less.
As I use to make generaly heavier pieces with a lot of forging/hammering work like bangles/torque bracelets proper annealing is important, so I go to practice what I just have learned from this video.
I have also a question; when I melt up overworked/over annealed metal and cast new blanks, will it have the right properties back? As apparently I can't use the metal anymore as it is now.
And is quenching the metal after heating it nessecary or is it enough to let it cool down at the air?
Andrew , great introduction to annealing. Question that wasn't addressed. After annealing do you let it cool to touch , or quench it.
Great vid, thanks! :) How do I make my gold casts\designs harder as an end product though?
I've heard something about heating it up to 400c and letting it cool down, is there truth to that?
Can you make a vid on that?
Also - did you just put your hand to the flame?? :O 7:33
Excellent
If i have over-annealed a piece, is there any way to salvage it?
Or is that silver ruined forever?
Hi Andrew, thank you so much for this video! What kind of temperature do I need to reach in order to anneal a 925 silver wire (diameter: 2 mm)? Is it possible to use a kitchen torch...? Thanks!
I hope this works on steel wire too! I just bought a roll of tie wire for some projects and apparently didn't get soft annealed.
Hello Andrew Berry at the benches. I love your videos and i have learned much from them, as a silver hobbyist. I have some silver spoons and forks i am going to melt for further use. The silver is 830 and 813 silver. Does the same rule annealing 830 silver as for the sterling silver?
Hi Andrew. Could you tell me the process of how to add gold to coloured glass? To make that lovely colour like saphiret glass?
Do you use Anti-UV safety glasses when you solder/anneal? Thank you Andrew, excellent instruction!
Looking to bend 4/0 copper battery lugs. I was going to put the terminal on a vice heat it with a butane/propane torch and lightly bend the terminal before crimping it to the wire. Any thoughts would be greatly appreciated.
I'm a beginner, can you provide a price friendly tool list for what need to buy to get started. Just a basic list would be to helpful. Thank you so much.
Thank you, I am now ready to anneal my rifle brass cases
Thank you.. amazing and helpful tutorial
Thank you veryyyyyyyyy much Andrew berry
Andrew, is it possible to anneal with a microtorch?
Quite informative, thank you.
Hi. Annealing 18kt gold, do I quench immediately like silver? Thank you.
How do you anneal pure silver ( 999 ) or gold? I've found that it tends to melt at the temperatures described for sterling.