I have never seen a horseshoe build-up like that, in one shot. You are a dental Magician! :)) In those fully edentulous cases, (meaning that there are no other teeth to stop the bite), it is usually hard to determine the correct plane of occlusion (parallel line as you call it) or the Frankfort Horizontal plane as it's called in the literature. The length (or height of occlusion) is also difficult to establish. Very impressive result of course with beautiful aesthetic contours as well. Big fan of your skill level Vera, watching you work is a humbling experience, thanks for sharing!
Thank you!😊 It was a reconstruction of an old bridge that we had to strip porcelain off of and for some reason nobody duplicated it before taking porcelain off… I really hope it works🤞
Noticed you left a conecting bar to prevent distortion of the metal frame, during the porcelain procces. Masahiro Kuwata (Color Atlas of Ceramo-Metal Technology) Before cutting of the frame from the poured sprues and resevoir, should stress relive the casting at about 1000-1100 Cel. for 10-20 min. Have the metal dep. cast you a thin 0.5 mm about 5-10 mm wide and 3-5 cm strip of fav. metal. place it at degass temp and see how it warps. I Stress relive all bridges. Very nice work
@@verahadden4712 At home geting ready for next week Easter Celeb. Pryviet. Listening to.Helene Fisher. Russian born but her Russian about as bad as mine.🤣
Здравствуйте, Елена! Прошу прощения, что долго не отвечалa - просто в отпуске была - но сейчас обязательно прочитаю все сообщения и отвечу на вопросы. Обязательно сделаю дополнительное видео по Vita Porcelain для вас как только попадется подходяшая работа🤗😉
No Vera..if you are using VMK and your prescribed shade is A1 you need OD( opaque dentin A3 in thin layer of around 0.3mm on top of it you use A1 dentin then your transparents/translucents/effects etc..then bake ..then cover it with Ename ( use WN +EN1 + A1 DENTIN in ratio 1:1:1 ( you are using your custom made enamel for that particular shade) ...when we build teeth from in out we first starting with CHROMA then HUE and last is VALUE.. for A1 shade CHROMA is A3 ,HUE is A1 and VALUE is ENAMEL with WN ,EN1 and A1 dentin ... for A2 shade CHROMA is B3 hue is always same as "SHADE" in this example its A2 and Value is same WN,En1 and A2... NECK is ok to use as occlusal but almoust never bucaly except if you dont have space.....i looked at your metal substructure and there is ALLOOOOT of metal and little space to give a proper natural deepth ..and is not problrm with dentist he prepared those teeth with enough space but person who was doing Substructure design overbuilded it
Hi! Mahesh! I use Ivoclar Programat 510 and I love it! It is easy to use and relatively affordable + it has all the functions you need to fire big cases like roundhouses and all on 4 zirconia cases: infrared sensors for slow heating at start of the program and cooling in the end. That would be my first choice for a furnace 😊🤗
Здравствуйте, Стас! Я использовала в этом видео Inside 44 Initial GC для шейки и FD91(флуоресцентный дентин) для режущего края под дентином. Эти два материала представляют собой непрозрачные дентины, которые я обычно использую, чтобы скрыть металл на металлических каркасах. Я не знаю, какую фарфоровую систему вы используете, но в любой системе их можно заменить непрозрачным фарфором. Надеюсь, это было полезно, и если у вас все еще есть вопросы, дайте мне знать, я буду радa помочь😊🤗❤️
Hi! I use Inside (IN) intense opacious dentine for neck and fluorescent dentine(FD) for edge. I use them to hide the metal copings because regular dentine is too translucent. Regular Opacious dentine would work well instead of IN and FD
I have never seen a horseshoe build-up like that, in one shot. You are a dental Magician! :)) In those fully edentulous cases, (meaning that there are no other teeth to stop the bite), it is usually hard to determine the correct plane of occlusion (parallel line as you call it) or the Frankfort Horizontal plane as it's called in the literature. The length (or height of occlusion) is also difficult to establish. Very impressive result of course with beautiful aesthetic contours as well. Big fan of your skill level Vera, watching you work is a humbling experience, thanks for sharing!
Thank you!😊 It was a reconstruction of an old bridge that we had to strip porcelain off of and for some reason nobody duplicated it before taking porcelain off… I really hope it works🤞
Nice work doctor ❤ I hope learn from you
You're awesome. It's really a great job, very natural and in line with the natural color of Shid Jaide. ❤❤❤❤..
Thanks ...brother from Yemen❤
Muito prática técnica,e ficou Natura parabéns ! obrigado por expor para todos!!❤
Hola, me encantó tu trabajo y tu técnica. Felicidades, gracias por compartir.
¡Hola! Me alegro que este video te parezca interesante, gracias 😁
@@verahadden4712 Es facinante.
Vera That’s an excellent idea with the spray bottle I never thought about that. I’m gonna have to try that. Thank you.
Sure! 😊 One of my subscribers shared this trick with me: I am using a small bottle from perfume- it creates very fine gentle mist 🙌🤗
Hello, very beautiful. What is the function of the bar that structures it from the most distal part? Best regards.
Hola Vera..
Como siempre una maravillosa rehabilitación dental.
Saludos!!
Super 😍 girl!
I wish I had a brush like that so I could be as good as you at building up thank you I hope you notice from Philippines
Very Thanks , Copacabana - Rio de Janeiro - Brasil 🇧🇷😎👉👉
Which polish did you put after the translucent one?
Beautiful buildup
So Amazing. Thank you.
Noticed you left a conecting bar to prevent distortion of the metal frame, during the porcelain procces. Masahiro Kuwata (Color Atlas of Ceramo-Metal Technology) Before cutting of the frame from the poured sprues and resevoir, should stress relive the casting at about 1000-1100 Cel. for 10-20 min. Have the metal dep. cast you a thin 0.5 mm about 5-10 mm wide and 3-5 cm strip of fav. metal. place it at degass temp and see how it warps. I Stress relive all bridges. Very nice work
Hi, William! I did not know that, thank you for sharing this knowledge with me and also for the compliment☺️🤗
@@verahadden4712 At home geting ready for next week Easter Celeb. Pryviet. Listening to.Helene Fisher. Russian born but her Russian about as bad as mine.🤣
Beautiful Work!!
Thank You for sharing.
Thank you! 🫶😊😉
THANK YOU VERY MUCH VERA. ВЕРА МНОГО БЛАГОДАРЯ.
ПОЗДРАВИ ОТ МЕН БОРИС
СОФИЯ❤ БЪЛГАРИЯ ❤️
❤️❤️❤️🤗
did you mentioned that if we don’t apply opaque dentine and start with just dentine the result would be gray ?
can you do a video of Opaque a bridge?
Вера можно пожалуйста показывать перед нанесением номер массы и транспорента и эмали
Здравствуйте, Елена! Прошу прощения, что долго не отвечалa - просто в отпуске была - но сейчас обязательно прочитаю все сообщения и отвечу на вопросы. Обязательно сделаю дополнительное видео по Vita Porcelain для вас как только попадется подходяшая работа🤗😉
Good job i floow in Egypt
Thank you🫶😊🤗
Nice work
Thank you
Which material is using??
Vita or design or........
رائع ❤
Vc é fantástica, parabéns, show 😊
Thank you 🙏 😊
Nice Work as always
Thank you, Abdul😊
Hello how do you prevent the crack after the bake
No Vera..if you are using VMK and your prescribed shade is A1 you need OD( opaque dentin A3 in thin layer of around 0.3mm on top of it you use A1 dentin then your transparents/translucents/effects etc..then bake ..then cover it with Ename ( use WN +EN1 + A1 DENTIN in ratio 1:1:1 ( you are using your custom made enamel for that particular shade) ...when we build teeth from in out we first starting with CHROMA then HUE and last is VALUE.. for A1 shade CHROMA is A3 ,HUE is A1 and VALUE is ENAMEL with WN ,EN1 and A1 dentin ... for A2 shade CHROMA is B3 hue is always same as "SHADE" in this example its A2 and Value is same WN,En1 and A2... NECK is ok to use as occlusal but almoust never bucaly except if you dont have space.....i looked at your metal substructure and there is ALLOOOOT of metal and little space to give a proper natural deepth ..and is not problrm with dentist he prepared those teeth with enough space but person who was doing Substructure design overbuilded it
How much brush can you send brush like that
Hello . Can you tell me what masses you used? one by one.
Дуже гарно.
Hi
What was the liquid that you put on the gum part?
بسیار زیبا❤❤
Здравствуйте, сделайте пожалуйста видео о заливки такой модели и изготовление каркаса !
Is that a lucky patient?
Hi! I think that a lucky patient is the one that only needs a cleaning and has healthy natural teeth of their own😉
Nice work
Вера непонятно про массу VITA и люминарии в какой пропорции. Можно показать подробнее на фронтальных зубах и показать номер массы
Красотка!
👍😊🤩
Привіт. Як завжди робота на висоті!
☺️❤️🤗
Which furnace are you using,and which is better vita or ivolcar,,suggestion please
Hi! Mahesh! I use Ivoclar Programat 510 and I love it! It is easy to use and relatively affordable + it has all the functions you need to fire big cases like roundhouses and all on 4 zirconia cases: infrared sensors for slow heating at start of the program and cooling in the end. That would be my first choice for a furnace 😊🤗
do you mix incical powder to dentin the last powder you apply to the build up?
Hi! I usually do not mix dentine with enamel, I do it only if I have to add a lot to the work that I have already fired
bonjour si possible que vous faites une vidéo en expliquant le produitde ceramique que vous utilisez etape par etape svp
Saludos vera te admiro
😊🤗❤️
Good work 👍mam
Thank you 😊
Nice work sir
😁❤️
Good work aap ka
Thank you, Manjar! 😊
Fine mam how about you
Çok güzel elinize yağlıķ
☺️🤗🫶
Wow ❤
Damn good
Nice
Why is there a connector or runner bar on the pontic for that?
Hi! For a full arch restoration , we always attach a bar to make sure it casts properly. It is also easier to hold while applying porcelain. 😊
I hope I can Have with the brush even if you make it old because the brush we use is difficult when it comes to the anterior, it can't do a sharp edge
Здравствуйте. Как начинающем у керамисту, вы посоветовали бы массу vita vm13?
Very nice
Thank you 🙏 😊
bonjour si possible que vous faites une vidéo en expliquant le produit de céramique que vous utilisez étape par étape svp
Ok😊😉
Nicework. But voice ❤️❤️
😊 Thank you!
hi ..please your firing program
Hi, I believe there are some videos where I show program, try my most popular video
Very nice mam.but u didn't reply my comments i did in your previous vidoes
Let me check, I did reply! Check again please
Waiting for your next video
Drop soon mam🙏
Hi, Muhammad! Sorry I didn’t make videos lately- I was on vacation, but I will make a video this week I promise 😊🤗
Здравствуйте. Подскажите название 😮эффекта под дентином в первом обжиге?
Здравствуйте, Стас! Я использовала в этом видео Inside 44 Initial GC для шейки и FD91(флуоресцентный дентин) для режущего края под дентином. Эти два материала представляют собой непрозрачные дентины, которые я обычно использую, чтобы скрыть металл на металлических каркасах. Я не знаю, какую фарфоровую систему вы используете, но в любой системе их можно заменить непрозрачным фарфором. Надеюсь, это было полезно, и если у вас все еще есть вопросы, дайте мне знать, я буду радa помочь😊🤗❤️
@@verahadden4712 Большое Вам спасибо. Очень помогли. Всего наилучшего.
Good❤
амейзинг!😍👍👏
Благодарю!😉😁🤗
😊😊
Thank you🙏😊
Qual modelador usa?
¡Hola! Yo uso Gc Initial para MC modeling liquid 😊
Can u write what is first layer u put i cant understand it sorry
Hi! I use Inside (IN) intense opacious dentine for neck and fluorescent dentine(FD) for edge. I use them to hide the metal copings because regular dentine is too translucent. Regular Opacious dentine would work well instead of IN and FD
Mam which material is use in lingual side
Hi! I used dentine A1 and Enamel 58 on top
❤
🎉🎉
😍😍😍😍
С языч ной стороны какая масса по режещему краю
Русская штоли?
Waiting for a new video vera
👏👍
Thank you, Christophe!😊
👍👍👍🙏🙏🙏
❤❤❤❤😍😍
❤️☺️
работа шикарная , но у тебя и русская аудитория есть )))) говори хоть чуть чуть по русский )))
😊❤️🤗
Hello mam 😊
Hi!😊👋
Привет vera как дела
очень красивая работа
мне интересует работа
Здравствуйте! Как ваши дела?
Нормально больше спасибо раньше я делал серебряные зубы теперь занялся керамикой
Я спрошу тебя, чего я не знаю
Большие зубы не понравились
Говори по русский акцент ужас
Çok çok gerez olmüş
🤭